多级孔芳香骨架材料的合成及固载硫脲催化剂的研究

合成了一种多级孔芳香骨架材料(PAF-70); 使用由氨基修饰过的单体, 应用该合成策略得到了同样具有窄分布介孔的含有氨基活性位点的PAF材料, 并通过硫脲单体与其氨基活性位点的反应, 将硫脲基团引入PAF-70材料中, 获得了含有硫脲催化位点的材料(PAF-70-thiourea). 氮气吸附-脱附测试结果显示, PAF-70存在孔径分布较窄的介孔, 介孔孔径为3.8 nm, 与模拟计算值(约3.7 nm)吻合. 热重分析结果表明, PAF-70具有很高的热稳定性. PAF-70在大多数溶剂中可以稳定存在, 具有良好的化学稳定性. 将PAF-70-thiourea作为催化剂, 应用在N-溴代琥珀酰亚胺(NBS)氧化醇类的反应中, 其表现出较高的催化活性、 较高的稳定性和广泛的底物适用性. 与含有相同硫脲催化位点的金属有机框架(MOF)材料(IRMOF-3-thiourea)作为催化剂对比, 进一步证实PAFs材料非常适合作为催化有机反应的固载平台.     

Insights into the efficient charge separation over Nb2O5/2D-C3N4 heterostructure for exceptional visible-light driven H2 evolution

Two-dimensional carbon nitride(2 D-C₃ N₄)nanosheets are promising materials in photocatalytic water splitting,but still suffer from easy agglomeration and fast photogene rated electron-hole pairs recombination.To tackle this issue,herein,a hierarchical Nb₂ O₅/2 D-C₃ N₄ heterostructure is precisely constructed and the built-in electric field between Nb₂O₅ and 2 D-C₃ N₄ can provide the driving force to separate/transfer the charge carriers efficiently.Moreover,the strongly Lewis acidic Nb₂O₅ can adsorb TEOA molecules on its surface at locally high concentrations to facilitate the oxidation reaction kinetics under irradiation,resulting in efficient photogene rated electrons-holes separation and exceptional photocatalytic hydrogen evolution.As expected,the champion Nb₂O₅/2 D-C₃N₄ heterostructure achieves an exceptional H2 evolution rate of 31.6 mmol g^-1 h^-1,which is 213.6 times and 4.3 times higher than that of pristine Nb₂O₅ and2 D-C₃N₄,respectively.Moreover,the champion heterostructure possesses a high apparent quantum efficiency(AQE)of 45.08%atλ=405 nm and superior cycling stability.Furthermore,a possible photocatalytic mechanism of the energy band alignment at the hetero-interface is proposed based on the systematical characterizations accompanied by density functional theory(DFT)calculations.This work paves the way for the precise construction of a high-quality heterostructured photocatalyst with efficient charge separation to boost hydrogen production.     

痕量K元素对煤基碳材料NOx低温吸附功能的影响机理

本研究选取准东煤为碳材料前驱体，以水热耦合痕量K元素的方法对其进行活化。通过实验探究K质量浓度对碳吸附性能的影响，同时系统研究了材料的NO_x低温吸附性能。实验结果表明，活化液中K₂CO₃质量浓度为0.0067g/mL时，所制得的样品对NO_x的吸附性能较好，其饱和NO_x吸附时间为3200 s。通过低温N₂物理吸附研究发现，该质量浓度下样品的孔结构发展较好，比表面积达到708.6 m²/g。此外，本研究通过XPS、SEM等手段对不同质量浓度K₂CO₃活化的碳基材料进行了物化表征，并对不同质量浓度K₂CO₃活化制备的样品进行了表面性质分析，通过FT-IR对样品表面的吸附过程进行研究，发现准东煤基碳材料优良的吸附性能与表面结构相关，研究中采用DFT手段对反应机理进行验证，结果表明，K可促进C-O键的形成，而活性C-O结构是促进NO_x吸...     

Is it universal that the layered-spinel structure can improve electrochemical performance?

The introduction of spinel phase to form the layered-spinel structure(LSS)is an effective way to improve the electrochemical performance of Li-and Mn-rich layered oxides(LMR).But is this structure universal for all LMR systems?In this work,different Mn/Ni ratio systems with the LSS are discussed in detail.It is found that,high discharge capacity(200.8 mA h g^-1 at 1C rate;1C=250 mA h g^-1)as well as high capacity-retention(94%at 1C rate after 100 cycles)can be achieved by forming the LSS for low-Ni system(Mn/Ni=5.0).However,the capacity retention decreases severely in the high-Ni system(Mn/Ni=3.5,2.6).For example,when the ratio of Mn/Ni is 3.5,the capacity-retention of the layered-spinel sample was only 65.8%,compared to the 83%of the original LMR sample.The Ex-situ XRD,XPS,and HRTEM results demonstrate that the introduction of spinel phase in high-Ni system accelerates the transition and collapse of the crystal structure.This work provides guidance for optimizing the proportions of elements and the design of structures for the LMR.     

