 对β-FeSi₂晶体进行了原位X射线衍射高压研究。利用同步辐射X射线衍射原位研究了β-FeSi₂的高压相演化，发现压力在4.3 GPa时出现相变，在25.8 GPa时相变完成。指标化结果表明：经高压处理后得到的产物具有四方结构，其晶格常数为：a=b=1.004 9 nm，c=0.339 4 nm。     

Growth of bulk single crystals β-FeSi2 by chemical vapour deposition

Bulk single crystals β-FeSi2, as a new photoelectric and thermoelectric material, has been successfully grown using chemical vapor transport techniqueby using iodine as transport agent in a sealed ampoule. The effects of crystal growth condition on quality and morphologies of the single crystals were studied. Both needle-like and grain-like single crystals were gained. By changing substrate temperature, tetrahedral high quality α-FeSi2 single crystals were also obtained.     

3-氨基-1,3,4,5-四氢-2H-1-苯并氮杂革-2-酮的合成

以3-溴-1,3,4,5-四氢-2H-1-苯并氮杂--2-酮为起始原料,与苄胺反应制得3-苄氨基-1,3,4,5-四氢-2H-1-苯并氮杂(堇)-2-酮(2);2经5％ Pd/C催化加氢合成了3-氨基-1,3,4,5-四氢-2H-1-苯并氮杂——革)-2-酮(3),总收率90％.最佳氢化反应条件为:以无水乙醇为溶剂,5％ Pd/C用量为总用量的10％,于100℃/2.5 MPa条件下反应10 h,3的收率95.5％,纯度99.7％.5％ Pd/C可套用7次,收率稳定在95％左右.     

FeSi2单晶化学气相生长

利用化学气相输运方法, 以碘作为传输剂, 在封闭的石英安瓿中制备出了优质新型的光电及热电半导体材料β-FeSi₂单晶. 在大量实验基础上深入研究了生长工艺对单晶质量、形态的影响, 除了得到大尺寸针状β-FeSi₂单晶外, 还获得了大尺寸颗粒状单晶. 通过改变衬底温度, 得到了四面体柱状优质的α-FeSi₂单晶.     