In-situ electrochemical study of chalcopyrite pressure oxidation leaching from 110 °C to 150 °C under saturated vapor pressure

Pressure oxidation leaching behavior of chalcopyrite in sulfuric acid solution from 110 °C to 150 °C were investigated by in-situ electrochemical methods. Leaching experiments under saturated vapor pressure conditions were used to simulate the anoxic environment that may be encountered in industrial applications. Scanning electron microscope and X-ray photoelectron spectroscopy were used to characterize the morphology and the chemical status of chalcopyrite surface. Results show that the copper extraction was increased with the increase of leaching temperature. Under the optimal leaching conditions under saturated vapor pressure, the copper and iron extraction are 8.3% and 29.8%, respectively. When the temperature increased from 110 °C to 150 °C, the self-corrosion potential and electrochemical reaction resistance firstly increased and then decreased. In contrast, the resistance of the passive film was always increased with the increase of temperature. The electrochemical study results indicated that the increase in temperature affected the oxidation of chalcopyrite by altering the kinetics of the cathodic reaction and the anodic passivation. Both the self-corrosion current density (i_corr) and rate constant were affected by the reduction of Fe(III). The XPS results show that elemental sulfur and H₃O(Fe₃(SO₄)₂(OH)₆) were the main leaching solid products. The formation of H₃O(Fe₃(SO₄)₂(OH)₆) not only caused a decrease in cathodic reaction kinetics, but also increased the resistance of mass transfer process. Due to the faster release of iron, copper-rich sulphides were formed, which mixed with the elemental sulfur and/or H₃O(Fe₃(SO₄)₂(OH)₆) led to coverage of the chalcopyrite surface.     

Diffusion Model of a Non-Integer Order PIγ Controller with TCP/UDP Streams

In this article, a way to employ the diffusion approximation to model interplay between TCP and UDP flows is presented. In order to control traffic congestion, an environment of IP routers applying AQM (Active Queue Management) algorithms has been introduced. Furthermore, the impact of the fractional controller PIγ and its parameters on the transport protocols is investigated. The controller has been elaborated in accordance with the control theory. The TCP and UDP flows are transmitted simultaneously and are mutually independent. Only the TCP is controlled by the AQM algorithm. Our diffusion model allows a single TCP or UDP flow to start or end at any time, which distinguishes it from those previously described in the literature.     

Negative thermal expansion in NbF_3 and NbOF_2:A comparative theoretical study

Thermal expansion control is always an obstructive factor and challenging in high precision engineering field. Here,the negative thermal expansion of Nb F_3 and Nb OF_2 was predicted by first-principles calculation with density functional theory and the quasi-harmonic approximation(QHA). We studied the total charge density, thermal vibration, and lattice dynamic to investigate the thermal expansion mechanism. We found that the presence of O induced the relatively strong covalent bond in Nb OF_2, thus weakening the transverse vibration of F and O in Nb OF_2, compared with the case of Nb F_3.In this study, we proposed a way to tailor negative thermal expansion of metal fluorides by introducing the oxygen atoms.The present work not only predicts two NTE compounds, but also provides an insight on thermal expansion control by designing chemical bond type.     

Ultrahigh Loading Copper Single Atom Catalyst for Palladium-free Wacker Oxidation

Wacker oxidation is an industry-adopted process to transform olefins into value-added epoxides and carbonyls. However, traditional Wacker oxidation involves the use of homogeneous palladium and copper catalysts for the olefin addition and reductive elimination. Here, we demonstrated an ultrahigh loading Cu single atom catalyst(14% Cu, mass fraction) for the palladium-free Wacker oxidation of 4-vinylanisole into the corresponding ketone with N-methylhydroxylamine hydrochloride as an additive under mild conditions. Mechanistic studies by ¹⁸O and deuterium isotope labelling revealed a hydrogen shift mechanism in this palladium-free process using N-methylhydroxylamine hydrochloride as the oxygen source. The reaction scope can be further extended to Kucherov oxidation. Our study paves the way to replace noble metal catalysts in the traditional homogeneous processes with single atom catalysts.     

Stability of Multiplier Ideal Sheaves

Chinese Annals of Mathematics, Series B - In the present article, the authors find and establish stability of multiplier ideal sheaves, which is more general than strong openness.     

