发光铱(Ⅲ)配合物抗肿瘤活性研究及应用

铱(Ⅲ)配合物因其发光量子产率高且波长易调控、发光寿命长和光稳定性好的特点,在发光材料领域备受关注。铱(Ⅲ)配合物细胞渗透能力强,能靶向多种细胞组织并影响其结构和功能,表现出独特的抗肿瘤活性,是目前金属抗肿瘤药物特别是PDT光敏剂方向的研究热点。本文重点关注铱(Ⅲ)配合物的结构对其发光性能与抗肿瘤性能的影响,综述了近期铱(Ⅲ)配合物在生物成像、探针与传感、抗肿瘤诊疗等领域的研究进展,并对目前研究中存在的问题及其应用前景进行探讨和展望。     

Theoretical study of (e,2e) triple differential cross sections of pyrimidine and tetrahydrofurfuryl alcohol molecules using multi-center distorted-wave method

We report theoretical studies of electron impact triple differential cross sections of two bio-molecules,pyrimidine and tetrahydrofurfuryl alcohol,in the coplanar asymmetric kinematic conditions with the impact energy of 250 eV and ejected electron energy of 20 eV at three scattering angles of-5°,-10°,and-15°.Present multi-center distorted-wave method well describes the experimental data,which was obtained by performing(e,2e)experiment.The calculations show that the secondary electron produced by the primary impact electron is strongly influenced by the molecular ionic multi-center potential,which must be considered when the low energy electron interacts with DNA analogues.     

直接碳燃料电池燃料的研究进展

直接碳燃料电池(DCFC)是一种清洁高效利用碳资源发电的装置。其因能量转换率高,对环境污染小,燃料选择范围广等优点获得了越来越多的关注。DCFC的性能与使用的燃料密切相关,为了探究燃料对DCFC的影响,本文分别阐述了石墨、炭黑、中密度纤维板、生物质、煤、活性炭的特性及改性方法,分析讨论了燃料表面含氧官能团以及燃料中的金属催化剂对阳极电化学反应的促进作用,发现燃料表面化学性质要比比表面积更加重要。同时,本文也提出了对生物质这一优良的可再生资源的期待,为未来DCFC燃料的发展提供参考。     

石墨烯负载的氧配位钴单原子稳定金属锂负极

Lithium (Li)-based batteries are the dominant energy source for consumer electronics, grid storage, and electrified transportation. However, the development of batteries based on graphite anodes is hindered by their limited energy density. With its ultrahigh theoretical capacity (3860 mAh∙g⁻¹), low redox potential (−3.04 V), and satisfactorily low density (0.54 g∙cm⁻³), Li metal is the most promising anode for next-generation high-energy-density batteries. Unfortunately, the limited cycling life and safety issues raised by dendrite growth, unstable solid electrolyte interphase, and "dead Li" have inhibited their practical use. An effective strategy is to develop a suitable lithiophilic matrix for regulating initial Li nucleation behavior and controlling subsequent Li growth. Herein, single-atom cobalt coordinated to oxygen sites on graphene (Co-O-G SA) is demonstrated as a Li plating substrate to efficiently regulate Li metal nucleation and growth. Owing to its dense and more uniform lithiophilic sites than single-atom cobalt coordinated to nitrogen sites on graphene (Co-N-G SA), high electronic conductivity, and high specific surface area (519 m²∙g⁻¹), Co-O-G SA could significantly reduce the local current density and promote the reversibility of Li plating and stripping. As a result, the Co-O-G SA based Li anodes exhibited a high Coulombic efficiency of 99.9% at a current density of 1 mA∙cm⁻² with a capacity of 1 mAh∙cm⁻², and excellent rate capability (high current density of 8 mA∙cm⁻²). Even at a high plating capacity of 6 mAh∙cm⁻², the Co-O-G SA electrode could stably cycle for an ultralong lifespan of 1300 h. In the symmetric battery, the Co-O-G SA based Li anode (Co-O-G SA/Li) possessed a stable voltage profile of 18 mV for 780 h at 1 mA∙cm⁻², and even at a high current density of 3 mA∙cm⁻², its overpotential maintained a small hysteresis of approximately 24 mV for > 550 h. Density functional theory calculations showed that the surface of Co-O-G SA had a stronger interaction with Li atoms with a larger binding energy, −3.1 eV, than that of Co-N-G SA (−2.5 eV), leading to a uniform distribution of metallic Li on the Co-O-G SA surface. More importantly, when matched with a sulfur cathode, the resulting Co-O-G SA/lithium sulfur full batteries exhibited a high capacity of 1002 mAh∙g⁻¹, improved kinetics with a small polarization of 191 mV, and an ultralow capacity decay rate of 0.036% per cycle for 1000 cycles at 0.5C (1C = 1675 mA∙g⁻¹) with a steady Coulombic efficiency of nearly 100%. Therefore, this work provides novel insights into the coordination environment of single atoms for the chemistry of Li metal anodes for high-energy-density batteries.     

