The curing process of a polysulfide (PSF) with a triacrylate crosslinker in the presence of an amine catalyst at room temperature is a rapid Michael addition. This reaction was monitored by real‐time infrared spectrum (RTIR). The results of the RTIR show that the consumptions of thiol and acrylate are stoichiometric until 80% conversion, indicating the characteristics of a “click” reaction. Dielectric analyzer (DEA) and dynamic mechanical analyzer (DMA) were employed to investigate the curing kinetics from which the activation energies of this curing reaction were obtained and shown to correlate with each other. In addition, the influences of the types and amount of amine catalyst, the different molecular weights of PSFs, and the triacrylate crosslinkers were discussed. Copyright © 2011 John Wiley & Sons, Ltd.     

三羟甲基丙烷三丙烯酸酯-甲基丙烯酸甲酯沉淀聚合制备单分散聚合物微球

以三羟甲基丙烷三丙烯酸酯(TMPTA)为交联剂,甲基丙烯酸甲酯(MMA)为共聚单体,偶氮二异丁腈为自由基引发剂,以乙醇或乙醇-水混合物作溶剂,在2 wt%的单体浓度下通过沉淀聚合制备了交联聚合物微球.探究了聚合时间、混合溶剂的含水量以及交联剂TMPTA用量对聚合过程及聚合产物的影响.结果表明,增加TMPTA用量可提高单体转化率和微球产率;所得微球的粒径则随着TMPTA用量的增加而减小.TMPTA用量占单体总量40 wt%至80 wt%,反应时间不少于6 h时可制得高度单分散聚合物微球,产率达到80%以上.在反应介质中加入水可明显提高单体转化率和微球产率,当混合溶剂中水的体积分数为35%时,仍可制得高度单分散聚合物微球,产率可达94%;但当混合溶剂中水的体积分数达40 vol%时,所得微球的多分散系数增大.     

含三个硬脂酰胺基的树枝状季铵盐的制备

由三羟甲基丙烷三丙烯酸酯(TMPTA)和乙二胺(EDA)直接进行M ichael加成反应,合成端基为3个NH2的树枝状大分子G(NH2)3,用硬脂酰氯将其端氨基进行酰胺化得到端基为3个硬脂酰基的树枝状大分子GS(R)3,产率为82.4%。GS(R)3进一步与碘甲烷反应,其分子中的3个仲氨基被季铵化,生成树枝状季铵盐GI(R)3,产率为82.0%。讨论了反应温度、反应时间和原料配比对GS(R)3和GI(R)3产率的影响,并用红外、核磁和元素分析对GS(R)3和GI(R)3的结构进行表征。     

悬浮聚合法制备磁性分子印迹聚合物微球

以苯胺和二甲基苯胺为模板分子、甲基丙烯酸(MAA)为功能单体、三羟甲基丙烷三丙烯酸酯(TRIM)为交联单体、Fe3O4为磁性组分,采用悬浮聚合法制备了磁性分子印迹聚合物微球(MMIPMs)。结果表明,改性Fe3O4微粒在MMIPMs中分散较好,MMIPMs在水性介质中对模板分子的选择吸附性较差,但在有机介质中有较好的选择吸附性。     

二苯甲酮／胺：紫外光固化涂料中的新型引发剂

通过三羟甲基丙烷三丙烯酸酯与二乙胺的迈克尔加成反应,合成了一种新型叔胺衍生物,利用＾１Ｈ ＮＭＲ对其进行了验证。当该叔胺与二苯甲酮配合使用时,表现出很好的固化速度并能代替昂贵的光引发剂１１７３,使紫外光固化涂料的成本显著降低。同时,对该二苯安双分子引发剂的作用机理进行了探讨。     

伽马射线辐射原位强化增韧含三羟甲基丙烷三丙烯酸酯的PET/弹性体合金

在少量的交联剂三羟甲基丙烷三丙烯酸酯存在下,研究了高能伽马射线辐射对PET/弹性体（ST2000）合金的原位强化增韧效应.在PET合金熔融共混的高温下,TMPTA可与PET和ST2000的分子链发生反应,使PET和ST2000发生分子内和分子间的交联,增强界面相互作用,使得PET合金的冲击性能提高,但拉伸强度有所下降.PET合金经过高吸收剂量的伽马射线辐照后,可以原位增加体系内部弹性相和界面相的化学交联程度,进一步提升PET合金的综合力学性能.当吸收剂量为100 kGy时,样条在冲击测试条件下未发生断裂,同时拉伸强度几乎保持不变.     

