以磷化铁为添加剂沿(111)面生长磷掺杂金刚石大单晶

掺杂是调控金刚石性能的一种重要手段。本文采用温度梯度法,在5.6 GPa、1 312 ℃的条件下,选用Fe₃P作为磷源进行磷掺杂金刚石大单晶的合成。金刚石样品的显微光学照片表明,随着Fe₃P添加比例的增加,金刚石晶体的颜色逐渐变深,包裹体数量逐渐增加,晶形由板状转变为塔状直至骸晶。金刚石晶形的变化表明Fe₃P的添加使生长金刚石的V形区向右偏移,这是Fe₃P改变触媒特性的缘故。红外光谱分析表明,Fe₃P的添加使金刚石晶体中氮含量上升,这说明磷的进入诱使氮原子更容易进入金刚石晶格中。激光拉曼光谱测试表明,随着Fe₃P添加比例的增加,所合成的掺磷金刚石的拉曼峰位变化不大,其半峰全宽(FWHM)值变大,这说明磷的进入使得金刚石晶格畸变增加。XPS测试结果显示,随着Fe₃P添加比例的增加,金刚石晶体中磷相对碳的原子百分含量也会增加,这意味着添加Fe₃P所合成的金刚石晶体中有磷存在。     

气相输运沉积制备c轴择优取向的碘化铋薄膜

铋基卤化物材料因其无毒和优良的光电性能而显示出巨大的应用潜力。BiI₃作为一种层状重金属半导体,已被用于X射线检测、γ射线检测和压力传感器等领域,最近其作为一种薄膜太阳能电池吸收材料备受关注。本文采用简单的气相输运沉积(VTD)法,以BiI₃晶体粉末作为蒸发源,在玻璃基底上得到高质量c轴择优取向的BiI₃薄膜。并通过研究蒸发源温度和沉积距离对薄膜物相和形貌的影响,分析了BiI₃薄膜择优生长的机理。结果表明VTD法制备的BiI₃薄膜属于三斜晶系,其光学带隙为~1.8 eV。沉积温度对薄膜的择优取向有较大影响,在沉积温度低于270 ℃时,沉积的薄膜具有沿c轴择优取向生长的特点,超过此温度,c轴择优取向生长消失。在衬底温度为250 ℃、沉积距离为15 cm时制备的薄膜结晶性能最好,晶体形貌为片状八面体。     

Negative thermal expansion in NbF_3 and NbOF_2:A comparative theoretical study

Thermal expansion control is always an obstructive factor and challenging in high precision engineering field. Here,the negative thermal expansion of Nb F_3 and Nb OF_2 was predicted by first-principles calculation with density functional theory and the quasi-harmonic approximation(QHA). We studied the total charge density, thermal vibration, and lattice dynamic to investigate the thermal expansion mechanism. We found that the presence of O induced the relatively strong covalent bond in Nb OF_2, thus weakening the transverse vibration of F and O in Nb OF_2, compared with the case of Nb F_3.In this study, we proposed a way to tailor negative thermal expansion of metal fluorides by introducing the oxygen atoms.The present work not only predicts two NTE compounds, but also provides an insight on thermal expansion control by designing chemical bond type.     

新型功能碳材料的高压截获

高性能功能材料在诸多领域具有广泛的应用前景,是人们一直关注的研究热点。高压可以有效地改变物质的原子间距和成键方式,是获得新型功能材料的重要途径。在碳材料的高压研究中,许多有趣的功能碳材料,如光学透明碳、高强度弹性碳和超硬非晶碳等,已经通过不同的碳前驱体合成。本文简要介绍了作者近年来在低维碳基纳米复合材料高压研究中取得的进展,基于设计的不同低维碳前驱体,高压下截获了具有超硬特性、新型压致共价聚合及发光增强的碳材料。     

A self-powered and sensitive terahertz photodetection based on PdSe2

With the rapid development of terahertz technology, terahertz detectors are expected to play a key role in diverse areas such as homeland security and imaging, materials diagnostics, biology, medical sciences, and communication. Whereas self-powered, rapid response, and room temperature terahertz photodetectors are confronted with huge challenges. Here, we report a novel rapid response and self-powered terahertz photothermoelectronic (PTE) photodetector based on a low-dimensional material: palladium selenide (PdSe₂). An order of magnitude performance enhancement was observed in photodetection based on PdSe₂/graphene heterojunction that resulted from the integration of graphene and enhanced the Seebeck effect. Under 0.1-THz and 0.3-THz irradiations, the device displays a stable and repeatable photoresponse at room temperature without bias. Furthermore, rapid rise (5.0 μs) and decay (5.4 μs) times are recorded under 0.1-THz irradiation. Our results demonstrate the promising prospect of the detector based on PdSe₂ in terms of air-stable, suitable sensitivity and speed, which may have great application in terahertz detection.     