水热法制备二氧化锡/钨酸铋复合光催化材料及其催化活性研究

本文用水热法制备了正交晶系的纳米球状结构的二氧化锡和正交晶系的由片状聚集成球状结构的钨酸铋,并且对二者进行了复合,制备出了二氧化锡/钨酸铋复合光催化材料。采用X射线衍射(XRD)、扫描电子显微镜(SEM)、比表面积测试仪(BET)、紫外可见分光光度计等技术对复合样品的结构、形貌、比表面积、孔容孔径和光学性质进行了表征。用碘钨灯模拟太阳光,分别以二氧化锡、钨酸铋和二氧化锡/钨酸铋复合材料为催化剂降解罗丹明B(RhB),研究所制备的二氧化锡/钨酸铋复合材料的光催化活性。光催化90 min时二氧化锡、钨酸铋和二氧化锡/钨酸铋对罗丹明B的降解率分别是9%、22%和30%。实验结果表明,在可见光下,二氧化锡/钨酸铋复合材料的光催化活性要高于单一的二氧化锡和钨酸铋。     

脱硫石膏制备硫酸钙晶须结晶动力学研究

结晶动力学能够揭示结晶过程本质,通过测定溶液中Ca2浓度来确定硫酸钙晶须的转化率,从而确定硫酸钙晶须结晶动力学参数,得到转化率与时间的关系式:X=1/｛1+e6^[-10.01977t(0.0956-c)+1.1188]｝,(0≤t≤6.0).研究了影响硫酸钙晶须结晶动力学的影响因素降温速率和陈化时间,利用SEM对制备的硫酸钙晶须进行表征.结果表明:自然冷却条件下,陈化时间6h,制备出的硫酸钙晶须结晶发育完整,晶须平均长径比达到150,平均直径为2.1 μm.     

中空介孔SiO2纳米球的制备、改性及其对Al3+荧光识别研究

中空介孔SiO2由于中空多孔的结构而常用作功能材料的基底.将中空介孔SiO2进行官能团修饰,并应用为荧光传感材料是中空介孔SiO2一个重要的研究领域.本论文采用聚丙烯酸(PAA)为中空模板,聚醚F127为造孔剂,正硅酸乙酯(TEOS)为硅源,氨水为催化剂在乙醇体系中制备了中空介孔SiO2纳米球.系统研究了搅拌速度和聚醚F127引入量对中空介孔SiO2纳米球形貌及比表面积的影响.通过透射电镜、N2-等温吸附脱附曲线等表征说明该合成方法具有很好的普适性,通过调节F127的引入可以实现对比表面积的有效控制.通过氨基化、席夫碱反应进行荧光修饰,进一步研究表明荧光修饰后的中空介孔SiO2纳米球在水溶液中能够实现对Al3+的有效检测,检测限为1.19×10 -7M.     

陶瓷基功能材料载体纤维增强效果及机理

以陶瓷基功能材料载体为研究对象,按照其生产工艺配方,研究了纤维种类(莫来石、氧化铝、氧化锆)及其添加量对陶瓷基功能材料载体性能的影响.在相同实验条件且不影响其功能化参数前提下,将其与未添加纤维的空白试样力学性能进行对比.结果表明,试样经1200℃烧成后,相比莫来石与氧化铝纤维增强的陶瓷基功能材料载体,氧化锆纤维的增强效果最好.当氧化锆纤维的添加量为0.8 wt;时,试样的吸水率和气孔率均较低,分别为2.0;、4.0;,相比空白对比试样抗折强度增强了42.4;.     

氨基功能化磁性CoFe2O4/氧化石墨烯去除电镀废水中Cr(Ⅵ)的研究

使用改良的hummers法制备出的氧化石墨烯为载体,采用共沉淀法制备出磁性CoFe2O4/氧化石墨烯(MGO),再使用三乙烯四胺(TETA)对磁性CoFe2O4/氧化石墨烯进行氨基功能化,制备出氨基功能化磁性CoFe2O4/氧化石墨烯吸附剂.采用X-射线衍射仪(XRD)、傅里叶变换红外光谱仪(FT-IR)和扫描电子显微镜(SEM)对TETA-MGO的物相、化学组成和微观形貌进行表征,以TETA-MGO作为吸附剂去除电镀废水中Cr(Ⅵ),探讨吸附性能和吸附机理,分析TETA-MGO在外加磁场下的液固分离和再生吸附性能.结果表明纳米级立方尖晶石相磁性CoFe2O4均匀生长于氧化石墨烯的表面和片层之间,TETA通过C-N键与磁性氧化石墨烯(MGO)相连,氨基功能化成功,活性吸附位点增点.室温下,pH =2时吸附效果最佳,吸附120 min时达到吸附平衡,平衡吸附量约为48.66 mg·g-1,TETA-MGO对Cr(Ⅵ)的吸附动力学和吸附热力学可分别使用拟二级动力学模型和Langmuir等温吸附模型描述,吸附过程主要属于化学吸附控制的单分子层吸附,使用外加磁场可以对TETA-MGO实现简单的固液分离,TETA-MGO经过6次再生吸附后,对Cr(Ⅵ)的吸附量仅下降19.67;,说明具有良好的循环再生吸附能力.     

LaNi0.5Co0.5O3催化剂对甲烷二氧化碳干重整反应在CO2渗透膜反应器中的影响

制备了混合导体膜反应器,通过电化学方法捕获CO2,并将其用于甲烷二氧化碳干重整反应中.采用XRD, SEM,TPR等技术系统研究了LaNi0.5Co0.5O3催化剂在膜反应器中对甲烷二氧化碳干重整反应的影响.结果表明:LaNi0.5Co0.5O3催化剂在甲烷干重整反应中能原位析出纳米金属Ni和Co,对反应起到了较好的催化作用,同时抑制了积碳.催化剂还具有良好的氧化还原性能,可以循环利用.