现代分析仪器在高中化学教学中的应用*——以“防晒霜的防晒效果实验探究”为例

从高中化学原子、分子等抽象性的知识教学出发,以防晒霜的防晒效果实验探究为例,探讨了现代分析仪器在高中化学教学中的应用。通过利用现代分析仪器紫外可见分光光度计,结合紫外线变色球实验探究防晒霜的防晒效果,分析并认识防晒霜中化学防晒的机理。结果表明,防晒霜的厚度越大、SPF越高,防晒霜的防晒效果越好,并且防晒霜的防晒效果可以持续一段时间,但是不同类型的防晒产品存在一定差异。在化学教学中渗透现代分析仪器的应用,为学生进一步了解化学学科在改变学习方式、拓宽学科知识领域、推动自身全面与可持续发展方面打下坚实的基础。     

中空介孔SiO2纳米球的制备、改性及其对Al3+荧光识别研究

中空介孔SiO2由于中空多孔的结构而常用作功能材料的基底.将中空介孔SiO2进行官能团修饰,并应用为荧光传感材料是中空介孔SiO2一个重要的研究领域.本论文采用聚丙烯酸(PAA)为中空模板,聚醚F127为造孔剂,正硅酸乙酯(TEOS)为硅源,氨水为催化剂在乙醇体系中制备了中空介孔SiO2纳米球.系统研究了搅拌速度和聚醚F127引入量对中空介孔SiO2纳米球形貌及比表面积的影响.通过透射电镜、N2-等温吸附脱附曲线等表征说明该合成方法具有很好的普适性,通过调节F127的引入可以实现对比表面积的有效控制.通过氨基化、席夫碱反应进行荧光修饰,进一步研究表明荧光修饰后的中空介孔SiO2纳米球在水溶液中能够实现对Al3+的有效检测,检测限为1.19×10 -7M.     

基于NiCo2O4纳米片电极的非对称混合电容器

The looming global energy crisis and ever-increasing energy demands have catalyzed the development of renewable energy storage systems. In this regard, supercapacitors (SCs) have attracted widespread attention because of their advantageous attributes such as high power density, excellent cycle stability, and environmental friendliness. However, SCs exhibit low energy density and it is important to optimize electrode materials to improve the overall performance of these devices. Among the various electrode materials available, spinel nickel cobaltate (NiCo₂O₄) is particularly interesting because of its excellent theoretical capacitance. Based on the understanding that the performances of the electrode materials strongly depend on their morphologies and structures, in this study, we successfully synthesized NiCo₂O₄ nanosheets on Ni foam via a simple hydrothermal route followed by calcination. The structures and morphologies of the as-synthesized products were characterized by X-ray diffraction, scanning electron microscopy, and Brunauer-Emmett-Teller (BET) surface area analysis, and the results showed that they were uniformly distributed on the Ni foam support. The surface chemical states of the elements in the samples were identified by X-ray photoelectron spectroscopy. The as-synthesized NiCo₂O₄ products were then tested as cathode materials for supercapacitors in a traditional three-electrode system. The electrochemical performances of the NiCo₂O₄ electrode materials were studied and the area capacitance was found to be 1.26 C·cm^-2 at a current density of 1 mA·cm^-2. Furthermore, outstanding cycling stability with 97.6% retention of the initial discharge capacitance after 10000 cycles and excellent rate performance (67.5% capacitance retention with the current density from 1 to 14 mA·cm^-2) were achieved. It was found that the Ni foam supporting the NiCo₂O₄ nanosheets increased the conductivity of the electrode materials. However, it is worth noting that the contribution of nickel foam to the areal capacitance of the electrode materials was almost zero during the charge and discharge processes. To further investigate the practical application of the as-synthesized NiCo₂O₄ nanosheets-based electrode, a device was assembled with the as-prepared samples as the positive electrode and active carbon (AC) as the negative electrode. The assembled supercapacitor showed energy densities of 0.14 and 0.09 Wh·cm^-3 at 1.56 and 4.5 W·cm^-3, respectively. Furthermore, it was able to maintain 95% of its initial specific capacitance after 10000 cycles. The excellent electrochemical performance of the NiCo₂O₄ nanosheets could be ascribed to their unique spatial structure composed of interconnected ultrathin nanosheets, which facilitated electron transportation and ion penetration, suggesting their potential applications as electrode materials for high performance supercapacitors. The present synthetic route can be extended to other ternary transition metal oxides/sulfides for future energy storage devices and systems.     

