铋化物发光玻璃中银表面等离激元对铒离子的发光增强作用

局域表面等离激元可以由自由空间的光直接激发,这也是局域表面等离激元的优点所在。研究铋化物发光玻璃中纳米银颗粒的表面等离激元对铒离子发光的增强效应、进一步的提高铋化物发光玻璃中铒离子的发光性能很有意义。首先,测量了(A)Er 3+(0.5%)Ag(0.5%):铋化物发光玻璃与(B)Er 3+(0.5%):铋化物发光玻璃样品的吸收谱,发现(A)Er 3+(0.5%)Ag(0.5%):铋化物发光玻璃在约600.0 nm处有一个较弱的宽的银表面等离激元共振吸收峰。同时发现两者都有典型的铒离子的吸收峰,它们的吸收几乎完全一样:在波峰形状、峰值强度和峰值波长等方面都很相近。测量了(A)Er 3+(0.5%)Ag(0.5%):铋化物发光玻璃和(B)Er 3+(0.5%):铋化物发光玻璃样品的激发谱,发现有位于379.0,406.0,451.0,488.0和520.5 nm的5个550.0 nm可见光的可见激发谱峰,和位于379.0,406.5,451.0,488.5,520.5,544.0,651.5和798.0 nm的8个1531.0 nm红外光的红外激发谱峰,容易指认出依次为Er 3+的4I 15/2→4G 11/2,4I 15/2→2H 9/2,4I 15/2→(4F 3/2,4F 5/2),4I 15/2→4F 7/2,4I 15/2→2H 11/2,4I 15/2→4S 3/2,4I 15/2→4F 9/2和4I 15/2→4I 9/2跃迁的吸收峰,通过测量发现(A)Er 3+(0.5%)Ag(0.5%):铋化物发光玻璃相对于(B)Er 3+(0.5%):铋化物发光玻璃样品的可见和红外激发谱的最大增强依次分别是238%和133%。最后,测量了它们的发光谱,发现有位于534.0,547.5和658.5 nm的三组可见发光峰,容易指认出依次为Er 3+的2H 11/2→4I 15/2,4S 3/2→4I 15/2,4F 9/2→4I 15/2荧光跃迁。还发现红外发光峰位于978.0和1531.0 nm,依次为Er 3+的4I 11/2→4I 15/2和4I 13/2→4I 15/2的荧光跃迁。通过测量发现(A)Er 3+(0.5%)Ag(0.5%):铋化物发光玻璃相对于(B)Er 3+(0.5%):铋化物发光玻璃样品的可见和红外发光谱的最大增强依次分别是215%和138%。对于银表面等离激元增强铒离子发光的机理,认为主要为纳米银颗粒的局域表面等离激元共振,造成金属纳米结构附近产生的局域电场的强度要远大于入射光的电场强度,从而导致了金属纳米结构对入射光产生强烈的吸收和散射,进而导致了荧光的增强;即局域表面等离子体共振局域场的场增强效应。     

千金子油理化性质及其脂肪酸和挥发油成分分析

对千金子油理化性质进行了系统的分析测试,并利用气相色谱法分析了千金子油脂肪酸及千金子挥发油,结果表明,千金子油中油酸含量最高占78.158%,其次是软脂酸、硬脂酸,分别为8.513%和5.523%;千金子挥发油中油酸、亚油酸和油酸-2-丙三醇酯含量较高,分别为17.747%,15.852%和13.196%.     

高功率激光运转条件下大模场掺镱石英光纤模式特性的仿真研究

在高功率激光运转条件下,掺杂稀土离子的量子亏损和玻璃材料的本征吸收均会造成光纤放大器中增益光纤温度的整体上升与梯度分布。在热平衡状态下,光纤材料的热光效应将会诱导光纤横向折射率的再分布,引发高功率激光运转条件下增益光纤模式特性的改变。为此,利用多物理场有限元建模的数值计算方法对高功率激光运转条件下大模场掺镱石英光纤的热致模式特性展开系统研究,分析总结大模场增益光纤的模式特性在不同激光运转功率、增益光纤设计参数(纤芯直径、数值孔径、热光系数)和光纤弯曲使用条件下的变化规律。结果表明,随着激光运转功率的增加,纤芯和包层之间的温差会变大,从而导致光纤的归一化参数V值增大,最终使模式的传输损耗系数减小,模式在纤芯区域的功率因子增大。     