疏水缔合悬浮稳定剂的合成及其对固井水泥浆稠度和悬浮稳定性的影响

针对大温差条件下固井水泥浆在固井过程中可能存在的悬浮失稳问题，本研究采用水溶液自由基聚合法来合成具有疏水缔合结构的聚合物作为悬浮稳定剂(PAAN)。通过红外光谱仪、凝胶渗透色谱仪、热重分析仪、高温流变仪、SEM、紫外分光光度计等表征PAAN的结构，发现PAAN随温度升高，形成分子间疏水缔合网状结构，保证了体系的粘度，从而起到有效的悬浮稳定作用。研究发现在40~110 ℃下，0.6%加量的PAAN可以保证固化后的水泥石柱顶部和底部密度差<0.01 g/cm³，且水泥浆稠化时间基本不变，表明PAAN可以保证水泥浆体系具有良好的悬浮稳定效果，且对水泥浆的其他性能无不良影响。     

基于抛光基材的热蒸镀铜箔生长高平整单层石墨烯薄膜

在石墨烯的化学气相沉积工艺中,铜箔是决定石墨烯薄膜质量的重要因素。传统铜箔由于制备工艺的限制,存在大量的缺陷,导致石墨烯薄膜的成核密度较高。本工作选用抛光铝板、抛光不锈钢板、微晶玻璃和SiO₂/Si作为基材,用热蒸镀法制备了不同粗糙度的铜箔,并详细讨论了以该系列铜箔生长高平整度石墨烯薄膜的条件及铜箔对石墨烯薄膜品质的影响。实验结果表明,铜箔以(111)取向为主,与基材分离后,表面具有纳米级平整度。在生长石墨烯后,从SiO₂/Si剥离的铜箔成核密度是4种基材中最小的。同时,从SiO₂/Si剥离的铜箔晶体结构变化最不明显,具有良好的结晶性,表面几乎不存在铜晶界缺陷。当压强为3 000 Pa,氢气和甲烷流速分别为300 mL/min和0.5 mL/min时,可以获得约1 mm横向尺寸的石墨烯单晶晶畴。     

水热法制备二氧化锡/钨酸铋复合光催化材料及其催化活性研究

本文用水热法制备了正交晶系的纳米球状结构的二氧化锡和正交晶系的由片状聚集成球状结构的钨酸铋,并且对二者进行了复合,制备出了二氧化锡/钨酸铋复合光催化材料。采用X射线衍射(XRD)、扫描电子显微镜(SEM)、比表面积测试仪(BET)、紫外可见分光光度计等技术对复合样品的结构、形貌、比表面积、孔容孔径和光学性质进行了表征。用碘钨灯模拟太阳光,分别以二氧化锡、钨酸铋和二氧化锡/钨酸铋复合材料为催化剂降解罗丹明B(RhB),研究所制备的二氧化锡/钨酸铋复合材料的光催化活性。光催化90 min时二氧化锡、钨酸铋和二氧化锡/钨酸铋对罗丹明B的降解率分别是9%、22%和30%。实验结果表明,在可见光下,二氧化锡/钨酸铋复合材料的光催化活性要高于单一的二氧化锡和钨酸铋。     

基于SEIR模型的COVID-19疫情防控效果评估和预测

通过对COVID-19疫情在中国的传播情况进行分析，建立了一个SEIR流行病模型，模型中将确诊人群分成已收治和未收治两类.先从理论上分析了模型的无病平衡点及其稳定性、基本再生数等关键问题；再结合实际数据，对武汉封城前和封城后两个阶段疫情的发展趋势进行数值模拟和比较分析，讨论了模型中一些重要参数对确诊人数的影响；最后，针对上述理论分析和数值模拟的结果，对之前采取的一些控制策略作了分析评估，同时对疫情后期发展进行预测.     

水热法一锅合成Ni/ZrO2加氢催化剂

采用水热法一锅合成了一系列四方相ZrO2负载Ni的加氢催化剂,以苯加氢生成环己烷为探针反应,对比研究了其同其它方法合成的Ni/ZrO2催化剂的催化加氢性能。通过XRD、H2-TPR、H2-TPD、TEM及N2物理吸附等表征及催化评估显示,相较于浸渍法得到的Ni/ZrO2催化剂,水热法一锅合成的Ni/ZrO2催化剂具有比表面积更大、纳米颗粒更小,Ni分布更均匀等特点,催化效果更佳。其中15%的Ni负载量为最佳负载量,表现出最佳的催化活性,在120℃左右即可转化率达到100%。