Tobias Grewe Xiaohui Deng Dr. Harun Tüysüz 《Chemistry (Weinheim an der Bergstrasse, Germany)》2014,20(25):7692-7697
A systematic study on the growth of Cr2O3 in three‐dimensional cubic ordered mesoporous silica (KIT‐6) and its replication through nanocasting is reported. By changing the loading time and amount of precursor, the size and shape of the obtained replica could be controlled to some extent. More interestingly, in contrast to previously published studies, when KIT‐6 with an aging temperature of 100 °C, which has a high degree of interconnectivity, was used as a hard template, a cubic ordered mesoporous Cr2O3 replica with an open uncoupled subframework structure and reduced symmetry was obtained. Formation of a replica with different symmetry and uncoupled subframework structure is not only related to the degree of interconnectivity of the parent, but also strongly depends on the type of metal oxide and its growth mechanism in the silica template. Nanocasting of Cr2O3 with a low loading results in a replica with monomodal pore size distribution that has same symmetry as the hard template, whereas increasing the loading amount alters the symmetry of the replica and yields a replica with bimodal distribution. 相似文献
2.
通过纳米浇铸法合成了有序介孔炭CMK-3,再通过浸渍法制备了Cu/CMK-3催化剂,并将其用于气相甲醇氧化羰基化反应。N2吸附-脱附测试、X射线衍射(XRD)以及透射电镜(TEM)的表征结果表明,Cu/CMK-3具有序介孔结构,活性Cu物种均匀分散于CMK-3的表面及孔道中,粒径为10~20 nm,远小于相同条件下制备的铜/活性炭(Cu/AC)催化剂。固定床反应器的活性评价结果显示450℃下制备的Cu/CMK-3催化活性最高,反应10 h内碳酸二甲酯(DMC)的时空收率(STY)达到286 mg·g^-1·h^-1,选择性为76%。长周期活性评价结果表明Cu/CMK-3稳定性较相同条件下制备的Cu/AC有大幅提高,50 h内DMC的STY降低了20%,75 h内降低了28%。 相似文献
3.
4.
Utilization of Environmentally Benign Dicyandiamide as a Precursor for the Synthesis of Ordered Mesoporous Carbon Nitride and its Application in Base‐Catalyzed Reactions 下载免费PDF全文
Assisted by a new dissolution procedure, dicyandiamide (DCDA), an environmentally benign and cheap precursor, has been employed for the synthesis of mesoporous carbon nitride (CN) materials through a nanocasting approach. The synthesized mesoporous materials possessed high specific surface areas (269–715 m2 g?1) with narrow pore‐size distributions (about 5 nm) and faithfully replicated the mesostructures of the SBA‐15 and FDU‐12 templates. Several characterization techniques, including XRD, SAXS, TEM, Raman and FTIR spectroscopy, XPS, and CO2‐TPD, were used to analyze the physicochemical properties of these materials and the results showed that the mesoporous CND materials had graphitic‐like structures and consisted of CN heterocycles, as well as amino groups. In a series of Knoevenagel condensation reactions, as exemplified by the reaction of various aldehydes and nitriles, these mesoporous CND materials demonstrated high and stable catalytic activities, owing to an abundance of basic sites. 相似文献
5.
分别采用纳米铸型法和溶胶-凝胶法制备了系列LaNiO3载体,并用沉积-沉淀法制备了系列Au/LaNiO3催化剂.对催化剂进行了XRD、BET、AAS、TEM和XPS等表征,测试了其对CO催化氧化活性.实验结果表明,纳米铸型法得到的LaNiO3-NCM具有介孔结构,且比表面积可达126 m2·g-1,以其为载体制备的Au/LaNiO3-NCM催化剂在30℃条件下将CO完全转化,活性远高于以传统溶胶-凝胶法制备的LaNiO3-SG为载体的金催化剂.XPS结果表明该Au/LaNiO3-NCM催化剂表面存在较多的氧化态Auδ+(0 < δ < 3)和晶格氧,且活性组分Au含量也较高,说明高比表面介孔LaNiO3载体有利于提高活性组分Au的负载量,从而提高催化剂催化活性. 相似文献
6.
