焊后热处理对聚变堆用奥氏体不锈钢MAG焊焊缝金属冲击韧性的影响

After heat treatment of metal active gas arc welding (MAG weld) joints of 316LN austenitic stainless steel for fusion reactor at different temperatures, Charpy impact test at liquid nitrogen temperature was carried out. The effects of heat treatment temperature on microstructure, fracture morphology and precipitates were studied with optical microscope, SEM and EDS analysis. Results indicated that the impact toughness of weld metal could be significantly improved by 873K heat treatment. However, with the rising of heat treatment temperature, the precipitates were generated gradually along the grain boundary and a gradual decrease of toughness occurred as well. All fracture was ductile. The dimple became shallow and less with the increase of temperature. Spherical and irregular precipitates were found at the bottom of the dimple. The spherical precipitates generated during welding were free from the influence of the heat treatment, and the irregular precipitates increased with the rising of temperature. High content of Mo in filler materials led to a great segregation of Mo at the grain boundary, which would promote the precipitation of σ phase. Impact toughness of weld metal decreased significantly when continuous distribution of σ phase formed at grain boundary.     

DNA环境中硒代胸腺嘧啶和腺嘌呤碱基对的激发态性质和光物理机理的理论研究

应用高精度的多态完全活化自洽场二级微扰理论方法, 在量子力学/分子力学组合方法的理论框架 QM(MS-CASPT2//CASSCF)/MM下, 系统研究了DNA环境中2-硒和4-硒取代胸腺嘧啶和腺嘌呤碱基对(2SeT-A和4SeT-A)的最低5个电子态(S₀, S₁, S₂, T₂和T₁)的结构、 性质和光物理过程. QM(MS-CASPT2//CASSCF)/MM计算揭示了DNA环境中2SeT-A和4SeT-A碱基对激发态性质和光物理过程差异性的来源, 提出的机理将有助于理解DNA类似物的光物理过程, 在光动力学治疗中具有潜在的应用.     

IPET:测定独个生物大分子三维空间结构的实验方法

蛋白质的动态特性和结构活性对于蛋白质功能的调控具有根本意义。传统的结构确定方法(包括X射线和电子显微镜单颗粒分析技术等)往往需要成千上万不同蛋白质分子的平均信号,因此难以确定蛋白质分子的动态结构。而电子显微断层成像技术是一种对独个生物个体结构从不同的观测角度照相、并计算来恢复该个体的三维结构密度图的方法。传统的冷冻电子断层成像重构方法采用整个大尺寸电镜图像进行重构计算,通常用来研究细菌、细胞切片等大尺寸生物个体在较低分辨率下的结构;由于分辨率的限制,不足以获得小尺寸的蛋白质分子的结构细节。最近,任罡研究小组提出一种独个生物颗粒的电子显微断层成像方法(individual-particle electron tomography,IPET)。该方法通过减小图像尺寸(直至所选区域只包含单个蛋白质分子)的策略,运用提出的FETR(focused electron tomography reconstruction)算法来提高独个大分子重构的分辨率。此方法不需要初始模型和大量分子的平均信号,同时能够容忍一定的测角误差。本文综述了IPET/FETR方法在确定独个分子结构过程中的具体步骤以及如何应用该方法来研究蛋白动态特性和结构变化特征。期望通过该综述和国内同行交流,分享最新的前沿研究,为赶超世界科技前沿的建设添砖加瓦。     

螺旋形超导带材的直流冲击实验研究

基于超导直流电缆应用,针对第二代高温超导带材Re BCO开展了直流冲击实验。首先,通过改变冲击条件(冲击电流大小和持续时间)得到带材的耐直流冲击特性,确定可保证带材性能完好的最大冲击电流幅值(安全电流)及其相应冲击时间。随后,针对实际电缆中超导带材是以螺旋形态缠绕于支撑管上,设计实验研究超导带材螺旋角和螺旋直径对其临界电流和耐冲击特性的影响规律,发现带材所能承受的最大冲击电流幅值随冲击作用时长的增加而逐渐下降、过大的螺旋角和过小的螺旋直径均会对带材造成损伤,影响其通流能力。上述研究结果为电缆的后续设计和制造提供了必要的参考依据。     

