富晶格位错的多孔铋纳米花高效电还原二氧化碳制甲酸盐※

二氧化碳转化已成为现今世界研究的热点. 本工作采用原位电化学转化的策略, 将简单溶剂热法合成的层状甲酸氧铋纳米花(BiOCOOH NFs)还原为带有大量晶格位错的多孔铋纳米花(p-Bi NFs). 研究结果表明, p-Bi NFs电催化二氧化碳转化为甲酸盐具有较小的过电位(436 mV). 在–1.8 V(相对饱和甘汞电极, vs. SCE)时, 甲酸盐的分电流密度(j_formate)高达24.4 mA•cm^-2, 法拉第效率(FE_formate)为96.7%, 且在超过500 mV的宽电位窗口内FE_formate超过90%, 并具有很好的稳定性. 该催化剂的高催化性能可归因于前驱体晶格坍塌和重构而形成特殊的多孔粗糙的微纳多级结构, 其表面富含晶格位错和缺陷等高本征活性位, 且具有较强的电子传递能力. 本研究为设计合成高性能的电催化二氧化碳还原产甲酸催化剂提供了新的思路.     

Multifunctional material Bi4Ge3O12: thermodynamic properties

Thermodynamic characteristics of a single crystal of bismuth orthogermanate (Bi₄Ge₃O₁₂), which are necessary to improve device portfolio, have been studied. It has been shown that bismuth orthogermanate is thermodynamically stable against decomposition into binary oxides at 50 °C, which gives us grounds to consider this compound promising for various applications.     

水热法制备二氧化锡/钨酸铋复合光催化材料及其催化活性研究

本文用水热法制备了正交晶系的纳米球状结构的二氧化锡和正交晶系的由片状聚集成球状结构的钨酸铋,并且对二者进行了复合,制备出了二氧化锡/钨酸铋复合光催化材料。采用X射线衍射(XRD)、扫描电子显微镜(SEM)、比表面积测试仪(BET)、紫外可见分光光度计等技术对复合样品的结构、形貌、比表面积、孔容孔径和光学性质进行了表征。用碘钨灯模拟太阳光,分别以二氧化锡、钨酸铋和二氧化锡/钨酸铋复合材料为催化剂降解罗丹明B(RhB),研究所制备的二氧化锡/钨酸铋复合材料的光催化活性。光催化90 min时二氧化锡、钨酸铋和二氧化锡/钨酸铋对罗丹明B的降解率分别是9%、22%和30%。实验结果表明,在可见光下,二氧化锡/钨酸铋复合材料的光催化活性要高于单一的二氧化锡和钨酸铋。     

Synthesis of Elusive Chloropnictenium Ions

This work describes the synthesis and full characterization of elusive chloropnictenium ion salts of the type [^RAr*N(SiMe)ECl][A] (^RAr*=2,6‐(CHPh₂)‐4‐R‐C₆H₂, R=Me, tBu; E=Sb, Bi; A^?=GaCl₄, Al(OCH(CF₃)₂)₄). In these species the cation is significantly stabilized by weak arene interactions to flanking phenyl groups of the ^RAr* moiety. In this context the bonding situation has been studied by computational means and the reactivity towards the Lewis base 4‐dimethylaminopyridine (dmap) was investigated.     

Bismuth(III) Flavonolates: The Impact of Structural Diversity on Antibacterial Activity,Mammalian Cell Viability and Cellular Uptake

A series of homoleptic and heteroleptic bismuth(III) flavonolate complexes derived from six flavonols of varying substitution have been synthesised and structurally characterised. The complexes were evaluated for antibacterial activity towards several problematic Gram-positive (Staphylococcus aureus, methicillin-resistant Staphylococcus aureus (MRSA), and vancomycin-resistant Enterococcus (VRE)) and Gram-negative (Escherichia coli, Pseudomonas aeruginosa) bacteria. The cell viability of COS-7 (monkey kidney) cells treated with the bismuth flavonolates was also studied to determine the effect of the complexes on mammalian cells. The heteroleptic complexes [BiPh(L)₂] (in which L=flavonolate) showed good antibacterial activity towards all of the bacteria but reduced COS-7 cell viability in a concentration-dependent manner. The homoleptic complexes [Bi(L)₃] exhibited activity towards the Gram-positive bacteria and showed low toxicity towards the mammalian cell line. Bismuth uptake studies in VRE and COS-7 cells treated with the bismuth flavonolate complexes indicated that Bi accumulation is influenced by both the substitution of the flavonolate ligands and the degree of substitution at the bismuth centre.     