Zhen Li Bin Dong Fei Geng Ganzuo Li 《Journal of Dispersion Science and Technology》2013,34(8):1066-1071
This article reports a novel preparation of mesoporous silica with series of 1-alky-3-methylimidazolium bromide (CnMIM)Br (n = 12, 14, 16), a kind of amphiphilic room-temperature ionic liquids (RTILs), as a template via a sol-gel nanocasting technique. The pore morphology and structures of these mesoporous silica were characterized by Transmission electron microscopy (TEM). The results show that the RTIL bearing longer alkyl chain is preferred to form the mesoporous silica material with bigger pores. (C16MIM)Br has been chosen to study how the various influencing factors affect the synthesis and structure of the mesoporous silica material, such as the acid concentration, the solling time, the gelling time and the calcination time. N2 adsorption-desorption isotherms measurement was used to characterize the pore size distribution and BET surface area. The results indicate that all of the factors can make an influence on the preparation of the mesoporous silica, which is more sensitive to the concentration of the acid. 相似文献
7.
8.
Razieh FAZAELI Hamid ALIYAN Shahram TANGESTANINEJAD Esmaeel MOHAMMADI Maryam BORDBAR 《催化学报》2012,(2):237-246
The elimination of the silica matrix of composites by HF occurred by a two-step reaction deposition of a Cs2.5H0.5PW12O40(CsHPW) salt nanocrystal.We used 2D hexagonal SBA-15 silica as a template for the nanofabrication of CsHPW nanoparticles.Nanocast CsHPW materials are stable against leaching and colloidization in polar solvents.The catalytic performance of the nanocast CsHPW materi-als exceeded that of bulk Cs2.5H0.5PW12O40,which is the most active among the acidic HPW salts.A series of novel 1,3,5-triaryl-pyrazoline derivatives were synthesized by the reaction between chalcone and phenylhydrazine in high yield in the presence of CsHPW salt nanocrystals. 相似文献
9.
Galeano C Güttel R Paul M Arnal P Lu AH Schüth F 《Chemistry (Weinheim an der Bergstrasse, Germany)》2011,17(30):8434-8439
The use of nanostructured yolk-shell materials offers a way to discriminate support and particle-size effects for mechanistic studies in heterogeneous catalysis. Herein, gold yolk-shell materials have been synthesized and used as model catalysts for the investigation of support effects in CO oxidation. Carbon has been selected as catalytically inert support to study the intrinsic activity of the gold nanoparticles, and for comparison, zirconia has been used as oxidic support. Au, @C materials have been synthesized through nanocasting using two different nonporous-core@mesoporous-shell exotemplates: Au@SiO(2)@ZrO(2) and Au@SiO(2)@m-SiO(2). The catalytic activity of Au, @C with a gold core of about 14 nm has been evaluated and compared with Au, @ZrO(2) of the same gold core size. The strong positive effect of metal oxide as support material on the activity of gold has been proved. Additionally, size effects were investigated using carbon as support to determine only the contribution of the nanoparticle size on the catalytic activity of gold. Therefore, Au, @C with a gold core of about 7 nm was studied showing a less pronounced positive effect on the activity than the metal oxide support effect. 相似文献
10.
Xiaoqiang Fan Jianmei Li Zhen Zhao Yuechang Wei Jian Liu Aijun Duan Guiyuan Jiang 《天然气化学杂志》2014,(2):171-178
Highly ordered mesoporous NiMoO4material was successfully synthesized using mesoporous silica KIT-6 as hard template via vacuum nanocasting method. The structure was characterized by means of XRD, TEM, N2adsorption-desorption, Raman and FT-IR. The mesoporous NiMoO4with the coexistence of α-NiMoO4and β-NiMoO4showed well-ordered mesoporous structure, a bimodal pore size distribution and crystalline framework. The catalytic performance of NiMoO4was investigated for oxidative dehydrogenation of propane. It is demonstrated that the mesoporous NiMoO4catalyst with more surface active oxygen species showed better catalytic performance in oxidative dehydrogenation of propane in comparison with bulk NiMoO4. 相似文献