Mechanical,thermal and morphological properties of poly(ε‐caprolactone)/zein blends

Blends of poly(ε‐caprolactone) (PCL) with zein (PCL/zein) in different proportions (100/0, 75/25, 50/50, 25/75 and 0/100 wt% containing 5 wt% glycerol) were compared based on their mechanical properties (tensile strength, elongation at break, and Young's modulus), and on their thermal properties, the latter determined by thermogravimetric analysis (TGA) and dynamic mechanical thermal analysis (DMTA). The morphology of the materials was studied by scanning electron microscopy (SEM). Blends of PCL/zein showed reduced tensile strength and elongation at break, but increased Young's modulus compared to the pure polymers, in agreement with the DMTA and SEM results. These findings indicated that PCL and zein were incompatible. TGA showed that the thermal stability was enhanced by the addition of zein to PCL, whereas SEM showed a poor interfacial interaction between the polymers. Copyright © 2004 John Wiley & Sons, Ltd.     

Studies on the chemical syntheses and on the characteristics of polyaniline derivatives

Syntheses of parent polyaniline and methyl, methoxy, and ethoxy ortho-substituted polyanilines were performed using the conventional chemical methodology and monitored using the new open-circuit-potential (V_oc) profile technique. The intermediate pernigraniline oxidation state was identified and isolated at the V_oc maximum (A) during the conventional chemical synthesis of poly(o-methoxyaniline) in the emeraldine oxidation state. The introduction of the substituent on the aniline ring leads to longer polymerization times and lower V_oc values. Syntheses in the presence of two different monomers in solution were also investigated and showed preferential polymerization of the monomer with the lowest V_oc potential. All polymers produced were characterized by elemental analysis, gel permeation chromatography, UV-VIS spectroscopy, and cyclic voltammetry. The influence of the substituent on the V_oc profile and on the polymer characteristics are rationalized in terms of steric and electronic effects. © 1995 John Wiley & Sons, Inc.     

Study of process parameters for starch,gluten, and glycerol mixtures

This work involved a study of the effect of processing variables (temperature, water content, rotor speed, and time) on the mechanical properties of starch:gluten:glycerol mixtures in the weight ratio of 40:40:20. The properties of the materials were affected by the processing variables. The torque decreased with water content, indicating that water facilitates the plasticization of mixtures, whereas the increase in temperature accelerated the evaporation of water, thus increasing the torque. Ultimate tensile strength was achieved at the lowest temperature (110°C) and the highest water content (20%), whereas maximum elongation was achieved for the material processed at the highest temperature, 150°C, and the fastest rotor speed, 70 rpm. Copyright © 2007 John Wiley & Sons, Ltd.     

A Layer‐by‐Layer Film of Chitosan in a Taste Sensor Application

Chitosan is alternated with sulfonated polystyrene (PSS) to build layer‐by‐layer (LBL) films that are used as sensing units in an electronic tongue. Using impedance spectroscopy as the principle method of detection, an array using chitosan/PSS LBL film and a bare gold electrode as the sensing units was capable of distinguishing the basic tastes – salty, sweet, bitter, and sour – to a concentration below the human threshold. The suitability of chitosan as a sensing material was confirmed by using this sensor to distinguish red wines according to their vintage, vineyard, and brands.

PCA Plot for red wine samples obtained from impedance measurements at 1 kHz for the sensor array comprising a 3‐bilayer chitosan/PSS film and a bare gold electrode.     

Nanocomposites of natural rubber and polyaniline-modified cellulose nanofibrils

Cellulose nanofibrils (CNF) were isolated from cotton microfibrils (CM) by acid hydrolysis and coated with polyaniline (PANI) by in situ polymerization of aniline onto CNF in the presence of hydrochloride acid and ammonium peroxydisulfate to produce CNF/PANI. Nanocomposites of natural rubber (NR) reinforced with CNF and CNF/PANI were obtained by casting/evaporation method. TG analyses showed that coating CNF with PANI resulted in a material with better thermal stability since PANI acted as a protective barrier against cellulose degradation. Nanocomposites and natural rubber showed the same thermal profiles to 200 °C, partly due to the relatively lower amount of CNF/PANI added as compared to conventional composites. On the other hand, mechanical properties of natural rubber were significantly improved with nanofibrils incorporation, i.e., Young’s modulus and tensile strength were higher for NR/CNF than NR/CNF/PANI nanocomposites. The electrical conductivity of natural rubber increased five orders of magnitude for NR with the addition of 10 mass% CNF/PANI. A partial PANI dedoping might be responsible for the low electrical conductivity of the nanocomposites.     

A comparative study of the non-isothermal degradation of natural rubber from Mangabeira (Hancornia speciosa Gomes) and Seringueira (Hevea brasiliensis)

Due to the increasing search for alternative sources of natural rubber (NR) whose properties are similar to Hevea brasiliesis, several sources have been studied in the past few years. Among them, Mangabeira (Hancornia speciosa Gomes), which is native to Amazon rainforest and other regions of Brazil, has a potential as another viable rubber source. As a continuation of a series of comparative studies between Hancornia and Hevea (clone RRIM 600) these two species by our research team, their thermal behavior was analyzed by thermogravimetry (TG) using Flynn–Wall–Ozawa’s approach in order to obtain kinetic parameters (reaction order, pre-exponential factor and activation energy) of the decomposition process. Results indicated that the thermal behavior of NR from Hancornia was comparable to Hevea with some differences observed as follows: reaction order for Hancornia was higher than for Hevea at the beginning of degradation and very close for temperatures over 350 °C; activation energy and pre-exponential factor had the same trend, i.e., increased with increasing degree of conversion remaining almost constant between 20 and 70% and then increasing for higher degrees, although Hevea was slightly more thermally stable than Hancornia. These major influences in the degradation process in the early stage are attributed to differences in non-rubber constituents present in these two species.     

