Beitrag zur Kenntnis des Systems Vanadin—Chrom—Stickstoff

The System V–Cr–N has been investigated at 1100 and 1400 °C and at nitrogen pressures between 1 and 1000 atmospheres by X-ray techniques. VN and CrN on the one hand and V₂N and Cr₂N on the other are forming complete series of solid solutions. The phase field of the mononitride solid solution is dependent on nitrogen pressure and temperature conditions.

---

---

Auszug aus der Diplomarbeit des Herrn Dipl.-Ing. Dr.W. Schebesta.     

Die Phase La2U2N5

In the system U–La–N a new phase of composition La₂U₂N₅ was observed. The differaction pattern of this phase can be indexed with a tetragonal unit cell:a=8.43 Å,c=8.50 Å andc/a=1.008. The pseudocubic sub-cell withaca/2 is closely related to the CsCl-type.

Auszug aus der von der Technisch-Naturwissenschaftlichen Fakuktät der TU Wien approbierten Diplomarbait des Herrn Dipl.-Ing.J. Waldhart.     

Hochtemperatur-röntgenographische Untersuchungen an manganreichen Mangan—Vanadin-und Mangan—Chrom—Legierungen

Zusammenfassung Die manganreiche Seite der Systeme Mn–V und Mn–Cr wurde hochtemperatur-röntgenographisch untersucht. Im System Mn–V treten bei 90 At% Mn zwei bisher nicht beobachtete Phasen, und , mit -bzw. -Manganstruktur auf. Diese gehören möglicherweise der Klasse der -bzw. -Phasen an. Die -Mischphase besitzt einen größeren Existenzbereich als in der Literatur angegeben. Die Existenz der -Phase Mn₃V, sowie die Phasenzustände bis 80 At% Mn und bei manganreicheren Legierungen unterhalb 700°C werden bestätigt. Das lineare thermische Ausdehnungsverhalten der Phasen , und sowie des -und -Mischkristalls werden angegeben. Für den manganreichen Teil wird ein vorläufiges Zustandsdiagramm entworfen. Im System Mn–Cr konnte in großen Zügen Über-einstimmung mit Literaturangaben gefunden werden. Es wird das lineare thermische Ausdehnungsverhalten der -Phase Mn₃Cr angegeben.

---

High temperature X-ray investigation of Mn—rich Mn—V and Mn—Cr alloys

The manganese rich portions of the phase diagrams Mn–V and Mn–Cr have been investigated by means of a high temperature X-ray technique. In the system Mn–V two new phases, and , have been observed with -manganese and -manganese type structure, resp. These phases are probably to be classified as -and -phase. The -manganese solid solution with vanadium has a wider range of homogeneity as compared with previous work. The existence of a -phase Mn₃V and phase equilibria below 700°C reported previously could be confirmed. The linear thermal expansion of the intermetallic compounds , , , the -and -manganese solid solutions with vanadium has been evaluated. A tentative phase diagram for the manganese rich portion is given. The main features of the system Mn–Cr according to previous investigations could be confirmed. The linear thermal expansion of the -phase Mn₃Cr is reported.

---

---

Mit 8 Abbildungen

---

Herrn Prof. Dr.Hans Nowotny in Dankbarkeit gewidmet.     

Über die Mischbarkeit von UN mit LaN,CeN, PrN,NdN, SmN,GdN, DyN,und ErN

X-Ray studies of the mixed nitride phases indicate complete miscibility in all cases. Lattice parameters generally showed negative deviations from the additivity rule.

Teilauszug aus der Dissertation des Dipl.-Ing.J. Waldhart an der Technischen Universität Wien, Österreich.     

Die Kristallstruktur von Cr3(C,N)2 und Cr2VC2

Zusammenfassung Die Kristallstruktur der isotypen Phasen Cr₃(C,N)₂ und Cr₂VC₂ wird röntgenographisch bestimmt. Die Struktur gehört der Raumgruppe D _2h ¹⁷ an; sie enthält sowohl oktaedrische wie auch trigonal-prismatische Bauelemente und steht in enger Beziehung zu Cr₃C₂.

---

The crystal structure of the isostructural phases Cr₃(C,N)₂ and Cr₂VC₂ has been determined by X-ray diffraction method. It belongs to the space group D _2h ¹⁷ and contains octahedral as well as trigonal-prismatic groups and is related to Cr₃C₂.

