MoO2微米空心球的水热合成及合成机理研究

Micrometer-sized MoO2 hollow spheres were synthesized hydrothermally with ammonium heptamolybdate tetrahydrate as molybdenum source, Cetyltrimethylammonium bromide as structure-directing agent and C2H5OH as reducing agent, respectively. The products were investigated by X-ray diffraction, thermo- gravimetry and differential thermal analysis, scanning electron microscopy, transmission electron microscopy and X-ray photoelectron spectroscopy. A morphology transition of "blocks-solid spheres-hollow spheres" during the growth process was observed and the possible mechanism for the formation of MoO2 samples was proposed to be through a microscale Kirkendall effect.     

四氧化三钴粉末的沉淀法制备及表征

以硝酸钴为钴源,碳酸铵为沉淀剂,采用沉淀法制备四氧化三钴粉体。采用TG、XRD、IR、激光粒度分析仪等对前驱体碱式碳酸钴和产物四氧化三钴进行了表征及分析。研究了焙烧温度、反应物浓度和反应时间等因素对产物的影响。     

MoO2微米空心球的水热合成及合成机理研究

在阳离子表面活性剂的作用下,以钼酸铵为钼源,乙醇作为还原剂合成了微米级MoO2空心球．采用X射线粉末衍射、热重-差热、扫描电子显微镜、透射电镜和X射线光电子能谱对合成的样品进行了表征,并对MoO2空心球可能的形成机理进行了讨论.在MoO2空心球的形成过程中,发现了样品从“大块-实心球-空心球”的形貌转化过程,空心球的形成机理可用微米尺度的Kirkendall效应解释．     

高质量AIP04-5分子筛大单晶的合成与表征

以拟薄水铝石作为铝源，正磷酸为磷源，正三丙胺(TPA)作模板剂，采用水热法合成了AIPO4-5分子筛．在不同的反应物配比、温度以及晶化时间条件下，得到了不同尺寸的AIPO4-5分子筛单晶．实验表明，反应物质的摩尔比为Al2O3：P2O5：TPA：C2H5OH：H2O：HF=1：1．2：2．66：80：1000：0．7，反应温度为457K，晶化时间48h是生成六方AIPO4-5分子筛大单晶较适宜的条件；在该反应条件下合成出纵向尺度最大达到2．0mm、具有完整六方棱柱形态的MPO4-5分子筛单晶；部分晶体的横向尺度达到0．31mm．用扫描电镜观察晶体的形貌：AlPO4-5分子筛晶体结构通过SMART1000单晶衍射仪鉴定．     

高质量AlPO4-5分子筛大单晶的合成与表征

以拟薄水铝石作为铝源,正磷酸为磷源,正三丙胺(TPA)作模板剂,采用水热法合成了AlPO4 5分子筛.在不同的反应物配比、温度以及晶化时间条件下,得到了不同尺寸的AlPO4 5分子筛单晶.实验表明,反应物质的摩尔比为Al2O3∶P2O5∶TPA∶C2H5OH∶H2O∶HF=1∶1. 2∶2. 66∶80∶1000∶0. 7,反应温度为457K,晶化时间48h是生成六方AlPO4 5分子筛大单晶较适宜的条件;在该反应条件下合成出纵向尺度最大达到2. 0mm、具有完整六方棱柱形态的AlPO4 5分子筛单晶;部分晶体的横向尺度达到0. 31mm.用扫描电镜观察晶体的形貌;AlPO4 5分子筛晶体结构通过SMART1000单晶衍射仪鉴定.