含纳米晶颗粒的Yb3+/Er3+共掺透明碲酸盐玻璃陶瓷的光谱性质研究

在组成为15Li2O-15Nb2O5-70TeO2-0.1Er2O3-0.4Yb2O3（%, 摩尔分数）的碲酸盐玻璃基础上, 采用两步热处理法制备了透明的含纳米晶颗粒碲酸盐玻璃陶瓷. 通过X射线衍射（XRD）测试表明, 玻璃陶瓷中的晶体颗粒组成为Yb6Te5O19.2或Er6Te5O19.2, 晶粒尺寸约为55 nm. 根据Judd-Ofelt理论计算了Er^3＋离子在基质玻璃和玻璃陶瓷中的光谱参数Ωt（t＝2, 4, 6）以及Er^3＋：4I15/2→4I13/2跃迁自发辐射几率, 根据McCumber理论计算了Er^3＋：4I13/2→4I15/2跃迁的发射截面. 测试了基质玻璃和玻璃陶瓷的拉曼光谱, 对比研究了铒离子在基质玻璃和玻璃陶瓷中1.5 μm处荧光和上转换光谱特性.     

铒离子浓度对掺Er3+碲酸盐玻璃的Judd-Ofelt理论参数的影响

制备了四种不同铒离子掺杂浓度的碲酸盐玻璃,通过测定吸收光谱计算了吸收谱线的振子强度,根据Judd-Ofelt理论计算了不同浓度下Er3 离子发光光谱的强度参数Ωi(i=2,4,6),计算了自发辐射电偶和磁偶跃迁概率、辐射寿命、荧光分支比等参数,讨论了Er3 离子浓度变化对以上这些参数的影响.测试了Er3 :4I13/2→4I15/2跃迁对应的荧光光谱和Er3 :4I13/2能级荧光寿命.最后应用McCumber理论计算了玻璃中Er3 :4I13/2→415/2跃迁对应的受激发射截面大小.结果表明:振子强度基本上随Er3 离子浓度的增大而增强;随着Er3 离子浓度的增加,自发辐射跃迁概率A基本呈现出递增的趋势,但荧光分支比β却只有很小的变化;Er3 :4I13/2→4I15/2的发射截面随Er3 离子浓度的增大而改变很小,有效线宽都在50 nm左右.     

272 W quasi-single-mode picosecond pulse laser of ytterbium-doped large-mode-area photonic crystal fiber

A large-mode-area(LMA) ytterbium-doped photonic crystal fiber(PCF) with core NA of 0.034 and core diameter of 50 μm was made by the stack-and-draw technique. The core is formed by Yb~(3+)/Al~(3+)/F-/P~(5+) co-doped silica glass containing 0.09 mol% Yb_2O_3 with an absorption coefficient at 976 nm up to 3.2 d B/m. The core glass with homogeneous distribution of Yb~(3+) ions and refractive index difference of 4 × 10~(-4) compared with pure silica was prepared by the sol-gel method and heat homogenization at 2000°C. Laser power amplification of this LMA PCF was studied using a seed source of 21 ps pulse duration and 48.7 MHz repetition rate at 1030 nm wavelength. With pump power of 520 W, a maximum 272 W(266 k W peak power) quasi-single-mode laser output with M~2 of 2.2 was achieved in a 4.7 m fiber length bent at a diameter of 47 cm with slope efficiency of 52%, and no obvious mode instability, stimulated Raman scattering, or thermal damage on the end facet of the fiber were observed.     

掺铒的纳米相氟氧化物玻璃陶瓷的多光子红外量子剪裁

研究了掺铒的纳米相氟氧化物玻璃陶瓷(Er(3):FOV)的红外量子剪裁现象,测量了红外和可见的Er(3):FOV的荧光光谱.结果发现光激发²H_11/2能级的⁴ I_13/2→⁴I_15/2荧光跃迁的近似量子剪裁效率已达约186.28%.计算了有关的无辐射弛豫速率、自发辐射速率和能量传递速率,分析了有关的能量传递动力学过程,发现     

A Novel Ce3＋/Tb3＋ Codoped Phosphate Glass as Down-Shifting Materials for Enhancing Efficiency of Solar Cells

