Yb:CaF2–YF3 transparent ceramics ultrafast laser at dual gain lines

Yb³⁺:CaF₂-YF₃ transparent ceramics with excellent optical quality was successfully fabricated by hot-pressed method. Pulsed laser properties of this ceramics were investigated for the first time. Laser diode (LD) was applied as the pump source to generate a dual-wavelength mode-locked (ML) laser. The maximum average output power was 310 mW, which represents the highest output power of ultrafast calcium fluoride ceramic laser. The spectrum separated at 1048.9 nm and 1049.7 nm with a total pulse duration of 8.9 ps. The interval period between the beating signals was about 4.3 ps, corresponding to a 0.23 THz beat pulse repetition rate. These results demonstrate its potential in producing dual-wavelength ultrashort pulses. These Yb³⁺:CaF₂-YF₃ ceramics with low-cost and short-preparation period are ideal candidate materials for ultrafast lasers.     

基于DIS数字信息化系统对透光物质透光性能的研究

采用DIS数字信息化系统,对不同浓度的蓝墨水溶液在激光光源照射下的透射平均照度及照度分布图像进行实验研究,得到了平均照度值随溶液浓度变化的规律。对不同颜色塑料膜片对白炽灯光源透过照度值及照度分布图像进行实验研究得到及其相关之规律。     

Eu:Lu2O3透明闪烁陶瓷的制备与性能

采用湿化学法合成了Eu原子掺量5%的Lu₂O₃陶瓷前驱体,通过SEM、XRD研究了煅烧前后前驱体和1 100 ℃煅烧4 h后粉体的形貌、结构以及物相。结果表明煅烧后的粉体为纳米类球形、高分散且结晶性良好的颗粒。颗粒尺寸为68.5 nm。使用煅烧后的粉体为原料,在1 650 ℃真空烧结30 h制备了高透过率的Eu:Lu₂O₃陶瓷,晶粒尺寸为46 μm,在611 nm处的直线透过率可以达到66.3%。此外对陶瓷的吸收曲线、光致激发和发射光谱特性以及X射线激发发射光谱进行研究。可观察到,Eu:Lu₂O₃陶瓷存在基质和激活离子两类吸收,光致发光光谱和X射线激发发射光谱均可以看出Eu:Lu₂O₃陶瓷存在极强的⁵D₀→⁷F₂跃迁发光,位于611 nm处。对比商业的BGO单晶的X射线发射光谱,可得本实验中制备的陶瓷的光输出为85 000 ph/MeV。Eu:Lu₂O₃陶瓷本身有着高X射线以及高能粒子的阻止能力,结合高光输出特性,表明Eu:Lu₂O₃陶瓷在X射线成像等领域具有巨大的潜在应用价值。     

Copper as a Robust and Transparent Electrocatalyst for Water Oxidation

Copper metal is in theory a viable oxidative electrocatalyst based on surface oxidation to Cu^III and/or Cu^IV, but its use in water oxidation has been impeded by anodic corrosion. The in situ formation of an efficient interfacial oxygen‐evolving Cu catalyst from Cu^II in concentrated carbonate solutions is presented. The catalyst necessitates use of dissolved Cu^II and accesses the higher oxidation states prior to decompostion to form an active surface film, which is limited by solution conditions. This observation and restriction led to the exploration of ways to use surface‐protected Cu metal as a robust electrocatalyst for water oxidation. Formation of a compact film of CuO on Cu surface prevents anodic corrosion and results in sustained catalytic water oxidation. The Cu/CuO surface stabilization was also applied to Cu nanowire films, which are transparent and flexible electrocatalysts for water oxidation and are an attractive alternative to ITO‐supported catalysts for photoelectrochemical applications.     

Metal grid technologies for flexible transparent conductors in large-area optoelectronics

Mechanically flexible optoelectronic devices such as flexible displays, touch-screens, wearable electronics and solar cells are attracting significant commercial interest. In these devices, a transparent conductor is an essential element that delivers or collects the electrical current to the active material while it allows light to enter or exit from the device. The transparent conductor is composed of a transparent conductive film and a metallic grid providing electrical conduction over the large area. In this article, we review the established processes used by the industry as well as emerging solution-based methods for processing metal grids. Furthermore, we review the issues and potentials of these emerging processes facing for large-area deployment. In the final section, we evaluate three applications of flexible transparent conductors in: perovskite-based solar cells, organic light emitting diodes and electrochromic windows.     

Synthesis of transparent block copolymers consisting of poly(diisopropyl fumarate) and poly(2-ethylhexyl acrylate) segments by reversible addition-fragmentation chain transfer polymerization using trithiocarbonates as the chain transfer agents

The reversible addition-fragmentation chain transfer polymerization of diisopropyl fumarate (DiPF) was carried out using ethyl 2-[[(dodecylthio)thioxymethyl]thio]-2-methylpropionate (T1) and 1,1′-(1,2-ethanediyl) bis[2-[[(dodecylthio)thioxymethyl]thio]-2-methylpropionate] (T2) as the monofunctional and difunctional chain transfer agents (CTAs) to synthesize poly(diisopropyl fumarate) (PDiPF) with a rigid chain conformation. The obtained PDiPF had a well-controlled molecular weight, molecular weight distribution, and structure of the chain ends. Size exclusion chromatography and NMR measurements revealed an excellent introduction efficiency (84–98%) of the terminal trithiocarbonate group into the polymer chain end. They were available as the monofunctional and difunctional macro-CTAs to synthesize the AB and ABA block copolymers, respectively. While the well-controlled block copolymers were solely obtained by the polymerization of 2-ethylhexyl acrylate as the second monomer in the presence of PDiPF as the macro-CTA, the block copolymerization of DiPF using poly(2-ethylhexyl acrylate) as the macro-CTA failed. The trithiocarbonate group at the chain end was completely removed by the reaction with n-butylamine and it was valid for the improvement of the coloration and other optical properties of the transparent polymers. © 2018 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2018 , 56, 2584–2594     

Highly transparent cerium doped gadolinium gallium aluminum garnet ceramic prepared with precursors fabricated by ultrasonic enhanced chemical co-precipitation

Cerium doped gadolinium gallium aluminum garnet (GGAG:Ce) ceramic precursors have been synthesized with an ultrasonic chemical co-precipitation method (UCC) and for comparison with a traditional chemical co-precipitation method (TCC). The effect of ultra-sonication on the morphology of powders and the transmittance of GGAG:Ce ceramics are studied. The results indicate that the UCC method can effectively improve the homogenization and sinterability of GGAG:Ce powders, which contribute to obtain high transparent GGAG ceramic with the highest transmittance of 81%.     

(Gd,Lu)3Al5O12∶Tb3+,Eu3+透明陶瓷制备与发光性能

通过简单的化学沉淀法制备了纳米前驱体,结合真空烧结工艺,制备了一系列镥稳定钆铝石榴石{(Gd, Lu)₃Al₅O₁₂∶Tb,Eu}透明陶瓷。将透明陶瓷加工成1 mm厚的圆片,对透明陶瓷样品进行了X射线衍射、光致发光、透过率和衰减时间等表征。高温烧结过后,陶瓷样品仍保持稳定的石榴石相。选定313 nm作为透明陶瓷的激发波长,可获得最强的荧光发射。此外,通过对不同样品进行紫外可见荧光测试,获得了由绿光到红光的可调节发射。在313 nm激发,543 nm和591 nm的监测波长下,透明陶瓷样品均具有Eu³⁺的毫秒级衰减时间。