Preparation of bismuth sulfide nanoparticles as targeted biocompatible nano-radiosensitizer and carrier of methotrexate

In this study, Bi₂S₃@BSA–Bio–MTX nanoparticles (NPs) were synthesized for the first time by bovine serum albumin (BSA)-mediated biomineralization (Bi₂S₃@BSA NPs) followed by covalent bonding of biotin (Bio) and methotrexate (MTX) on the surface of the Bi₂S₃@BSA NPs via carbodiimide chemistry. The synthesized NPs were globular and exhibited uniform morphology with a hydrodynamic diameter of 107.6 ± 6.81 nm (mean ± standard deviation) and zeta potential of −20.9 ± 2.18 mV. Drug release from Bi₂S₃@BSA–Bio–MTX NPs indicated an enzyme-dependent release pattern. The in vitro biocompatibility of NPs was confirmed by investigating their cytotoxicity against the HEK-293 cell line and hemolysis assay test, whereas the in vivo biocompatibility of the NPs was evaluated and confirmed by the lethal dose 50 (LD₅₀) test. To evaluate the in vitro anticancer activity of the functionalized NPs and MTX, their cytotoxic effects was assessed against 4T1 cancer cells by 5-dimethylthiazol-z-yl)-2,5-diphenyltetrazolium bromide (MTT) assay with and without X-ray radiation. Results showed that Bi₂S₃@BSA–Bio–MTX NPs have excellent anticancer activity, especially following X-ray radiation.     

Enhancement of Photocatalytic Activity of Sodium Bismuth Titanate by Doping with Copper,Silver, and Tin Ions

Perovskite type oxides, sodium bismuth titanate (Na_0.5Bi_0.5TiO₃), and Ag⁺, Cu²⁺, and Sn²⁺ doped Na_0.5Bi_0.5TiO₃ were prepared by pechini and ion exchange methods, respectively. Photocatalytic activities of these catalysts were tested by decomposition of methylene blue (MB) under visible light irradiation. Results showed that the photocatalytic activity of metal ion doped Na_0.5Bi_0.5TiO₃ was higher than undoped Na_0.5Bi_0.5TiO₃. Relatively high photocatalytic performance of Ag⁺‐doped Na_0.5Bi_0.5TiO₃ is mainly ascribed to the efficient separation of electron‐hole (e^–, h⁺) pairs, lower bandgap energy and the creation of active hydroxyl radicals ( ^? OH). Further, the Ag⁺‐doped Na_0.5Bi_0.5TiO₃ catalyst showed good reusability up to four cycles. A possible mechanism for the enhanced photocatalytic performance was proposed. The synthesized photocatalysts were characterized by XRD, SEM, EDS, XPS, FT‐IR, and UV/Vis DRS techniques.     

火试金-原子吸收光谱法测定锡阳极泥中金、银含量

锡阳极泥是锡冶炼过程中的一种中间产物,其中含有大量的金、银等贵金属。准确测定锡阳极泥中金、银含量有很重要的现实意义。采用火试金法能实现锡阳极泥中金、银含量的连续测定,方法准确度高,精密度好,金、银回收率在97.46%~101.66%,能很好地满足锡阳极泥中高品位金、银的测定。     

Lead‐Free,Air‐Stable All‐Inorganic Cesium Bismuth Halide Perovskite Nanocrystals

Lead‐based perovskite nanocrystals (NCs) have outstanding optical properties and cheap synthesis conferring them a tremendous potential in the field of optoelectronic devices. However, two critical problems are still unresolved and hindering their commercial applications: one is the fact of being lead‐based and the other is the poor stability. Lead‐free all‐inorganic perovskite Cs₃Bi₂X₉ (X=Cl, Br, I) NCs are synthesized with emission wavelength ranging from 400 to 560 nm synthesized by a facile room temperature reaction. The ligand‐free Cs₃Bi₂Br₉ NCs exhibit blue emission with photoluminescence quantum efficiency (PLQE) about 0.2 %. The PLQE can be increased to 4.5 % when extra surfactant (oleic acid) is added during the synthesis processes. This improvement stems from passivation of the fast trapping process (2–20 ps). Notably, the trap states can also be passivated under humid conditions, and the NCs exhibited high stability towards air exposure exceeding 30 days.     

Er3+掺杂Li2O-SrO-ZnO-Bi2O3玻璃中Er3+离子在1.53 μm处的荧光发射特性

采用传统的熔融法制备了Er~(3+)掺杂的新型铋酸盐玻璃(Li_2O-SrO-ZnO-Bi_2O_3,LSZB),并对其光谱性质进行了表征,分析了玻璃的拉曼光谱、吸收光谱、荧光光谱,利用Judd-Ofelt理论研究了其荧光特性。LSZB玻璃样品中Er~(3+)的~4I_(13/2)→~4I_(15/2)跃迁发射峰位于1.53 μm处,半高宽约为78 nm。样品中Er~(3+)的~4I_(13/2)能级寿命为2.848 ms,量子效率为99.93%,受激发射截面达到9.76×10~(-21)cm~2。以上结果显示,Er~(3+)掺杂LSZB玻璃有良好的光谱特性。