For the purpose of improving conversion efficiency of solar cells by applying the effect of the wavelength conversion of rare earth ions, photo-luminescence and excitation spectrums of Ce3＋-Tb3＋ doped phosphate glass are investigated. Results show that incorporating Ce3＋ ions to Tb3＋-doped phosphate glass can greatly increase the absorption coefficient in the range 300-400 nm and then the energy transfer （ET） from Ce3＋ to Tb3＋ occurs. In addition, increasing Tb3＋ concentration in Ce3＋/Tb3＋ co-doped phosphate glass can greatly enhance the ET efficiency and 545 nm emission intensity. This shows that Ce3＋/Tb3＋ co-doped phosphate glass would be a promising down-shifting material for enhancing the efficiency of solar cells.     

Watt-level Yb-doped silica glass fiber laser with a core made by sol-gel method

A Yb-doped silica glass fiber laser with a core made by sol-gel method is reported. The maximum power of 1.14 W is obtained with a pump power of 5.46 W at a wavelength of 976 nm. The slope efficiency is 34%. The refractive index fluctuation across the core is below 5×10^-4 at a doping level of Yb 0.15 mol%, A203 4.0 mol%, and P2O5 2.0 mol%. High background attenuation of 6 dB/m at 1 053 nm limites the slope efficiency and maximum output power.     

氟氧化物玻璃陶瓷中铒激活中心的双光子三光子与四光子近红外量子剪裁发光

研究了掺铒的氟氧化物玻璃陶瓷的双光子、三光子与四光子近红外量子剪裁发光.我们测量了掺铒的氟氧化物玻璃陶瓷的X 射线衍射谱、吸收谱、从可见到近红外的发光光谱与激发光谱.当Er3+浓度从0.5％增加到2.0％,发现铒离子的4I15/2→2G7/2,4I15/2→4G9/2,4I15/2→4G11/2,4I15/2→2H9/2,4I15/2→(4F3/2,4F5/2),4I15/2→4F7/2,4I15/2→2H11/2,4I15/2→4S3/2,4I15/2→4F9/2,与4I15/2→4I9/2红外激发谱峰的强度增加了大约5.64,4.26,2.77,7.31,6.76,4.75,2.40,11.14,2.88,和4.61倍,同时,铒离子的4I15/2→2G7/2,4I15/2→4G9/2,4I15/2→4G11/2,4I15/2→2H9/2,4I15/2→(4F3/2,4F5/2),与4I15/2→4F7/2的可见激发谱峰的强度减小了1.36,1.93,3.43,1.01,2.24和2.28倍.也就是说我们发现红外发光与激发的强度都增强了2～11倍,与此相伴的可见的发光与激发强度都减小了一到三倍.而且,1 543.0与550.0 nm发光的激发谱不仅在峰值波长而且也在波峰形状上非常相近.上述实验结果证实了所看到的现象为多光子近红外量子剪裁发光现象.为了更好的分析量子剪裁的过程与机理,还测量了主要的可见与红外发光强度随激发强度的改变;发现所有可见和红外发光强度都基本上是随激发强度成线性变化关系;其中,可见的发光强度随激发强度的改变呈略大于线形一次幂的变化关系,它是由于小的激发态吸收造成的;而1 543.0 nm红外发光强度随激发强度的变化呈略小于线形一次幂的变化关系,它即是量子剪裁发光的特征现象.还发现4I9/2能级的双光子量子剪裁主要由{4I9/2→4I13/2,4I15/2→4I13/2} ETr31-ETa01交叉能量传递所导致;4S3/2能级的三光子量子剪裁主要由{4S3/2→4I9/2,4I15/2→4I13/2} ETr53-ETa01和{4I9/2→4I13/2,4I15/2→4I13/2} ETr31-ETa01交叉能量传递所导致;2H9/2能级的四光子量子剪裁主要由{2H9/2→4I13/2,4I15/2→4S3/2} ETr91-ETa05,{4S3/2→4I9/2,4I15/2→4I13/2} ETr53-ETa01和{4I9/2→4I13/2,4I15/2→4I13/2} ETr31-ETa01交叉能量传递所导致.上述研究结果对目前的全球热点新一代量子剪裁太阳能电池很有价值.