采用浸渍法制备Fe-VO_x/SAPO-34和Fe-VO_x/TiO₂脱硝催化剂,探究SAPO-34分子筛与TiO₂两种载体负载铁钒基氧化物催化活性及抗碱性能的差异。借助X射线衍射(XRD)、X射线光电子能谱(XPS)、氨气程序升温脱附(NH₃-TPD)、氢气程序升温还原(H₂-TPR)、原位红外漫反射(in-situ DRIFTs)等表征手段对催化剂的骨架结构、表面物化性质、氧化还原能力以及对反应气体的吸脱附情况进行分析。结果表明:SAPO-34分子筛内部特定的孔道结构和稳定的骨架,有利于活性组分在载体上均匀分散,降低碱金属对表面活性中心的物理覆盖作用;同时其表面丰富的酸位点能够作为碱金属捕获位,保护催化剂表面的活性中心,保证催化剂的吸附-反应过程能够正常进行,从而使Fe-VO_x/SAPO-34表现出良好的抗碱金属能力。     

g-C3N4-W18O49复合光催化剂的制备及其光催化机理研究

通过简单的溶剂热法成功制备出了g-C3N4-W18O49复合光催化剂,采用XRD、SEM、TEM以及PL对所得催化剂的物相结构及形貌和光学性能进行了表征,通过降解甲基橙和光解水产氢实验研究所得催化剂的催化性能及其催化机理.由实验可知,W18O49的含量为50;时所得g-C3N4-W18O49复合光催化剂的降解性能最好,其降解率比纯g-C3N4纳米片提高48;;为进一步研究复合光催化剂的电子-空穴传输机理,我们又进行了光解水制氢实验.结果表明:单一的W18O49无产氢活性,它的复合明显降低了g-C3N4的产氢速率,说明复合结构中光生电子是从g-C3N4传递到了W18O49,表现出明显的Ⅱ型异质结复合特征,而不是部分文献所提出的Z型方式.     

两个基于2,5-二甲氧基对苯二甲酸和咪唑衍生物的超分子钴配位聚合物的结构及光催化反应

本文以咪唑衍生物为配体,通过水热合成法与钴离子制备出两个配位聚合物:{[Co(DTA)(1,4-DIB)(H₂O)]·H₂O}_n(1)和[Co(DTA)(1,3-BMIB)]_n(2)(1,4-DIB=1,4-二(1H-咪唑-1-基)苯; 1,3-BMIB=1,3-二(4-甲基-1H-咪唑-1-基)苯;H₂DTA=2,5-二甲氧基对苯二甲酸)。利用X射线单晶衍射、粉末衍射、热失重、元素分析、红外光谱以及固体紫外-可见光谱等对两个配合物进行了表征。结构分析证实配合物1和2是通过二维结构堆积成的三维超分子化合物。粉末衍射测试则显示两个配合物在水中有很好的稳定性。固体紫外-可见光谱显示两个配合物属半导体材料,对紫外-可见光有很强的吸收作用。在光催化实验中,配合物1和2可加快亚甲基蓝的降解速度。     

17β-雄甾醇-[3,2-b]-吲哚的合成

以表雄酮为原料,经羟基氧化、羰基保护、还原、Fischer吲哚环化等反应合成了17-β-醇-雄甾-[3,2-b]-吲哚(5),总收率43.2%,其结构经1H NMR,IR和MS确证。生物活性初步测试结果表明:与雄诺龙相比,5对淡色库蚊的杀虫活性显著提高,在浓度为400 mg·L-1时,杀虫率为41.5%。     

焊后热处理对聚变堆用奥氏体不锈钢MAG焊焊缝金属冲击韧性的影响

After heat treatment of metal active gas arc welding (MAG weld) joints of 316LN austenitic stainless steel for fusion reactor at different temperatures, Charpy impact test at liquid nitrogen temperature was carried out. The effects of heat treatment temperature on microstructure, fracture morphology and precipitates were studied with optical microscope, SEM and EDS analysis. Results indicated that the impact toughness of weld metal could be significantly improved by 873K heat treatment. However, with the rising of heat treatment temperature, the precipitates were generated gradually along the grain boundary and a gradual decrease of toughness occurred as well. All fracture was ductile. The dimple became shallow and less with the increase of temperature. Spherical and irregular precipitates were found at the bottom of the dimple. The spherical precipitates generated during welding were free from the influence of the heat treatment, and the irregular precipitates increased with the rising of temperature. High content of Mo in filler materials led to a great segregation of Mo at the grain boundary, which would promote the precipitation of σ phase. Impact toughness of weld metal decreased significantly when continuous distribution of σ phase formed at grain boundary.     

新型氨基嘧啶环戊并[b]吲哚衍生物的合成及抗肿瘤活性

3-吲哚丙酸为原料，经环化、N-甲基化、Claisen-Schmidt缩合、环加成反应得到新型氨基嘧啶环戊并[b]吲哚衍生物。经¹HNMR、¹³CNMR以及HR-MS（ESI）表征。采用细胞增殖抑制实验法（MTT法）测定6a~6j对人肝癌（HepG-2）、人子宫颈癌（Hela）和人鼻咽癌（CNE-1）瘤株的体外抑制活性。6b对这些肿瘤细胞的抑制活性最好，其IC50值分别为大于50 μmol/L（HepG-2）、15.2 μmol/L（Hela）和14.8 μmol/L（CNE-1），但均弱于顺铂。