Electrospun poly(lactic acid) nanofibers loaded with silver sulfadiazine/[Mg–Al]‐layered double hydroxide as an antimicrobial wound dressing

Poly(lactic acid) (PLA) is a versatile, bioabsorbable, and biodegradable polymer with excellent biocompatibility and ability to incorporate a great variety of active agents. Silver sulfadiazine (SDZ) is an antibiotic used to control bacterial infection in external wounds. Aiming to combine the properties of PLA and SDZ, hydrotalcite ([Mg–Al]‐LDH) was used as a host matrix to obtain an antimicrobial system efficient in delivering SDZ from electrospun PLA scaffolds intended for wound skin healing. The structural reconstruction method was successfully applied to intercalate silver sulfadiazine in the [Mg–Al]‐LDH, as evidenced by X‐ray diffraction and thermogravimetric analyses. Observations by scanning electron microscopy revealed a good distribution of SDZ‐[Mg–Al]‐LDH within the PLA scaffold. Kinetics studies revealed a slow release of SDZ from the PLA scaffold due to the intercalation in the [Mg–Al]‐LDH. In vitro antimicrobial tests indicated a significant inhibitory effect of SDZ‐[Mg–Al]‐LDH against Escherichia coli and Staphylococcus aureus. This antibacterial activity was sustained in the 2.5‐wt% SDZ‐[Mg–Al]‐LDH–loaded PLA nanofibers, which also displayed excellent biocompatibility towards human cells. The multifunctionality of the PLA/SDZ‐[Mg–Al]‐LDH scaffold reported here is of great significance for various transdermal applications.     

Self-assembled films of cellulose nanofibrils and poly(<Emphasis Type="Italic">o</Emphasis>-ethoxyaniline)

Nanostructured films of poly(o-ethoxyaniline) (POEA) alternated with cellulose nanofibrils (CnF) were successfully produced by self assembly (SA) at different pH values and investigated by atomic force microscopy and ultraviolet-visible spectroscopy. Results show that it was possible to build up films by alternating POEA and CnF layers with relatively precise architectural control by controlling the number of layers and pH. Film thickness had a dependence on pH which is a combination of the effects of the deposited amount for each POEA layer and the pH at which the absorption of the cellulose nanofibrils was carried out. Comparison of alternated layers of POEA and CnF with multi-immersions of POEA at different pH values, as measured by the ratio between slopes of the straight lines of deposited amount of polymer versus the number of self-assembled layers, shows that alternate deposition at pH 2 has a fourfold increase in the slope. Alternatively, at pH 5, there is no significant difference whether the deposition is alternated (POEA–CnF) or not (POEA).     

Nanoscale conformational ordering in polyanilines investigated by SAXS and AFM

Understanding the adsorption mechanisms in nanostructured polymer films has become crucial for their use in technological applications, since film properties vary considerably with the experimental conditions utilized for film fabrication. In this paper, we employ small-angle X-ray scattering (SAXS) to investigate solutions of polyanilines and correlate the chain conformations with morphological features of the nanostructured films obtained with atomic force microscopy (AFM). It is shown that aggregates formed already in solution affect the film morphology; in particular, at early stages of adsorption film morphology appears entirely governed by the chain conformation in solution and adsorption of aggregates. We also use SAXS data for modeling poly(o-ethoxyaniline) (POEA) particle shape through an ab initio procedure based on simulated annealing using the dummy atom model (DAM), which is then compared to the morphological features of POEA films fabricated with distinct pHs and doping acids. Interestingly, when the derivative POEA is doped with p-toluene sulfonic acid (TSA), the resulting films exhibit a fibrillar morphology-seen with atomic force microscopy and transmission electron microscopy-that is consistent with the cylindrical shape inferred from the SAXS data. This is in contrast with the globular morphology observed for POEA films doped with other acids.     

Effect of X-ray radiation on the structure of P (VDF/TrFE) copolymers

Structural changes in poly(vinylidene fluoride)-trifluoroethylene [P(VDF-TrFE)] copolymers caused by X-ray irradiation were investigated by molecular weight determination, EPR analysis, FTIR spectroscopy, gel content, DSC thermal analysis, X-ray diffraction, and piezoelectricity measurements. Samples exhibit radiation-induced conductivity (RIC) due to the formation of radical ions. These radicals are generated by bond cleavage, which could react, leading to structural changes such as oxidation, double bond formation, chain scission, and crosslinking. The increasing gel content with radiation dose indicated that crosslinkings of the polymer chains predominate. Irradiation on P(VDF-TrFE) caused the melting temperature, heat of fusion, and Curie temperature to decrease. These results are consistent with the partial destruction of crystalline domains. © 1997 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 35 : 1201–1205, 1997