甲醇在不同结构氧化钨-Pt/C催化剂上的电催化氧化行为

采用水热法合成2种氧化钨（WO3）纳米材料,并利用XRD和电子探针显微分析仪（EPMA）进行了表征。 利用循环伏安法研究了Pt-WO3/C电极对甲醇氧化的电催化活性。 结果表明,Pt-WO3/C催化剂对甲醇氧化的电催化活性优于Pt/C催化剂,且氧化钨质量分数为20%的Pt-氧化钨/C催化效果最好。 与青铜相氧化钨掺杂的Pt/C电极比较,掺杂焦绿石型氧化钨的Pt/C电极催化性能有很大提高,这是由于焦绿石型氧化钨表面具有较多OHads。 质量分数20%的Pt-焦绿石型氧化钨/C在0.5 mol/L CH3OH+1 mol/L H2SO4溶液中对甲醇氧化的峰电流密度达到87.2×10-3 A/cm2。     

微悬臂梁检测三肽Gly-Gly-His与Cu~(2+)的相互作用过程

将三肽Gly-Gly-His(GGH)共价键合到MPA修饰的微悬臂梁表面,研究了肽与Cu2+的相互作用过程.研究发现,在Cu2+浓度较高时,Cu2+能快速与不同肽链上的羧基和咪唑环配位,并通过连锁反应诱导悬臂梁向镀金面偏转;而后肽链上的氮原子与Cu2+配位,同时构象发生变化,由直链转变成折叠状,进而增加链间的作用力使悬臂梁反向偏转;而Cu2+浓度低时不能实现连锁反应诱导悬臂梁表面快速的形成向内的拉力,直接通过构象变化推动悬臂梁反向偏转.考察了溶液pH值、Cl-浓度对GGH与Cu2+作用的影响,结果表明,在pH 7.0的条件下GGH与Cu2+作用导致悬臂梁偏转最大.Cl-的存在会与Cu2+形成CuCl2–xx配合物不易与肽链结合.     

一维链状柔性羧酸镉配位聚合物[Cd(p-BDOA)·2H2O]n的合成、结构与性质研究(英)

A novel 1-D Cd(Ⅱ) coordination polymer, [Cd(p-BDOA)·2H₂O]_n(I) ( p-BDOA^2-=benzene-1,4-dioxyacetate dianion) has been synthesized and characterized by elemental analysis, IR, PL, TG and X-ray single crystal diffraction. The Crystal crystallizes in monoclinic system, the space group is C2/c, with the crystal cell parameters a=1.175 1(1) nm, b=0.551 0(1) nm, c=1.827 7(2) nm, β=96.14(2)°, and V=1.176 6(3) nm^3,, M_r=372.60, R=0.045 9, wR=0.127 9. The Cd(Ⅱ) ion has a trigonal prism coordination configuration that defined by four carboxyl O atoms from two different p-BDOA^2- ligands and two water molecules. Adjacent Cd(Ⅱ) ions are linked by carboxylate groups with the bidentate coordination mode, giving rise to a chain structure with the adjacent Cd…Cd distance of 1.526 3(5) nm. Furthermore, such chains are linked by hydrogen bonds to form supramolecular network. The results of PL and TG show that the complex exhibits intense fluorescent emissions and its chain skeleton is thermally stable up to 419 K. CCDC: 220443.     

碱基腺嘌呤与胸腺嘧啶在Au(111)电极上的共吸附

用循环伏安法(CV)和电化学扫描隧道显微镜(ECSTM)在HClO4溶液中研究了配对碱基腺嘌呤(Adenine,A)与胸腺嘧啶(Thymine,T)在Au(111)电极上的共吸附行为.CV曲线表明,A和T的电化学共吸附行为更接近于A的电化学吸附行为.高分辨STM图像显示,在物理吸附区域碱基A和T分子之间通过氢键作用形成一种不同于单组分的网络结构.根据STM图像提出一个可能的模型,并给出了在Au(111)电极上共吸附时A和T分子之间可能的氢键作用方式.     