基于有序介孔碳的氯离子选择性电极的制备及其在手持传感系统中的应用

以有序介孔碳(OMC)球为离子-电子转换层,制备了固态氯离子选择性电极,构建了基于离子敏感的场效应晶体管(ISFET)的手持式传感系统,用于检测人体血清中的氯离子。优化了OMC前驱体的碳化温度,探究了OMC形貌结构对电极传感性能的影响;电极柔性化制备后考察了其在手持系统中对氯离子的检测效果。结果表明,最优条件下,电极在5.12×10^-4~1.02 mol/L的浓度范围呈现线性响应,响应斜率为60 mV/decade。该柔性电极在手持传感系统中展现出高灵敏度和重现性,可用于人体血清样品中氯离子的检测,其回收率为96.3%~104.9%。     

单分散键合型含铕聚苯乙烯微球的制备与荧光传感性能

制备了一种可定性定量检测水溶液中三价铁离子的含铕聚苯乙烯微球, 分别用固体核磁碳谱(¹³C CP/MAS NMR)、 傅里叶变换红外光谱(FTIR)、 X射线光电子能谱(XPS)、 扫描电子显微镜(SEM)、 透射电子显微镜(TEM)、 元素分析、 粒度分析和ζ电位分析等对其化学组成和结构形貌进行表征. 当铕配合物单体用量低于2.5%时, 可以得到稳定的单分散键合型含铕聚苯乙烯微球. 用紫外光激发时, 该含铕聚苯乙烯微球发射铕离子的特征红光. Fe³⁺能猝灭该微球的荧光, 酸根离子和其它金属离子对其干扰较少; 猝灭效率与Fe³⁺浓度在0~300 μmol/L浓度范围内均呈线性关系; 随着铕配合物单体用量的增加, 微球的荧光增强, 其在检测Fe³⁺的荧光时, 猝灭常数(K_SV)增加, 检测限(LOD)下降. 调节铕配合物单体的用量, 可获得热性能优异、 红光发射强度高且稳定性好的单分散聚苯乙烯荧光微球, 对Fe³⁺荧光检测显示出较高的选择性, 在生物检测和环境保护等领域具有较高的应用价值.     

Pd/PdO纳米复合微球的合成及催化性能

采用甲基丙烯酸锌加速还原氯化钯(PdCl₂) 溶液中的钯离子(Pd ²⁺)为钯(Pd) 纳米微球, 进而用得到的钯纳米微球直接制备钯/氧化钯(Pd/PdO) 纳米复合微球. 通过扫描电子显微镜(SEM)、 透射电子显微镜(TEM)、 粉末X射线衍射分析(XRD)及X射线光电子能谱分析(XPS) 等方法对 Pd/PdO 纳米复合微球进行表征, 结果表明, 制备的纳米复合微球为表面粗糙、 大小均一的纳米微球. 采用紫外-可见吸收光谱(UV-Vis) 等方法考察了 Pd/PdO 纳米复合微球在对硝基苯酚(4-NTP) 还原反应中的催化性能, 发现其具有良好的催化活性和循环稳定性.     

基于点击化学法的SiO2微球有序阵列组装对PDMS薄膜表面改性的研究

利用端烯与巯基之间的光点击亲电加成化学反应,将表面富含巯基的二氧化硅微球均匀的附着在端烯修饰的聚二甲基硅氧烷(PDMS)表面,完成微球在PDMS表面的组装。分别采用傅里叶红外光谱仪、光学显微镜、接触角测量仪对修饰前后的基质材料进行表征检测,结果证实修饰在PDMS表面的端烯消失形成硫醚键,得到附着均匀的二氧化硅微球基质材料。通过这种方法,可以方便的在不同基材上负载二氧化硅微球。     

巴基斯坦Mw≥5.8地震时空对称与旋转规律研究及趋势判断

灾害预测是世界难题，选取1966年以来巴基斯坦M_w≥5.8地震数据，基于可公度理论和对称性原理，采用蝴蝶结构图和灾害统计方法分析了巴基斯坦M_w≥5.8地震的时空对称性，对下一次发生地震的位置进行趋势判断，并结合可能触发地震的主要天文因素，从地震触发机理上验证了判断结果的可靠性。 结果表明：（1）巴基斯坦M_w≥5.8历史地震可公度性良好，2018、2019年发震信号较强；（2）巴基斯坦M_w≥5.8地震在空间上呈三边形对称结构，震中空间变化具有两点线空间迁移规律和空间旋转规律，且在70.9 °E～77.7 °E，31.5 °N～37 °N发生M_w≥5.8地震的可能性较大；（3）巴基斯坦M_w≥5.8地震多发生在太阳黑子数下降段，这也进一步佐证了2018、2019年该地区发生地震的可能性。 该研究对完善统计方法，验证统计案例有重大意义，对巴基斯坦防灾减灾有参考价值。