Nickel (II) tetrapyridyl complexes as electrocatalysts and precatalysts for water oxidation

Two nickel complexes, [Ni(tpen)](ClO₄)₂.0.5CH₃COCH₃ ( 1 ) and [Ni(tpbn)](ClO₄)₂ ( 2 ), of tetrapyridyl ligands N,N,N′,N′-tetrakis(2-pyridyl-methyl)-1,2-ethanediamine (tpen) and N,N,N′,N′-tetrakis(2-pyridyl-methyl)-1,4-butanediamine (tpbn) were prepared and their catalysis for water oxidation reaction (WOR) studied. In 0.1 M phosphate buffer solution (PBS) of pH 8.0, complex 1 is a homogeneous molecular catalyst with an overpotential of ~440 mV and a Faradaic efficiency of 89%. At pH ≥ 9.0, complex 1 degraded gradually during the catalytic process and formed NiO_x composite (nickel oxide with general formula Ni_xO_yH_z) active for WOR. In contrast, complex 2 deteriorated under measured conditions (pH 8.0–12.0) and formed NiO_x composite active for WOR. The NiO_x composite derived from 1 in 0.1 M PBS at pH 11.0 showed an activity with an overpotential of ~500 mV, a Tafel slope of ~90 mV/decade and a Faradaic efficiency of 97%. Mechanisms were proposed for water oxidation catalyzed by 1 and 2 . This work revealed that the catalytic activity of the nickel complexes was related to the flexibility of the tetrapyridyl ligands and the adaptability of the coordination sphere of the nickel(II) center.     

Dinuclear gold (I)-di-N-heterocyclic carbene complexes: syntheses,structure, density functional theory calculation and photoluminescence study

The synthesis and characterizations for a series of dinuclear gold (I)-di-NHC complexes, 1–8 through the trans-metalation method of their respective silver (I)-di-NHC complexes, i–viii are reported (where NHC = N-heterocyclic carbene). The successful complexation of a series of unusual non-symmetrical and symmetrical di-NHC ligands, 3,3'-(ethane-1,2-diyl)-1-alkylbenzimidazolium-1'-butylbenzimidazolium (with alkyl = methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, benzyl) with the gold (I) ions are suggested by elemental analysis, Fourier transform-infrared, ¹H- and ¹³C-NMR data. The ¹³C-NMR spectra of 1–8 show a singlet sharp peak in the range of 190.00–192.00 ppm, indicating the presence of a carbene carbon that bonded to the gold (I) ion. From single crystal X-ray diffraction data, the structure of complex 6 with the formula of [di-NHC-Au (I)]₂·2PF₆ is obtained [where NHC = 3,3'-(ethane-1,2-diyl)-1-hexylbenzimidazolium-1'-butylbenzimidazolium]. The photophysical study in solid state of 6 displays an intense photoluminescence with a strong emission maxima, λ_em = 480 nm, upon excitation at 340 nm at room temperature. Interestingly, the emission maximum at 77 K shows a structural character with a strong peak at 410 nm, a medium at 433 nm and a weak at 387 nm, accompanied by a tail band to about 500 nm.     

Nickel(II) Schiff base complex supported on nano‐titanium dioxide: A novel straightforward route for preparation of supported Schiff base complexes applying 2,4‐toluenediisocyanate

For the first time, a novel, straightforward and inexpensive route for immobilization of metals in Schiff base complex form is reported applying 2,4‐toluenediisocyanate as a precursor of primary amine group. A nickel(II) Schiff base complex supported on nano‐TiO₂ was designed and synthesized as an effective heterogeneous nanocatalyst for organic reactions, and well characterized using various techniques such as Fourier transform infrared spectroscopy, field emission scanning electron microscopy, transmission electron microscopy, X‐ray diffraction, energy‐dispersive X‐ray analysis and thermogravimetric analysis. The catalytic efficiency of the complex was evaluated in selective oxidation of sulfide to sulfoxide by hydrogen peroxide as an oxidant under solvent‐free conditions at room temperature, which successfully resulted in high yield and high conversion of products. Effective factors including solvent type, oxidant and catalyst amount were also optimized. The catalyst shows outstanding reusability and could be impressively recovered for six consecutive cycles without significant change of its catalytic efficiency.