Synthesis and characterization of molybdenum incorporated mesoporous aluminophosphate

A synthesis of molybdenum incorporated mesoporous aluminophosphate with long-chain n-alkylamine as template material had been prepared under non-aqueous condition. These materials were extensively characterized by using X-ray diffraction (XRD), nitrogen sorption isotherms, nuclear magnetic resonance of ²⁷Al and ³¹P (NMR), inductive coupled plasma (ICP), electron spin resonance (ESR), Fourier transform infrared (FTIR) and thermogravimetric-differential thermal analysis (TG-DTA). Morphology of the materials had been observed by using transmission electron microscope (TEM) that revealed the mesoporous materials possessed wormhole-like structures. Alkaline solvent extraction using n-butylamine/ethanol had been efficiently removed the n-alkylamine from the mesoporous samples which yielded BET surface areas around 550-730 m²/g. BJH analysis showed a narrow pore size distribution which increased with increasing of the carbon chain length of alkylamine (template). Valence state and coordination of the molybdenum in the obtained samples were investigated by using ESR and FTIR where it was found that Mo⁴⁺ and Mo⁶⁺ molybdenum species existed in the molybdenum incorporated mesoporous aluminophosphate in tetrahedral coordination.     

Synthesis and refractive‐index control of fluoropolymers by the polyaddition of bis(epoxide)s and triazine di(aryl ether)s

The polyaddition of fluorine‐containing bis(epoxide)s and fluorine‐containing triazine di(aryl ether)s were examined to give the corresponding fluorine‐containing poly(cyanurate)s. It was observed that the synthesized fluoropolymers had good thermal stabilities and good film‐forming properties. The glass transition temperatures (T_g's) and refractive‐indices (n_D's) of synthesized polymers were determined by differential scanning calorimetry and ellipsometry, respectively, and it was found that the values of T_g's and n_D's were supported by their fluorine containing ratios and skeletons. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4421–4429, 2007     

New poly(butylene succinate)/layered silicate nanocomposites. II. Effect of organically modified layered silicates on structure,properties, melt rheology,and biodegradability

A series of new poly(butylene succinate) (PBS)/layered silicate nanocomposites were prepared successfully by simple melt extrusion of PBS and organically modified layered silicates (OMLS). Three different types of OMLS were used for the preparation of nanocomposites: two functionalized ammonium salts modified montmorillonite and a phosphonium salt modified saponite. The structure of the nanocomposites in the nanometer scale was characterized with wide-angle X-ray diffraction and transmission electron microscopic observations. With three different types of layered silicates modified with three different types of surfactants, the effect of OMLS in nanocomposites was investigated by focusing on four major aspects: structural analysis, materials properties, melt rheological behavior, and biodegradability. Interestingly, all these nanocomposites exhibited concurrent improvements of material properties when compared with pure PBS. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 3160–3172, 2003     

Characterization and determination of linear alkylbenzenesulfonates in environmental water samples by high-performance liquid chromatography with a hydrophilic polymer column and electrospray ionization mass spectrometric detection.

A liquid chromatography-mass spectrometry (LC/MS) method was developed for the separation and determination of linear alkylbenzenesulfonates (C10-C14 LAS) in environmental water samples using a hydrophilic polymer column (Shodex Mspak GF-310 4D). This method involves a solid-phase extraction of the LAS samples with a Sep-Pak PS-2 cartridge. The LAS components were separated on the column with a mobile phase of 29% (w/v) acetonitrile-water containing 0.8 mM di-n-butylammonium acetate and 0.2 M acetic acid, and were detected by mass spectrometry with electrospray ionization. Detection limits of the developed method based on selected ion monitoring (SIM) technique for the C10-C14 LAS standards were 13-47 ng L(-1). The concentrations of the C10-C14 LAS in the environmental water samples ranged between 5-317 microg L(-1) for a river water sample and 0.4-6.4 microg L(-1) for a seawater sample. Linear relationships between the logarithms of retention factors and the alkyl chain lengths for each phenyl positional isomer of LAS could successfully be used for the identification of the isomer peaks.     

Bump formation on a glass surface with a transparent coating using femtosecond laser processing

The morphology of a glass surface having a transparent coating processed with focused femtosecond laser pulses is investigated. The transparent coating is formed of poly-methyl methacrylate (PMMA). When the glass was coated with a PMMA film with a thickness of 2.8 μm, bumps were formed over a wide range of axial focus positions. The same laser pulse energy produced cavities when processing bare glass with no coating. The bumps were formed as a result of suppressing material emission from the glass surface by a shielding effect of plasma generated by ablation of the PMMA film and by physical blocking of the PMMA film. A thinner film with a thickness of 0.7 μm produced a reduced shielding effect, forming an exploded bump with a small pit at its center and debris around the periphery. PACS 44.10.+i; 61.80.Ba; 79.20.Ds     

Temporal analysis of products (TAP) study on oxygen storage properties over Pt−Rh/CeO2 catalyst

The oxygen storage capacity of CeO₂, Ce_0.9Pr_0.1O₂, Pt?Rh/CeO₂ and Pt?Rh/Ce_0.9Pr_0.1O₂ was investigated by conventional GC pulse method and transient pulse techniques. It is shown that incorporation of PrO_y into CeO₂ matrix strongly promotes oxygen storage capacity (OSC) measured using the transient pulse technique. The improvement of OSC at low temperature is observed in Pt?Rh loaded onto CeO₂ and Ce?Pr catalysts.     

Separation of fulvic acid from soil extracts based on ion-pair formation with a cationic surfactant.

A novel method for separating fulvic acid (FA) from soil extracts is proposed. The FA, defined as the acid-soluble fraction of an alkaline extract of soil, was separated based on the precipitation of an ion-pair with a cationic surfactant, such as domiphen bromide. The precipitate was dissolved in aqueous HCl to produce H+ -type FA and a surfactant chloride (SUR-Cl). SUR-Cl, in the aqueous solution, was removed by extraction with CHCl3. After the aqueous phase was passed through a cation-exchanger (H+ -type), H+ -type FA (FA-SUR) was obtained as a powder by lyophylization. The chemical characteristics of FA-SUR were compared with an FA sample separated according to the method of the International Humic Substances Society using a DAX-8 resin (FA-DAX). The oxygen content, O/C atomic ratio and total acidity of the FA-SUR were significantly larger than the corresponding values for FA-DAX. The solid-state CPMS 13C NMR spectra indicated that the higher oxygen content of the FA-SUR could be due to alcoholic hydroxyl groups and polysaccharides as well as carboxylic groups. These results show that FA-SUR is more polar and hydrophilic than FA-DAX.     

An efficient synthesis of 5-diethoxymethylimidazole-4-carboxylate,a potential precursor for various imidazole derivatives

Anionic cycloaddition of methyl isocyanoacetate to diethoxyacetonitrile afforded methyl 5-diethoxymethylimidazole-4-carboxylate, a useful imidazole nucleus with two different functional groups.     

Chemical and biological modification of bleomycin,an antitumor antibiotic

Dedicated to Professor John C. Sheehan on the occasion of his sixty-fifth birthday. Chemical and biological modifications of bleomycin, an antitumor glycopeptide antibiotic, have been achieved by three procedures analogous to the modifications of penicillin.