2-硝基萘激发态衰减动力学和光解通道的从头计算研究

采用密度泛函理论(DFT)和完全活化空间自洽场理论(CASSCF)计算方法,在CASSCF(10,10)/6-31G(d)//CASPT2(10,10)/Aug-cc-PVDZ计算水平下,研究了2-硝基萘(2NN)S1(ππ*)激发态的衰减动力学.获得了2NN及其亚硝酸酯异构体(ISO)的基态、低能激发态和势能面交叉点的优化结构和能量,以及异构化反应的过渡态结构和能垒;给出了S0,T1和S1态时ISO沿N—O键的势能曲线;描绘了激发态衰变路径图.结果表明,被激发至S1(ππ*)激发态后,2NN经S1T3,S1T2交叉点发生S1!T3,S1!T2系间窜越过程再经T2T1锥形交叉点发生T2!T1内转换过程,最后无辐射衰减到T1态.具体衰减路径可以描述为S1-FC-2NN!S1T3-MIN-2NN或S1T2-MIN-2NN!T3-MIN-2NN或T2-MIN-2NN!T2T1-MIN-2NN!T1-MIN-2NN.该条路径能垒较小,T1态瞬态物种形成效率较高,为2NN激发态衰变动力学中最重要的无辐射衰变通道.在S0,T1和S1态势能面上,2NN!ISO异构化反应的能垒高,跃迁概率十分低下,难以形成芳氧自由基(Ar O"),2NN紫外光解离效率很低.     

ITER ���򳡴���֧��U �����Լк��ӷ����Ż�

利用试验及数值模拟技术研究了ITER 极向场磁体支撑U 型韧性夹的焊接变形规律,模拟和实际测量的比较验证了模拟的准确性,从而得到了U 型夹焊缝变形的基本规律,并改进现有夹具类型。基于验证好的热力边界条件以及优化的夹具,对三种焊接方案的U 型韧性夹的焊接变形进行了计算,从而提出了极向场磁体支撑制造的优化方案。优化后的焊接方案将焊接变形控制在0.6mm 以内。     

新型镍离子亲和色谱介质的制备及其性能考察

以氯甲基化聚苯乙烯交联微球(氯球)为载体基质、N,N-二甲基甲酰胺(DMF)为溶剂、N,N-二异丙基乙胺(DIEA)催化,将合成的Lys(Boc)-OEt、氯乙酸乙酯连接到微球上。经水解使羧基裸露,与Ni²⁺螯合,制得新型镍离子亲和色谱介质。将其应用于His-Lys-Tyr三肽及Phe-His-Thr三肽纯化研究。以不含组氨酸的六肽作为杂质模型,用所制备的镍离子亲和介质进行分离。结果表明,所制备的镍离子亲和介质对两个含组氨酸的三肽具有很好的亲和作用,并实现了与不含组氨酸六肽的分离。     

ITER 极向场磁体支撑U 型韧性夹焊接方案优化

利用试验及数值模拟技术研究了ITER 极向场磁体支撑U 型韧性夹的焊接变形规律,模拟和实际测量的比较验证了模拟的准确性,从而得到了U 型夹焊缝变形的基本规律,并改进现有夹具类型。基于验证好的热力边界条件以及优化的夹具,对三种焊接方案的U 型韧性夹的焊接变形进行了计算,从而提出了极向场磁体支撑制造的优化方案。优化后的焊接方案将焊接变形控制在0.6mm 以内。     

纳米金/石墨烯复合膜修饰电极检测异烟肼

先采用滴涂法制备了石墨烯修饰电极(GR/GCE),然后采用电化学方法将纳米金沉积于石墨烯表面制备了纳米金/石墨烯复合材料修饰电极(Au NPs/GR/GCE)。研究了异烟肼(isoniazid,INZ)在该Au NPs/GR/GCE上的电化学行为。结果表明,异烟肼在该修饰电极上有良好的电化学响应。在优化条件下,线性扫描伏安法测定异烟肼的线性范围为1.0×10-7~1.0×10-4mol/L,检出限为5.0×10-8mol/L(S/N=3)。用该法测定了异烟肼注射液中异烟肼的含量,结果令人满意。     

掺杂Y2O3和BaCeO3提高MOD-YBCO超导性能的研究

本文通过在前驱液中添加过量钇盐和铈的有机盐,采用三氟乙酸盐-金属有机沉积法(TFA-MOD) 在铝酸镧单晶基体上制备了含有纳米氧化钇和纳米铈酸钡的YBCO薄膜. 与纯YBCO薄膜相比,掺杂Y₂O₃/BaCeO₃的YBCO膜的临界转变温度几乎保持不变,为91 K左右. 而掺杂Y₂O₃/BaCeO₃的YBCO膜的临界电流密度达到5.0 MA/cm² (77 K, 0T), 是纯YBCO膜临界电流密度的1.5倍.薄膜中的Y₂O₃和BaCeO₃可能在YBCO内部起到了 有效的钉扎磁通作用. 关键词： 钇钡铜氧薄膜 2O₃和纳米BaCeO₃')" href="#">纳米Y₂O₃和纳米BaCeO₃ 磁通钉扎 三氟乙酸盐-金属有机沉积