沉淀聚合法制备单分散聚(4-乙烯基吡啶-co-二乙烯基苯/三羟甲基丙烷三甲基丙烯酸酯)聚合物微球

以4-乙烯基吡啶(4-VP)为功能单体、二乙烯基苯(DVB)和三羟甲基丙烷三甲基丙烯酸酯(TRIM)为混合交联剂,偶氮二异丁腈(AIBN)为引发剂,乙腈为反应介质,采用沉淀聚合法制备单分散聚合物微球.考察了共聚单体、溶剂、引发剂等聚合条件对聚合物微球粒径、分散性以及产率的影响.并用扫描电镜(SEM)、激光粒度分析仪、热重分析仪和红外光谱对微球进行了表征.结果表明,聚合物微球的表面形貌和产率可通过改变溶剂体积、单体/交联剂摩尔比和引发剂浓度等因素进行控制.降低乙腈溶液体积、增加DVB摩尔比例及交联剂摩尔比、可增加聚合物粒径及粒度分布均匀性,而聚合物产率随溶剂体积和DVB摩尔比增大而减小,随交联剂摩尔比和引发剂浓度的增加而增加.在最优条件下,即DVB和TRIM两者摩尔比4∶1,单体/交联剂摩尔比1∶5,乙腈用量为5.6 m L(单体和交联剂占介质体积的7%),引发剂浓度为2 wt%~6 wt%(占总反应单体的量)时,可获得形貌规则、产率较高的单分散poly(4-VP-co-DVB/TRIM)微球,微球平均粒径约4.02μm,粒径分布指数(U)为1.013.此外,热重分析结果显示,聚合微球于350℃时开始分解,600℃时失重率达84.9%.     

Environmentally friendly method for the determination of acrylamide and trimethylolpropane in paper packaging materials by liquid chromatography with tandem mass spectrometry

A simple, rapid, and environmentally friendly method was developed for the determination of acrylamide and trimethylolpropane in paper packaging materials. No organic solvent was used and the matrix effect was investigated. The extract was directly analyzed by liquid chromatography with tandem mass chromatography for quantification and confirmation. The chromatographic separations were performed on a ZORBAX HILIC Plus (2.1 mm × 150 mm, 3μm; Agilent, USA) column with only one mobile phase (100% water). Calibration curves for acrylamide and trimethylopropane were achieved with concentrations ranging from 0.4 to 20 mg/kg and the corresponding r² values were 0.998 and 0.999, respectively. The recoveries were >85% with relative standard deviations <10%. The validated method was applied to the analysis of 50 real samples, and positive results were obtained for 30 samples. The result indicated that trimethylolpropane is associated with inks and printing activity and acrylamide is widely used as a papermaking additive in many paper packages. The concentrations of acrylamide and trimethylolpropane ranged from 0.41 to 7.5 and 0.50 to 8.8 mg/kg, respectively. The results of this study revealed that this method could be used accurately and precisely.     

丙烯酸铈(Ⅲ)-丙烯酸丁酯对明胶的接枝共聚鞣制

以（ＮＨ４）２Ｓ２Ｏ８－ＮａＨＳＯ３作引发剂,用丙烯酸丁酯和丙烯酸铈（Ⅲ）对明胶进行乳液接枝共聚鞣制。考察了乳化剂种类及用量、介质ＰＨ值,乳液固含量和离子浓度等因子对反应及乳液稳定性的影响,通过对合成聚合物与明胶结全形式的研究,探讨了接枝共聚鞣制的机理。