自掺杂SnO2微球的水热合成及其可见光催化性能

本研究采用水热法,以柠檬酸为螯合剂,通过控制n(Sn⁴⁺)/n(Sn²⁺)的数值,合成了由具有丰富氧空位的SnO₂纳米晶体组装成的微球。通过X射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、傅里叶红外光谱(FT-IR)、X射线光电子能谱(XPS)及UV-Vis漫反射光谱对SnO₂纳米微球进行表征分析,结果表明:在酸性水热条件和柠檬酸的螯合作用下,二氧化锡纳米晶体聚集形成微球;在Sn⁴⁺/Sn²⁺摩尔比例为3:7时,其微球尺寸最小,整体分散性较好;同时适量二价锡离子的掺杂使得该样品氧空位浓度达到最佳,氧空位的存在将使得样品光吸收范围拓展至可见光,因而该样品显示出较强的可见光催化效率,在8 min内完全降解甲基橙。     

射频等离子制备石墨烯负载Co3O4催化剂及其析氧性能研究

氢能的引入能有效提升配电网的供电可靠性,而电解水制氢是实现低碳转型的关键技术,开发高效的电解水催化剂势在必行。过渡金属氧化物储量大、催化活性高,是具有广阔应用前景的析氧反应催化剂。本文通过射频等离子体处理制备石墨烯上负载Co₃O₄析氧催化剂,XRD、Raman和XPS测试结果显示,二维结构石墨烯的引入加速表面电子迁移,增大了反应面积。等离子体处理促进了纳米粒子在石墨烯上的负载,利用等离子体刻蚀作用在催化剂表面制造出大量碳结构缺陷和氧空位结构,改善了活性位点分布,有效调控Co₃O₄电子结构,提高析氧催化活性。电化学测试表明,本文中合成的Co₃O₄@rGO在电流密度为50 mA·cm^-2时的过电位为410 mV,动力学反应速率较快,表现出优于商业IrO₂的析氧催化活性。     

BiVO4/TiO2 heterojunction with rich oxygen vacancies for enhanced electrocatalytic nitrogen reduction reaction

The large-scale production of ammonia mainly depends on the Haber–Bosch process, which will lead to the problems of high energy consumption and carbon dioxide emission. Electrochemical nitrogen fixation is considered to be an environmental friendly and sustainable process, but its efficiency largely depends on the activity and stability of the catalyst. Therefore, it is imperative to develop highefficient electrocatalysts in the field of nitrogen reduction reaction (NRR). In this paper, we developed a BiVO₄/TiO₂ nanotube (BiVO₄/TNT) heterojunction composite with rich oxygen vacancies as an electrocatalytic NRR catalyst. The heterojunction interface and oxygen vacancy of BiVO₄/TNT can be the active site of N₂ dynamic activation and proton transition. The synergistic effect of TiO₂ and BiVO₄ shortens the proton transport path and reduces the over potential of chemical reaction. BiVO₄/TNT has high ammonia yield of 8.54 μg·h⁻¹·cm⁻² and high Faraday efficiency of 7.70% in −0.8 V vs. RHE in 0.1 M Na₂SO₄ solution.     

氧缺陷TiO_2-B作为可充电锂离子电池负极材料的第一性原理研究(英文)

利用对氧缺陷的TiO_2-B材料进行密度泛函理论的计算,阐述了氧空穴对于TiO_2-B材料的电化学性质的影响。计算研究主要聚焦于缺陷材料的锂离子迁移和电子导电性等基本问题。计算结果表明在低锂离子浓度下(x(Li/Ti)≤0.25),相比于无缺陷的TiO_2-B,氧缺陷TiO_2-B有着更高的插入电压和更低的b轴方向迁移活化能,意味着锂离子的嵌入也更容易,这对于可充电电池的充电过程是有利的。而在高浓度下(x(Li/Ti)=1),锂饱和的氧缺陷TiO_2-B相较于无缺陷的TiO_2-B有着较低的插入电压,更有利于锂离子的脱嵌过程,这对于可充电电池的放电过程也是有利的。电子结构计算表明缺陷材料的禁带宽度在1.0-2.0 e V之间,低于无缺陷的材料的3.0 e V。主要态密度贡献者是Ti-Ov-3d,并且随着氧空穴的增加它的强度也变得更强。这就表明氧缺陷TiO_2-B有更好的电子导电性。     