具有不同形貌和择优取向的MxWO3·xH2O粉晶的制备与表征

采用沉淀结合渗析的方法，以钨酸钠、钨酸铵为原料，制备了不同形貌、具有择优取向的M_xWO₃·xH₂O(M=Na⁺，NH₄⁺，x<1)粉晶，利用SEM、XRD、TG、IR、XPS等手段对粉体进行表征，考察了不同渗析时间和焙烧温度对粉晶形貌、晶化程度及结构转变的影响。结果表明，长时间渗析后粉体的晶化程度明显提高，并沿(010)晶面方向择优生长，形貌由不规则形变为梭形和蝴蝶形。经空气气氛400 ℃焙烧后，Na_xWO₃·xH₂O和(NH₄)_xWO₃·xH₂O粉晶均转变为沿(200)晶面方向择优生长的立方青铜相，且形貌也发生改变。     

介稳态氧化钨超微粉体的水热合成与光致变色性质研究

Under hydrothermal conditions, the superfine powders of cubic pyrochlore-type of tungsten oxide and hexagonal tungsten bronze were obtained by using Na₂WO₄·2H₂O as the starting material. The products were characterized by XRD, TG, IR, UV and EPMA, respectively. The effects of the pH value, the acid concentration, reaction temperature and time on the structure and particle size of products were investigated in detail. The conditions for the preparation of superfine powders of tungsten oxide were optimized. The pH 2.5～4.5 of the reaction system led to the formation of a pyrochlore phase and pH 0.5～2.0 gave the hexagonal tungsten bronze structure. The photochromism property of the hexagonal tungsten bronze was studied. The results show that pyrochlore and bronze phases are decomposed at 300 ℃ and 450 ℃, respectively. With the increasing of temperature, the structure of the two oxides changes. The pyrochlore-type powder changes completely into triclinic Na₂W₄O₁₃ around 500 ℃, while the bronze phase into a mixture of Na₂W₆O₁₉ and triclinic WO₃ at 550 ℃. The powder of the hexagonal tungsten bronze showed better photochromism property.     

溶胶-凝胶法制备In-Cd纳米复合氧化物及其气敏性能研究

采用溶胶凝胶法制备了In20rCdln2O4和CdO-Cdln2O4纳米复合氧化物,利用扫描电子显微镜(SEM)和X射线衍射仪(XRD)对复合材料的形貌和结构进行表征,并对其进行了乙醇、丙酮等多种气体的气敏性能测试.结果表明Cdln2O4材料复合h12O3和CdO后显著提高了对丙酮和乙醇气体的灵敏度和选择性.     

原位生长的α-Fe2O3/ZnO异质纳米棒阵列对乙醇气体的高选择性检测

采用两步溶液法在陶瓷管上原位生长了ZnO纳米棒阵列,然后以ZnO纳米棒为载体,通过水热法在其表面负载α-Fe₂O₃纳米粒子,生成异质α-Fe₂O₃/ZnO复合纳米材料。 α-Fe₂O₃/ZnO纳米棒直径30~80 nm,长1 μm左右,交叉排列形成纳米棒阵列,α-Fe₂O₃纳米粒子粒径约10 nm,均匀分布在ZnO纳米棒表面。 将纯ZnO和α-Fe₂O₃/ZnO纳米棒阵列制成气敏元件,测试并对比了2种气敏元件的气敏性能,揭示其气敏机理。 结果表明:α-Fe₂O₃纳米粒子的复合显著提高了ZnO纳米棒阵列对乙醇气体的灵敏度和选择性,在工作温度370 ℃时,对100 μL/L乙醇气体的响应值为85.4,是同条件下ZnO器件对乙醇响应值(9.4)的9.1倍,响应时间7 s,最低检出限为0.01 μL/L。 相关研究可以应用于痕量乙醇的快速、高灵敏度和高选择性检测。     

ZnO纳米薄膜的制备及其气敏性质研究

纳米氧化锌薄膜具有光电、压电、压敏和气敏等多种性质,使其在透明导体、发光元件、太阳能电池窗口、光波导器、单色场发射显示器、高频压电转换器、微传感器等方面具有广泛的用途.     

反应离子束微细加工全息闪耀光栅研究

本文报道以无透镜傅里叶全息术变换记录的全息光栅作掩膜,应用反应离子束入射角控制光栅闪耀角,选择了合适刻蚀工艺参数,制得衍射效率为67%的SiO_2全息闪耀光栅。