密度泛函理论方法研究填料表面对聚合物摩擦化学的影响

采用超声分散法制备出氧化铝、高岭土、氧化硅/聚四氟乙烯复合材料, 使用线性往复摩擦磨损试验机对比三种复合材料的摩擦学性能. 结果表明 质量分数10%的氧化铝、高岭土能将聚四氟乙烯的磨损率降低约4个数量级, 而氧化硅仅能降低约3个数量级. 对金属对偶表面形成的转移膜的形貌和化学成分进行分析发现 氧化铝、高岭土/聚四氟乙烯在金属对偶面上形成了高度羧酸盐化的转移膜. 用密度泛函理论对三种填料表面上碳氟分子吸附过程进行模拟, 结果显示氧化铝、高岭土表面的路易斯酸性位点促进了碳氟分子的脱氟过程, 产生了更多的羧酸螯合物的中间产物; 氧化硅缺少路易斯酸性位点, 因此不能促进高度羧酸盐化的转移膜形成.     

Controlling thermomechanical behavior of semicrystalline hydrogenated polynorbornene through the cis- to trans-cyclopentylene ratio

Though polynorbornene synthesized by ring-opening metathesis polymerization has an intrinsically all-cis configuration of the cyclopentylene backbone rings, a fraction of these rings can be epimerized to the trans configuration during hydrogenation over suitable catalysts. By varying the method of hydrogenation, semicrystalline hydrogenated polynorbornenes (hPNs) with trans levels between 0 and 36% were obtained. With increasing trans content, the glass transition temperature, melting point, and enthalpy of melting decrease modestly. By contrast, the temperature at which the hPN crystal transitions into a rotationally disordered polymorph varies strongly with trans content, ranging from 126 °C (all-cis) to 71 °C at 27% trans; at trans contents of 34% and above, no rotationally-ordered phase is observed at any temperature. The room-temperature Young's modulus shows no dependence on trans content, while the yield stress drops by 20% at 1% trans content and slowly decreases further with additional epimerization. The temperature dependence of the Young's modulus differs for trans-containing versus all-cis polymers, while the temperature dependence of the yield stress is set by the polymorph type (rotationally ordered vs. disordered).     

气相输运沉积制备c轴择优取向的碘化铋薄膜

铋基卤化物材料因其无毒和优良的光电性能而显示出巨大的应用潜力。BiI₃作为一种层状重金属半导体,已被用于X射线检测、γ射线检测和压力传感器等领域,最近其作为一种薄膜太阳能电池吸收材料备受关注。本文采用简单的气相输运沉积(VTD)法,以BiI₃晶体粉末作为蒸发源,在玻璃基底上得到高质量c轴择优取向的BiI₃薄膜。并通过研究蒸发源温度和沉积距离对薄膜物相和形貌的影响,分析了BiI₃薄膜择优生长的机理。结果表明VTD法制备的BiI₃薄膜属于三斜晶系,其光学带隙为~1.8 eV。沉积温度对薄膜的择优取向有较大影响,在沉积温度低于270 ℃时,沉积的薄膜具有沿c轴择优取向生长的特点,超过此温度,c轴择优取向生长消失。在衬底温度为250 ℃、沉积距离为15 cm时制备的薄膜结晶性能最好,晶体形貌为片状八面体。     

Spectroscopic properties and bond dissociation energies of PbX,PbX±, PbX2 and PbX2± (X ​= ​F,Cl, Br,I)

Ab initio calculations have been performed to investigate some of the spectroscopic properties, like geometry, frequency, electron affinity, ionization potential and finally adiabatic bond dissociation energies (BDEs) of lead monohalides, lead dihalides and their ions viz. PbX, PbX^±, PbX₂, $\mathrm{P}\mathrm{b}{\mathrm{X}}_{\mathrm{2}}^{\pm }$ (X ?= ?F, Cl, Br, I) in their ground state at the QCISD(T)//MP2 level of theory using correlation consistent basis sets. For the validation of MP2 optimized geometry and frequency, we further obtained geometry and frequency of all the neutral and ionic systems using QCISD(T) method with the same basis sets. The BDEs of PbX₂ molecules are calculated using the BDEs of $\mathrm{P}\mathrm{b}{\mathrm{X}}_{\mathrm{2}}^{\pm }$ ions and taking ionization potential and electron affinity of various systems. The calculated values are found in good agreement with the available data. Most of the data for ionic systems are reported first time in literature.     