稀土掺杂对氯化氢氧化制氯气CuO-CeO2-SiO2催化剂结构和性能的影响

CuO-CeO₂-SiO₂ and rare-earth-doped CuO-Ce_0.9M_0.1O₂-SiO₂ (M=La, Pr, Nd) catalysts for recycling Cl₂ from HCl oxidation were prepared by a template method, using activated carbon as a hard template. The catalyst structures were determined using X-ray diffraction (XRD), N₂ adsorption-desorption, transmission electron microscopy (TEM), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and H₂ temperatureprogrammed reduction (H₂-TPR). The catalytic performances were also investigated. The results showed that La, Pr, and Nd cations were incorporated into the CeO₂ lattice and formed nanosized solid solutions; this greatly reduced the catalyst grain sizes, leading to higher surface areas. In addition, the oxygen vacancy concentrations were significantly improved. The changes in the structures and surface properties of the solid solutions significantly affected the HCl catalytic oxidation performances. The order of the activities of various catalysts was CuO-Ce_0.9La_0.1O₂-SiO₂>CuO-Ce_0.9Nd_0.1O₂-SiO₂>CuO-Ce_0.9Pr_0.1O₂-SiO₂>CuO-CeO₂-SiO₂. The oxygen vacancy concentrations of the solid solutions were strongly related to their catalytic activities. However, the structures and performances of the Ce_0.9M_0.1O₂-SiO₂ catalysts showed that an increase in the number of oxygen vacancies resulted in decreased catalytic activities of the solid solutions. Kinetic studies showed that oxygen adsorption could be the rate-determining step for rare-earth-doped catalysts; a higher oxygen vacancy concentration in the solid solution led to a slower reaction rate when the volumetric flow ratio of O₂ to HCl was 1. For the CuOCe_0.9M_0.1O₂-SiO₂ catalysts, spillover of oxygen species in the solid solution into the highly dispersed CuO interfaces was enhanced, which increased the overall reaction rate and gave high activity.     

Activation of α-Fe2O3 for Photoelectrochemical Water Splitting Strongly Enhanced by Low Temperature Annealing in Low Oxygen Containing Ambient

Photoelectrochemical (PEC) water splitting is a promising method for the conversion of solar energy into chemical energy stored in the form of hydrogen. Nanostructured hematite (α-Fe₂O₃) is one of the most attractive materials for a highly efficient charge carrier generation and collection due to its large specific surface area and the short minority carrier diffusion length. In the present work, the PEC water splitting performance of nanostructured α-Fe₂O₃ is investigated which was prepared by anodization followed by annealing in a low oxygen ambient (0.03 % O₂ in Ar). It was found that low oxygen annealing can activate a significant PEC response of α-Fe₂O₃ even at a low temperature of 400 °C and provide an excellent PEC performance compared with classic air annealing. The photocurrent of the α-Fe₂O₃ annealed in the low oxygen at 1.5 V vs. RHE results as 0.5 mA cm⁻², being 20 times higher than that of annealing in air. The obtained results show that the α-Fe₂O₃ annealed in low oxygen contains beneficial defects and promotes the transport of holes; it can be attributed to the improvement of conductivity due to the introduction of suitable oxygen vacancies in the α-Fe₂O₃. Additionally, we demonstrate the photocurrent of α-Fe₂O₃ annealed in low oxygen ambient can be further enhanced by Zn-Co LDH, which is a co-catalyst of oxygen evolution reaction. This indicates low oxygen annealing generates a promising method to obtain an excellent PEC water splitting performance from α-Fe₂O₃ photoanodes.     

The enhanced photo-stability of defective Ag3PO4 tetrahedron prepared using tripolyphosphate

Ag₃PO₄ is an excellent photocatalyst under visible light irradiation. However, the low stability due to photo-corrosion is still an obstacle in its application. It is a big challenge to improve stability using synthesis modification. Here, the photocatalyst stability enhancement was successfully prepared by tripolyphosphate. Photocatalyst was prepared by reacting AgNO₃ solution with STPP (sodium tripolyphosphate) solution to form a white suspension. The addition of phosphate solution to the white suspension produces yellow Ag₃PO₄ with a new type of defective photocatalyst. The XPS measurement showed that the increase of STPP concentration significantly decreased the Ag/P atomic ratio, indicating the silver vacancy formation on the surface of Ag₃PO₄. The photocatalytic reaction formed a metallic Ag with a lower d-space in the cube structure occurred in the silver vacancy of Ag₃PO₄. This defect increases the interaction of metallic silver and Ag₃PO₄. The enhanced photo-stability might be induced by metallic silver that can act as a photogenerated electron acceptor.     

