Comprehensive performance of a ball-milled La0.5Pr0.5Fe11.4Si1.6B0.2Hy/Al magnetocaloric composite

Due to the hydrogen embrittlement effect, La(Fe,Si)₁₃-based hydrides can only exist in powder form, which limits their practical application. In this work, ductile and thermally conductive Al metal was homogeneously mixed with La_0.5Pr_0.5Fe_11.4Si_1.6B_0.2 using the ball milling method. Then hydrogenation and compactness shaping of the magnetocaloric composites were performed in one step via a sintering process under high hydrogen pressure. As the Al content reached 9 wt.%, the La_0.5Pr_0.5Fe_11.4Si_1.6B_0.2H_y/Al composite showed the mechanical behavior of a ductile material with a yield strength of ~44 MPa and an ultimate strength of 269 MPa accompanied by a pronounced improvement in thermal conductivity. Due to the ease of formation of Fe-Al-Si phases and the several micron and submicron sizes of the composite particles caused by ball milling process, the magnetic entropy change of the composites was substantially reduced to ~1.2 J/kg· K-1.5 J/kg· K at 0 T-1.5 T.     

Concise synthesis of dopexamine dihydrochloride via benzyl protecting protocol

Benzyl protecting protocol was first employed in two routes for the concise synthesis of dopexamine dihydrochloride.This protecting group could be cleanly removed under mild condition and no unacceptable ion was brought to the final product.The total yield of route I was 43.8% from phenylacetic acid,while it was 54.1% of route II from 2-(3,4-bis(benzyloxy)phenyl)acetic acid.The titration purity of the final product was more than 99.5%,while any single or total impurities met the known standard of the drug by HPLC analysis.The measured residual palladium met an acceptable limit(<1 ppm) as an API for injection.     

Catalytic amplification based on hole-transporting materials as efficient metal-free electrocatalysts for non-enzymatic glucose sensing

Hole-transporting materials with tunable structures and properties are mainly applied in organic light-emitting diodes as transport layer. But their catalytic properties as signal amplifiers in biological assays are seldom reported. In this paper, a starburst molecule, 4,4,4″-tri(N-carbazolyl)-triphenylamine (TCT), containing a triphenylamine as the central core and three carbazoles as the peripheral functional groups was designed and synthesized. Subsequently, the hole-transporting material based on the TCT polymer, poly(TCT) (PTCT), was achieved via a low-cost electrochemical method and exploited as an efficient metal-free electrocatalyst for non-enzymatic glucose detection. Here, this hole-transporting material served three purposes: electrochemical recognition (owing to hydrogen bonding interaction and the biomimetic microenvironment created by the polymer), electrocatalysis (owing to the hole-transporting capability of triphenylamine and the catalytic property of carbazole), and signal amplification (owing to energy migration along the conductive polymer backbone). The electrocatalytic and sensing performances of the sensor based on PTCT were evaluated in detail. Results revealed that the PTCT film could efficiently catalyze the oxidation of glucose at a less-positive potential (+0.20 V) in the absence of any enzymes. The response to glucose was linear in the concentration range of 1.0–6000 μM, and the detection limit was 0.20 μM. With good stability and selectivity, the proposed sensor could be feasibly applied to detect glucose in practical samples. The encouraging sensing performances suggest that the hole-transporting material is one of the promising biomimetic catalysts for electrocatalysis and relevant fields.     

Toward Understanding the Enhanced Pseudocapacitive Storage in 3D SnS/MXene Architectures Enabled by Engineered Surface Reactions

The optimization of three-dimensional (3D) MXene-based electrodes with desired electrochemical performances is highly demanded. Here, a precursor-guided strategy is reported for fabricating the 3D SnS/MXene architecture with tiny SnS nanocrystals (≈5 nm in size) covalently decorated on the wrinkled Ti₃C₂T_x nanosheets through Ti−S bonds (denoted as SnS/Ti₃C₂T_x-O). The formation of Ti−S bonds between SnS and Ti₃C₂T_x was confirmed by extended X-ray absorption fine structure (EXAFS). Rather than bulky SnS plates decorated on Ti₃C₂T_x (SnS/Ti₃C₂T_x-H) by one-step hydrothermal sulfidation followed by post annealing, this SnS/Ti₃C₂T_x-O presents size-dependent structural and dynamic properties. The as-formed 3D hierarchical structure can provide short ion-diffusion pathways and electron transport distances because of the more accessible surface sites. In addition, benefiting from the tiny SnS nanocrystals that can effectively improve Na⁺ diffusion and suppress structural variation upon charge/discharge processes, the as-obtained SnS/Ti₃C₂T_x-O can generate pseudocapacitance-dominated storage behavior enabled by engineered surface reactions. As predicted, this electrode exhibits an enhanced Na storage capacity of 565 mAh g⁻¹ at 0.1 A g⁻¹ after 75 cycles, outperforming SnS/Ti₃C₂T_x-H (336 mAh g⁻¹), SnS (212 mAh g⁻¹), and Ti₃C₂T_x (104 mAh g⁻¹) electrodes.     

Influence of β-cyclodextrin complexation on photochemistry of bisphenols in aqueous solutions

1. Download : Download high-res image (117KB)
2. Download : Download full-size image

     

基于LIBS技术的水泥粉末在线成分分析

在工业现场生产水泥的过程中，各种成分的含量直接影响着水泥的质量，因此如何快速准确地监测水泥中各个成分的含量意义重大。采用的实验方式为，将不经过任何预处理的水泥粉末直接放入位于二维移动平台上的物料盒中，通过激光诱导击穿光谱(LIBS)直接对水泥粉末表面的不同位置进行激发检测，对得到的光谱数据首先进行归一化和主成分分析等预处理操作，然后针对水泥中Ca, Si, Al, Fe, Mg五种元素，分别建立偏最小二乘(PLS)和支持向量回归(SVR)两种定量分析模型进行方法比较。此外，对比了粉末状水泥与压片式水泥两种测量方式的结果。实验结果表明，采用粉末状水泥直接测量的方式下，针对水泥样品元素浓度与所得到的光谱中特征线强度的关系，SVR方法比PLS方法更具优势，粉末状水泥直接测量的精度接近压片式测量的精度，说明LIBS技术对水泥粉末状样品直接在线测量具有可行性。     

A concise synthesis of 3-substituted-7-amino-6-carboxyl-8-azachromones

We report on an approach to truncate the tricyclic 5H-chromeno[2,3-b]pyridin-5-one core of amlexanox, an approved drug under investigation for the treatment of obesity, to the bicyclic 4H-pyrano[2,3-b]pyridin-4-one (8-azachromone) core. A short, concise synthesis generates a key intermediate with requisite functionality on the pyridyl A-ring and iodo functionality on the 4-pyrone B-ring upon which palladium-catalyzed cross-coupling and subsequent reactions generate representative analogues. One of these shows a 14.2-fold increase in aqueous solubility over amlexanox.