4,5-环氧环己烷1,2-二甲酸单丁酯单缩水甘油酯/m-PDA的热固化特征

本文叔述了4,5-环氧环己烷1,2-二甲酸单丁酯单缩水甘油酯(DME-47)/间-苯二胺(m-PDA)体系的热固化特征。结果表明,由于DME-47中羧酸缩水甘油酯型环氧基的反应活性远大于脂环环氧基。所以,DME-47/m-PDA体系固化反应明显地分两阶段进行。由TBA恒温固化动力学数据求得体系在100—160℃表观反应活化能E_α=13.9kcal/mol,在160—240℃E_α=16.6kcal/mol,根据实验数据按Arrhenius关系式推算,本体系在室温25℃下可以存放80天左右而不凝胶化,20℃下可存放120天左右。     

THE CURING BEHAVIOR OF DIGLYCIDYL-4, 5-EPOXYCYCLOHEXANE-1,2-DICARBOXYLATE

The curing behavior of diglycidyl-4, 5-epoxycyclohexane-1, 2-dicarboxylate with m-phenylenediamine has been studied by using torsional braid analysis. It is shown that the whole curing processproceeds in two stages, that is, curing reaction at temperatures below 100℃mainly occurs at the ali-phatic epoxy rings, whereas a rapid increase in reaction rate of the remaining cycloaliphatic epoxy ringoccurs only at temperatures above 130℃. Between the temperature range from 100℃to 130℃, the"full reaction" of the aliphatic epoxy rings is approximated, while the reaction rate of the cycloaliphaticepoxy ring begins to increase gradually. The maximum glass transition temperature (T_(g∞)) of the systemdoes not emerge before 220℃. The apparent activation energy is 13 .2 kcal/mole.     

样条函数逼近法研究环氧树脂固化动力学

采用样条函数逼近DSC曲线,分别对4,5-环氧环已烷1,2-二甲酸二缩水甘油酯、四氢邻苯二甲酸二缩水甘油酯及双酚A二缩水甘油醚与间苯二胺的固化动力学作了研究.结果表明,样条函数逼近DSC曲线有较高的精度,由模拟函数处理实验数据取得较满意的结果.     

4,5-环氧环己烷1,2-二甲酸二缩水甘油酯/m-PDA固化体系的形态结构及动态力学行为

<正> 不少作者已对一般固化环氧树脂的形态结构作了研究。作者对4,5-环氧环己烷1,2二甲酸二缩水甘油酯(简称TDE-85)树脂固化行为研究的结果表明,由于TDE-85具有两种不同活性的环氧基,固化温度不同,两种环氧基参与开环交联反应程度不相同。本文在不同温度下采用SEM、TBA对TDE-85/m-PDA固化体系并研究其形态结构和相应的动态力学行为。以探讨TDE-85由于化学结构的特殊固化过程与形态结构间的关系。     

4,5-环氧环己烷1,2-二甲酸二缩水甘油酯的固化行为

本文用动态力学扭辨分析法,研究4,5-环氧环己烷1,2-二甲酸二缩水甘油酯与间苯二胺的热固化动态力学行为。结果表明:固化过程分两个阶段进行,低于100℃时,交联反应主要在缩水甘油酯链的环氧基上进行;100—130℃时为酯链环氧基反应趋近完全和酯环环氧基反应速率逐步增大的过渡区;130℃以上固化时,酯环环氧基才明显地参与固化交联反应。从Arrhenius关系曲线求得本固化体系凝胶点前表现反应活化能为13.2kcal/mol。