Synthesis of Organic-Inorganic Hybrid Particles by Sol-Gel Chemistry

The synthesis of ORganically MOdified SILica (ORMOSIL) particles has been carried out using both the hydrolytic and non-hydrolytic sol-gel routes. The hybrid (nano)composites are organically modified with an alkyl or aryl group covalently bonded to silicon. Hybrids have been synthesised in an aqueous sol-gel process by a modified Stöber route, producing spherical nanoparticles with diameters in the range 50–300 nm. The size of the particles can be controlled by control of certain reaction parameters. Smaller ormosil nanoparticles can be synthesised by a base-catalysed emulsion polymerisation route, by varying the type and concentration of surfactant and precursor feed rate. In this case, particles in the size range 3.5–10 nm can be obtained. Hybrids have been synthesised from hyperbranched polyesters by encapsulation in a silica matrix using the hydrolytic sol-gel route. Optimisation of the reaction conditions allows the hybrids to be produced as isolated sub-micron spherical particles. Ormosil particles have also been synthesised using the non-hydrolytic sol-gel route, which may lead to products of different morphologies because of the different polarity of the reaction medium. Different reaction conditions were studied in order to optimise the size and shape of the particles, including choice of solvent, use of surfactants and addition of polystyrene. Dimethylsulfoxide acts as a novel oxygen donor for the catalyst-free formation of colourless silsesquioxanes.     

Synthesis of poly(p‐phenylene sulfide) from bis(4‐bromophenyl) disulfide

Improved reaction conditions for the preparation of poly(p‐phenylene sulfide) (PPS) directly from bis(4‐bromophenyl) disulfide (BBD) have been established. Heating BBD with magnesium metal afforded only a low molecular weight polymer. PPS with a melting temperature around 280 °C was obtained from BBD in the presence of sodium carbonate or zinc metal. The best results were obtained with the addition of a catalytic amount of KI to the zinc–BBD mixture. Polymers prepared by the above methods are semicrystalline and dissolve in 1‐chloronaphthalene and have properties comparable to commercial PPS. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 900–904, 2006     

Synthesis and characterization of poly(arylene ether)s containing 6‐(4‐hydroxyphenyl)pyridazin‐3(2H)‐one or 6‐(4‐hydroxyphenyl)pyridazine moieties

A series of novel soluble pyridazinone‐ or pyridazine‐containing poly(arylene ether)s were prepared by a polycondensation reaction. The pyridazinone monomer, 6‐(4‐hydroxyphenyl)pyridazin‐3(2H)‐one ( 1 ), was synthesized from the corresponding acetophenone and glyoxylic acid in a simple one‐pot reaction. The pyridazinone monomer was successfully copolymerized with bisphenol A (BPA) or 1,2‐dihydro‐4‐(4‐hydroxyphenyl)phthalazin‐1(2H)‐one (DHPZ) and bis(4‐fluorophenyl)sulfone to form high‐molecular‐weight polymers. The copolymers had inherent viscosities of 0.5–0.9 dL/g. The glass‐transition temperatures (T_g's) of the copolymers synthesized with BPA increased with increasing content of the pyridazinone monomer. The T_g's of the copolymers synthesized from DHPZ with different pyridazinone contents were similar to those of the two homopolymers. The homopolymers showed T_g's from 202 to 291 °C by differential scanning calorimetry. The 5% weight loss temperatures in nitrogen measured by thermogravimetric analysis were in the range of 411–500 °C. 4‐(6‐Chloropyridazin‐3‐yl)phenol ( 2 ) was synthesized from 1 via a simple one‐pot reaction. 2 was copolymerized with 4,4′‐isopropylidenediphenol and bis(4‐fluorophenyl)sulfone to form high‐T_g polymers. The copolymers with less than 80 mol % pyridazinone or chloropyridazine monomers were soluble in chlorinated solvents such as chloroform. The copolymers with higher pyridazinone contents and homopolymers were not soluble in chlorinated solvents but were still soluble in dipolar aprotic solvents such as N‐methylpyrrolidinone. The soluble polymers could be cast into flexible films from solution. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3328–3335, 2006     

Facile synthesis of exfoliated and highly conductive poly(arylene disulfide)/graphite nanocomposites

Exfoliated graphite has been synthesized by first synthesizing H₂SO₄ intercalated compound in a H₂O₂‐H₂SO₄ mixture, followed by exfoliation under microwave irradiation. Poly(arylene disulfide)/graphite nanocomposites were then fabricated by absorbing cyclic(arylene disulfide) oligomers into the pores of exfoliated graphite. Subsequently, the nanocomposite precursor was subjected to heat treatment to carry out the in situ ring‐opening polymerization of the oligomers via free radical mechanism. The as‐prepared nanocomposite exhibited a exfoliated nanostructure as evidenced by transmission electron microscopy (TEM) observation. The nanocomposite with a very small amount of graphite, 5 wt%, possesses a highly electrical conductivity of 4 S/cm, therefore, many applications can be found as conductive materials. Copyright © 2004 John Wiley & Sons, Ltd.     

Kinetics and mechanism of the acid-catalysed decarboxylation of thecis-α- andcis-β-carbonato(3,6-dimethyl-1,8-diamino-3,6-diazaoctane)-cobalt(III) ions

Summary The acid-catalysed decarboxylation of thecis-- andcis--[CoL(CO₃)]⁺ complexes (L = 3,6-dimethyl-1,8-diamino-3,6-diazaoctane) have been studied over a range of HClO₄ concentrations and the temperatures 25, 35 and 45° at I = 1.0 mol dm^–3 (NaClO₄). The rate expression takes the form k_obs = k₀ + k₁[H⁺] where k_obs is the observed first order rate constant at constant hydrogen ion concentration. The k₀ term makes only a minor contribution to the overall reaction. Both complexes display solvent deuterium isotope effects ofca. 2.6 for the acid-catalysed decarboxylation, consistent with a rapid proton pre-equilibrium mechanism. Activation parameters have been determined and the mechanism of the reaction discussed. The magnitude of the solvent isotope effect is consistent with an A-1 type mechanism involving formation of a 5-coordinate intermediate.