Evolution Mechanism of Calcium Carbonate in Solution

Calcium carbonate was synthesized in a CaCl₂/NaCO₃ mixed solution by using ethylenedi-aminetetraacetic acid (EDTA) as an additive. The thermodynamics and kinetics analyses indicate that although the driving force of amorphous calcium carbonate (ACC) precipi-tation is always less than that of calcite and vaterite precipitation, the nucleation rate of ACC is greater than that of calcite and vaterite at the initial stage of the precipitation reaction. With the increasing incubation time, vaterite and calcite particles nucleate het-erogeneously by using the as-formed particles as active sites. Scanning electron microscopyimages indicate that the transformation mechanism of ACC and vaterite to calcite is the dissolution-recrystallisation reaction. The presence of EDTA not only improves the stabil-ities of ACC and vaterite, but also leads to forming enlongated, connected rhombohedralcalcite crystals after incubation 7 days in solutions. The ACC and vaterite are stabler in air than in solutions at room temperature, although the dissolution-recrystallisation reaction occurs on the surface.     

新型共混交联磺化聚醚醚酮/部分氟化磺化聚芳醚砜质子交换膜的制备与表征

制备了基于磺化聚醚醚酮(SPEEK)/部分氟化磺化聚芳醚砜(SPFAES)的共混交联型质子交换膜(CMB), 研究了其吸水率、 尺寸变化、 力学性能、 热性能、 质子电导率、 化学稳定性及电池性能等. 通过在溶液浇铸过程中加入脱水剂诱导高温脱水反应, 在共混体系内构建了交联结构. 结果表明, 由于SPEEK与SPFAES之间良好的相容性、 分散性和聚合物链的重排及交联作用, CMB膜在干态下均表现出出色的力学强度, 且物化稳定性得到大幅提升. 在低离子交换容量(1.21~1.51 mmol/g)条件下, CMB膜的质子电导率达到122~219 mS/cm(80 ℃), 在氢氧单电池中, CMB4膜的最大功率密度达到530.5 mW/cm²(80 ℃).     

填充型具有微孔结构的磺化聚芳醚砜/聚醚砜复合质子交换膜的制备及性能

制备了基于磺化聚芳醚砜(SPAES)及聚醚砜(PES)的填充型复合质子交换膜, 研究了其吸水率、 尺寸变化、 热-机械特性、 质子电导率、 甲醇透过性及稳定性等性能. 通过浸入沉淀相转化法, 采用磺化度分别为30%(S30), 40%(S40)及50%(S50)的SPAES与PES制备了系列微孔型复合质子交换膜 Sx-y(x为SPAES的磺化度, y为SPAES的质量分数); 然后利用真空抽滤法在微孔中填充S50制备了相应的填充型复合质子交换膜Sx-y+F50. 结果表明, 由于微孔的引入及皮层结构的存在, Sx-y膜在低离子交换容量(IEC)条件下仍具有较高的电导率、 优良的机械强度、 优异的化学稳定性及较低的甲醇透过性. 经S50填充后, Sx-y+F50膜的IEC及电导率明显提升, 甲醇透过率大幅下降, 但机械强度及化学稳定性未见劣化. 其中S30-40+F50膜(IEC=0.69 mmol/g)的综合性能最佳, 其质子电导率在90 ℃水中达到50.4 mS/cm; 经140 ℃水处理24 h后失重率仅为8.2%, 质子电导率降低仅9%; 经过芬顿试剂(3% H₂O₂, 20 mg/L FeSO₄, 80 ℃, 1 h)处理后失重率仅为0.66%; 甲醇透过率仅为6.8×10^-8 cm²/s.