水热法制备二氧化锡/钨酸铋复合光催化材料及其催化活性研究

本文用水热法制备了正交晶系的纳米球状结构的二氧化锡和正交晶系的由片状聚集成球状结构的钨酸铋,并且对二者进行了复合,制备出了二氧化锡/钨酸铋复合光催化材料。采用X射线衍射(XRD)、扫描电子显微镜(SEM)、比表面积测试仪(BET)、紫外可见分光光度计等技术对复合样品的结构、形貌、比表面积、孔容孔径和光学性质进行了表征。用碘钨灯模拟太阳光,分别以二氧化锡、钨酸铋和二氧化锡/钨酸铋复合材料为催化剂降解罗丹明B(RhB),研究所制备的二氧化锡/钨酸铋复合材料的光催化活性。光催化90 min时二氧化锡、钨酸铋和二氧化锡/钨酸铋对罗丹明B的降解率分别是9%、22%和30%。实验结果表明,在可见光下,二氧化锡/钨酸铋复合材料的光催化活性要高于单一的二氧化锡和钨酸铋。     

碳纳米管增强型复合材料功能梯度板的自由振动模型与尺度效应

基于一种新的各向异性修正偶应力理论，建立了碳纳米管增强复合材料功能梯度板的自由振动模型。该模型能够描述尺度效应，且仅包含一个尺度参数。基于一阶剪切变形理论和哈密顿原理推演了板的运动微分方程，并以四边简支板为例给出了自振频率的解析解。讨论了板的几何尺寸、碳纳米管体分比含量和分布方式等因素对板的自振频率的影响。结果表明，本文模型所预测的板的自振基频总是高于经典弹性理论的Mindlin板模型的预测结果，两者间的差异在板的几何尺寸接近尺度参数的值时非常明显，且会随着板的几何尺寸的增大而逐渐消失。     

Solution combustion synthesis,energy and environment: Best parameters for better materials

Solution combustion synthesis (SCS) is a worldwide used methodology for the preparation of inorganic ceramic and composite materials with controlled properties for a wide number of applications, from catalysis to photocatalysis and electrocatalysis, from heavy metal removal to sensoristics and electronics. The high versatility and efficiency of this technique have led to the introduction of many variants, which allowed important optimization to the prepared materials. Moreover, its ecofriendly nature encouraged further studies about the use of sustainable precursors for the preparation of nanomaterials for energy and environment, according to the concept of circular economy. On the other hand, the large variety of expressions to define SCS and the often-contradictory definitions of the SCS parameters witnessed a scarce consciousness of the potentiality of this methodology. In this review article, the most important findings about SCS and the selection criteria for its main parameters are critically reviewed, in order to give useful guidelines to those scientists who want to use this methodology for preparing materials with improved or new functional properties. This review aims as well (i) to bring more clarity in the SCS terminology (ii) to increase the awareness of the SCS as a convenient tool for the synthesis of materials and (iii) to propose a new perspective in the SCS, with special attention to the use of ecofriendly procedures. Part of the review is also dedicated to precautions and limitations of this powerful methodology.     

基于NiCo2O4纳米片电极的非对称混合电容器

The looming global energy crisis and ever-increasing energy demands have catalyzed the development of renewable energy storage systems. In this regard, supercapacitors (SCs) have attracted widespread attention because of their advantageous attributes such as high power density, excellent cycle stability, and environmental friendliness. However, SCs exhibit low energy density and it is important to optimize electrode materials to improve the overall performance of these devices. Among the various electrode materials available, spinel nickel cobaltate (NiCo₂O₄) is particularly interesting because of its excellent theoretical capacitance. Based on the understanding that the performances of the electrode materials strongly depend on their morphologies and structures, in this study, we successfully synthesized NiCo₂O₄ nanosheets on Ni foam via a simple hydrothermal route followed by calcination. The structures and morphologies of the as-synthesized products were characterized by X-ray diffraction, scanning electron microscopy, and Brunauer-Emmett-Teller (BET) surface area analysis, and the results showed that they were uniformly distributed on the Ni foam support. The surface chemical states of the elements in the samples were identified by X-ray photoelectron spectroscopy. The as-synthesized NiCo₂O₄ products were then tested as cathode materials for supercapacitors in a traditional three-electrode system. The electrochemical performances of the NiCo₂O₄ electrode materials were studied and the area capacitance was found to be 1.26 C·cm^-2 at a current density of 1 mA·cm^-2. Furthermore, outstanding cycling stability with 97.6% retention of the initial discharge capacitance after 10000 cycles and excellent rate performance (67.5% capacitance retention with the current density from 1 to 14 mA·cm^-2) were achieved. It was found that the Ni foam supporting the NiCo₂O₄ nanosheets increased the conductivity of the electrode materials. However, it is worth noting that the contribution of nickel foam to the areal capacitance of the electrode materials was almost zero during the charge and discharge processes. To further investigate the practical application of the as-synthesized NiCo₂O₄ nanosheets-based electrode, a device was assembled with the as-prepared samples as the positive electrode and active carbon (AC) as the negative electrode. The assembled supercapacitor showed energy densities of 0.14 and 0.09 Wh·cm^-3 at 1.56 and 4.5 W·cm^-3, respectively. Furthermore, it was able to maintain 95% of its initial specific capacitance after 10000 cycles. The excellent electrochemical performance of the NiCo₂O₄ nanosheets could be ascribed to their unique spatial structure composed of interconnected ultrathin nanosheets, which facilitated electron transportation and ion penetration, suggesting their potential applications as electrode materials for high performance supercapacitors. The present synthetic route can be extended to other ternary transition metal oxides/sulfides for future energy storage devices and systems.