---

---

Mit 1 Abbildung     

Über die Präparation und die Eigenschaften von Molybdän-Wolfram-Carbonitriden

Molybdenum-tungsten-carbonitrides can be prepared by reacting prealloyed powders of Mo and W with carbon in the presence of nitrogen or ammonia. Single phase carbonitrides (Mo, W) (C, N) with the WC-type structure can be obtained. The nitrogen content of these carbonitrides increases with increasing molybdenum content. Flowing ammonia has a decarburizing effect, which has to be counterbalanced by an addition of a carbonaceous gas such as methane. Nitrogen instead of ammonia is equally effective and gives carbonitrides which have a nitrogen content only insignificantly lower than the carbonitrides obtained in flowing ammonia. The lattice parameters of the carbonitrides are found to be slightly smaller than the lattice parameters of the corresponding carbides.

     

Lattice parameters and thermal expansion of δ-VN1−x from 298–1000 K

The thermal expansion of VN_1?x was determined from measurements of the lattice parameters in the temperature range of 298–1000 K and in the composition range of VN_0.707–VN_0.996. Within the accuracy of the results the expansion of the lattice parameter with temperature is not dependent on the composition. The lattice parameter as a function of composition ([N]/[V]=0.707?0.996) and temperature (298–1000 K) is given by $$\begin{gathered} a([N]/[V],T) = 0.38872 + 0.02488([N]/[V]) - \hfill \\ - (1.083 \pm 0.021) \cdot 10^{ - 4} T^{1/2} + (6.2 \pm 0.1) \cdot 10^{ - 6} T. \hfill \\ \end{gathered} $$ . The coefficient of linear thermal expansion as a function of temperature (in the same range) is given by $$\alpha (T) = a([N]/[V],T)^{ - 1} [( - 5.04 \pm 0.01) \cdot 10^5 T^{ - 1/2} + (6.2 \pm 0.1) \cdot 10^{ - 6} ].$$ . The average linear thermal expansion coefficient is $$\alpha _{av} = 9.70 \pm 0.15 \cdot 10^{ - 6} K^{ - 1} (298 - 1 000K).$$ . The data are compared with those of several fcc transition metal nitrides collected and evaluated from the literature.     

Über ein Perowskitoxid Ti3HgO

Zusammenfassung Es wird über ein Perowskitoxid der Zusammensetzung Ti₃HgO berichtet. Die Gitterkonstante der kubischen Elementarzelle beträgta=4,165 Å. Es wird angenommen, daß diese Phase mit einer schon früher als -Ti₃Hg beschriebenen Phase identisch ist.

---

A complex oxide Ti₃HgO with a perovskite type structure is reported. The lattice parameter of the cubic cell isa=4.165 Å. The identity of this phase with a previously reported compound -Ti₃Hg is thought to be very likely.

     

Pheromone, 3.Mitt.: Eine einfache Methode zur Steuerung der Reduktion von α-Alkoxy-carbonylverbindungen

Summary Enantiomerically pure 1,2-diols bearing optionallysyn oranti configurated secondary hydroxylic groups are synthesized from acetal-protected cyanohydrins. After resolution of the diastereomers the cyanohydrins are converted into -alkoxy-ketones by Grignard-reaction followed by reduction using common chelating or non-chelating agents. Among others syntheses of enantiomerically pure pheromones,endo-Brevicomin,exo-Brevicomin and Dispalure are given as examples.

Prof. Dr. Hans Berbalk zum 70. Geburtstag gewidmet     

Das kubische Tantalmononitrid (B 1-Typ) und seine Mischbarkeit mit den isotypen Übergangsmetallnitriden und-carbiden

The position of the recently detected cubic -TaN_1–x phase (B1 type) with respect to the other tantalum nitride phases in the system Ta–N is discussed and a tentative phase diagram for the partial system Ta–N is proposed. -TaN_1–x , a high temperature phase, is completely miscible with all isotypic mononitrides and monocarbides of the 4 a and 5 a group metals. Lattice parameters of the solid solutions are given.

---

---

Mit 4 Abbildungen

---

Herrn Prof. Dr.O. Hromatka zum 70. Geburtstag gewidmet.