Y掺杂WS2二维材料的第一性原理研究

WS₂由于其优异的物理和光电性质引起了广泛关注。本研究基于第一性原理计算方法,探索了本征单层WS₂及不同浓度W原子替位钇(Y)掺杂WS₂的电子结构和光学特性。结果表明本征单层WS₂为带隙1.814 eV的直接带隙半导体。进行4%浓度(原子数分数)的Y原子掺杂后,带隙减小为1.508 eV,依旧保持着直接带隙的特性,随着Y掺杂浓度的不断增大,掺杂WS₂带隙进一步减小,当浓度达到25%时,能带结构转变为0.658 eV的间接带隙,WS₂表现出磁性。适量浓度的掺杂可以提高材料的导电性能,且掺杂浓度增大时,体系依旧保持着透明性并且在红外光和可见光区对光子的吸收能力、材料的介电性能都有着显著提高。本文为WS₂二维材料相关光电器件的研究提供了理论依据。     

Design of Functional Carbon Composite Materials for Energy Conversion and Storage

The carbon composite materials have been a research hotspot in the fields of catalysis, energy conversion and so on, because of their features of large structure and morphology variety, good chemical and electrochemical stability, and high electronic conductivity, large specific surface area and rich active sites. This paper summarizes some research progress of carbon composite materials, including assembly methodologies, their structure regulation, properties, and related applications. Moreover, the current challenges and the prospects of these materials are also discussed.     

水热法制备二氧化锡/钨酸铋复合光催化材料及其催化活性研究

本文用水热法制备了正交晶系的纳米球状结构的二氧化锡和正交晶系的由片状聚集成球状结构的钨酸铋,并且对二者进行了复合,制备出了二氧化锡/钨酸铋复合光催化材料。采用X射线衍射(XRD)、扫描电子显微镜(SEM)、比表面积测试仪(BET)、紫外可见分光光度计等技术对复合样品的结构、形貌、比表面积、孔容孔径和光学性质进行了表征。用碘钨灯模拟太阳光,分别以二氧化锡、钨酸铋和二氧化锡/钨酸铋复合材料为催化剂降解罗丹明B(RhB),研究所制备的二氧化锡/钨酸铋复合材料的光催化活性。光催化90 min时二氧化锡、钨酸铋和二氧化锡/钨酸铋对罗丹明B的降解率分别是9%、22%和30%。实验结果表明,在可见光下,二氧化锡/钨酸铋复合材料的光催化活性要高于单一的二氧化锡和钨酸铋。     

Lanthanide SMMs Based on Belt Macrocycles: Recent Advances and General Trends

Enhancement of axial magnetic anisotropy is the central objective to push forward the performance of Single-Molecule Magnet (SMM) complexes. In the case of mononuclear lanthanide complexes, the chemical environment around the paramagnetic ion must be tuned to place strongly interacting ligands along either the axial positions or the equatorial plane, depending on the oblate or prolate preference of the selected lanthanide. One classical strategy to achieve a precise chemical environment for a metal centre is using highly structured, chelating ligands. A natural approach for axial-equatorial control is the employment of macrocycles acting in a belt conformation, providing the equatorial coordination environment, and leaving room for axial ligands. In this review, we present a survey of SMMs based on the macrocycle belt motif. Literature systems are divided in three families (crown ether, Schiff-base and metallacrown) and their general properties in terms of structural stability and SMM performance are briefly discussed.