Pseudo-epitaxial C60 films prepared by a hot-wall method

We have used both reflection-geometry and grazing-incidence-geometry X-ray scattering to study thin films of C₆₀ evaporated onto mica substrates via a hot-wall technique. The growth mode yields close-packed C₆₀ planes, which are parallel to the substrate surface and which exhibit out-of-plane correlation lengths of 850 Å. In the film plane the C₆₀ is at best pseudo-epitaxial, with a 0.9° distribution of crystallite orientations, a 450 Å in-plane correlation length, and a 3.7% lattice mismatch, better than obtained by other thin film techniques but far from the accepted definition of single crystal thin film epitaxy.     

The “corset effect” of spin-lattice relaxation in polymer melts confined in nanoporous media

Linear polyethylene oxides with molecular weightsM _w of 1665 and 10170 confined in pores with variable diameters in a solid methacrylate matrix were studied by proton field-cycling nuclear magnetic resonance relaxometry. The pore diameter was varied in the range of 9–57 nm. In all cases, the spin-lattice relaxation time shows a frequency dependence close toT ₁∞ v^3/4 in the range ofv=3·10^?1-2·10¹ MHz as predicted by the tube-reptation model. This protonT ₁ dispersion essentially reproduces that found in a previous deuteron study (R. Kimmich, R.-O. Seitter, U. Beginn, M. Möller, N. Fatkullin: Chem. Phys. Lett. 307, 147, 1999). As a feature particularly characteristic for reptation, this finding suggests that reptation is the dominating chain dynamics mechanism under pore confinement in the corresponding time range. The absolute values of the spin-lattice relaxation times indicate that the diameter of the effective tubes in which reptation occurs is much smaller than the pore diameters on the time scale of spin-lattice relaxation experimens. An estimation leads to a valued ^*～0.5 nm. The impenetrability of the solid pore walls, the uncrossability of polymer chains (“excluded volume”) and the low value of the compressibility in polymer melts create the “corset effect” which reduces the lateral motions of polymer chains to a microscopic scale of only a few tenths of a nanometer.     

Synthesis,characterization, and curing kinetics of novel ladder‐like polysilsesquioxanes containing side‐chain maleimide groups

Two ladder‐like polysilsesquioxanes (LPS) containing side‐chain maleimide groups have been synthesized successfully by reacting N‐(4‐hydroxyphenyl)maleimide (HPM) with LPS containing 100 mol % of chloropropyl groups (Ladder A ) and 50 mol % of each methyl and chloropropyl group (Ladder B ). HPM was synthesized by reacting maleic anhydride with 4‐aminophenol, and the resulting amic acid was imidized using p‐toluenesulfonic acid as a catalyst (Scheme 1 ). The LPSs were characterized by Fourier transform infrared (FTIR), ¹H nuclear magnetic resonance (NMR), proton‐decoupled ¹³C NMR, ²⁹Si NMR, wide‐angle X‐ray diffraction (WAXD), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). Characterization indicated that these polymers had ordered ladder‐like structures with possible defects. These polymers were soluble in common solvents at ambient temperature, which suggested that they were not crosslinked. Both the polymers and the HPM were cured, and their kinetics were followed by dynamic DSC. The Ozawa and Kissinger methods were used to calculate activation energies for curing. Curing increased the temperature at which both 5% weight loss and maximum rate of weight loss were observed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4036–4046, 2004     

Direct SCF structure optimization of large molecules on networks of workstations

A program to optimize the structure of large molecules at the Hartree–Fock level of theory running concurrently on a network of workstations is presented. Problems encountered in obtaining nearly optimal speedup and their solutions are discussed. A simple scheduling algorithm is presented that enables up to 99.5% of the code to run in parallel. © 1993 John Wiley & Sons, Inc.