具有高光催化活性的黑色TiO2（B）/锐钛矿双晶TiO2-x纳米纤维

高效TiO2基光催化材料的开发一直是催化领域的研究热点,主要的策略是如何有效地分离光生载流子.制备多晶相的TiO2材料可引入异质/相结结构使电子与空穴朝不同方向移动,从而避免电子与空穴复合;另外,在TiO2中掺杂其他金属或非金属也可以有效地降低电子与空穴的复合率,掺杂的元素作为电子捕获阱俘获光生电子,以实现电子空穴的有效分离.近些年,作为一种全新的掺杂剂,氧空穴可以有效改善TiO2的光催化活性,所制TiO2具有可见光的全光谱吸收能力,因此该类TiO2呈现出黑色.通过上述方法均可以制备出高活性TiO2基光催化材料,如果能够将这些方法耦合一起,则可能制备出活性更高的光催化剂.因此,本文将异相结结构和空穴掺杂耦合起来,用多孔钛酸盐衍生物在H2中高温焙烧制得一种全新的黑色TiO2(B)/锐钛矿双晶TiO2–x纳米纤维.不同于其他TiO2基光催化材料,该样品仅由Ti和O元素组成,通过Ti和O元素的组合,形成了双晶结构和空穴掺杂两种特殊的结构,借助场发射(FESEM)、拉曼光谱(Raman)、氮气物理吸脱附、X射线光电子能谱(XPS)、热重(TG)、紫外可见漫反射光谱(UV-Vis)和荧光光谱(PL)等表征分析了样品的结构及其光催化性能间构效关系. FESEM结果显示,黑色TiO2(B)/锐钛矿双晶TiO2–x为长1–5mm、宽0.2mm的纤维结构, Raman结果表明,锐钛矿相在特征波段(140 cm–1左右)和TiO2(B)的特征波段(220–260 cm–1)均发生蓝移,说明该两相中均存在氧空穴;该样表面未检测到Ti3+,因此氧空穴可能分散在TiO2(B)和锐钛矿相的体相中.根据黑色TiO2(B)/锐钛矿双晶TiO2–x和白色TiO2(B)/锐钛矿双晶TiO2的失重差,估算出前者的O/Ti原子比为1.97.光催化降解甲基橙实验结果显示,黑色TiO2(B)/锐钛矿双晶TiO2–x的光催化活性是白色双晶TiO2的4.2倍,锐钛矿TiO2的10.5倍,且连续反应10次后未出现失活现象,显示出了良好的光催化稳定性.前期,我们已经证明了白色TiO2(B)/锐钛矿双晶TiO2由于具有TiO2(B)和锐钛矿的异相结结构,致使其电子空穴有效地分离,从而表现出优异的光催化活性;本文的PL结果显示,由于氧空穴的引入,异相结与氧空穴两者共同作用,进一步促进了黑色TiO2(B)/锐钛矿双晶TiO2–x电子与空穴的有效分离,因此黑色TiO2(B)/锐钛矿双晶TiO2–x表现出高的光催化活性.由于其特殊的结构,黑色TiO2(B)/锐钛矿双晶TiO2–x纳米纤维将在环境与能源领域表现出良好的应用前景.     

15N/14N Isotopic Exchange in the Dissociative Adsorption of N2 on Tantalum Nitride Cluster Anions Ta3N3-

Adsorption and activation of dinitrogen (N₂) is an indispensable process in nitrogen fixation. Metal nitride species continue to attract attention as a promising catalyst for ammonia synthesis. However, the detailed mechanisms at a molecular level between reactive nitride species and N₂ remain unclear at elevated temperature, which is important to understand the temperature effect and narrow the gap between the gas phase system and condensed phase system. Herein, the ¹⁴N/¹⁵N isotopic exchange in the reaction between tantalum nitride cluster anions Ta₃¹⁴N₃^- and ¹⁵N₂ leading to the regeneration of ¹⁴N₂/¹⁴N¹⁵N was observed at elevated temperature (393-593 K) using mass spectrometry. With the aid of theoretical calculations, the exchange mechanism and the effect of temperature to promote the dissociation of N₂ on Ta3N3? were elucidated. A comparison experiment for Ta₃¹⁴N₄^-/¹⁵N₂ couple indicated that only desorption of ¹⁵N₂ from Ta₃¹⁴N₄¹⁵N₂^- took place at elevated temperature. The different exchange behavior can be well understood by the fact that nitrogen vacancy is a requisite for the dinitrogen activation over metal nitride species. This study may shed light on understanding the role of nitrogen vacancy in nitride species for ammonia synthesis and provide clues in designing effective catalysts for nitrogen fixation.