界面预湿处理对异质增强型PVDF中空纤维膜结构与性能的影响

以熔融纺丝聚氯乙烯(PVC)中空纤维多孔膜为增强体,聚偏氟乙烯(PVDF)为成膜聚合物,聚乙烯吡咯烷酮(PVP)为添加剂,N,N-二甲基乙酰胺(DMAc)为溶剂,配置铸膜液,采用同心圆牵引-涂覆法制备了异质增强型PVDF中空纤维膜.制备过程中,采用预湿溶液对增强体基膜表面进行预处理,研究了预湿溶液组成及含量对异质增强型PVDF中空纤维膜结构与性能的影响.结果表明,未经预湿处理的异质增强型PVDF中空纤维膜具有较厚的致密界面层;预湿溶液可对基膜表面孔起到保护作用,使异质增强型PVDF中空纤维膜的界面层变薄或形成多孔界面层,有益于改善增强型PVDF中空纤维膜的通透性能;与二甲基乙酰胺(DMAc)水溶液相比,以乙醇水溶液为预湿溶液所得异质增强型PVDF中空纤维膜的性能较优;当预湿液中乙醇含量为60 wt%时,所得增强型PVDF中空纤维膜的渗透性能较优,拉伸强度可达8.61 MPa.     

三醋酸纤维素/壳聚糖反渗透膜的制备及性能研究

以壳聚糖(CS)为抗菌剂和三醋酸纤维素(CTA)为基膜材料,通过液-液共混和相转化成膜技术制备了三醋酸纤维素/壳聚糖共混反渗透膜(CTA/CS-RO),以改善醋酸纤维素反渗透膜的抗菌性能.采用傅里叶红外光谱、X-射线光电子能谱、扫描电子显微镜、水接触角、X-射线衍射光谱等对其结构和性能进行表征.结果表明,CTA/CS-RO中CS与CTA之间存在氢键作用,并且CS随着双扩散过程向膜表面迁移;膜厚度随着CS含量的递增而减小,横断面结构由指状孔转变成海绵状.CS的添加有利于共混膜亲水性、水通量和力学性能的提高.当CS含量为0.75%~1.00%时,膜样品在保持较高的盐截留率(R90%)的同时其断裂伸长率和结晶度没有显著变化.动态接触抗菌测试结果表明,CTA/CS-RO对大肠杆菌和金黄色葡萄球菌均具有抑菌作用.特别地,当CS含量为0.75%~1.00%时,膜样品对大肠杆菌和金黄色葡萄球菌的抑菌率分别为65%~72.5%和16%~51%.综合分析,CTA/CS共混反渗透膜制备过程中CS的加入量保持在0.75%~1.00%时膜的综合性能最优.     

熔融纺丝制备中空纤维膜研究进展

中空纤维膜作为一种重要的分离膜材料,其制备方法一直以来是膜技术研究领域的热点。相对于溶液法纺丝制膜方法而言,熔融纺丝法具有使用溶剂量少、环境友好、所得中空纤维膜力学性能较优等特点,已成为目前中空纤维膜制备的重要技术之一。本文根据工艺将熔融纺丝制膜方法区分为熔融纺丝-拉伸法和热致相分离法,分别就这两种方法中空纤维膜的制备技术及致孔机理进行介绍,并对二者的研究历史及现状进行了论述,最后,还指出了熔融纺丝制备中空纤维膜研究领域有待解决的问题。     

纤维编织管增强型中空纤维膜研究

采用二维编织技术将聚丙烯腈(PAN)长丝编织成中空纤维编织管作为增强体,分别以聚丙烯腈(PAN)和聚偏氟乙烯(PVDF)为成膜聚合物,N,N-二甲基乙酰胺(DMAc)为溶剂,聚乙烯吡咯烷酮(PVP)为添加剂,调制铸膜液,采用同心圆挤出-涂覆法制备了PAN纤维编织管同质增强型PAN中空纤维膜和异质增强型PVDF中空纤维膜.研究表明,所得PAN纤维编织管增强型中空纤维膜断裂强度最大可超过75 MPa,在伸长率10%范围内,表面分离层与增强体之间界面结合良好;表面分离层具有类似于非对称膜的结构,铸膜液可浸入纤维编织管纤维空隙中,铸膜液浸入部分固化后未影响膜的通透性能;随成膜聚合物浓度增加,膜纯水通量减小,牛血清白蛋白(BSA)截留率增大;随添加剂PVP浓度增加,膜的纯水通量先增大后减小,在8 wt%左右达最大值,BSA截留率随PVP浓度增加而单调增加;同质增强型中空纤维膜界面结合程度优于异质增强型.     

二极管阵列检测—偏最小二乘吸光光度法同时测定铜锌

研究了以２－（５－溴－２－噻唑偶氮）５－二乙氨基苯酚（５－Ｂｒ－ＰＡＤＡＰ）作显色剂,ＣＣＤ（Ｃｈａｒｇｅ Ｃｏｕｐｌｅｄ Ｄｅｖｉｃｅ,电荷耦器件）二极管阵列检测分光光度装置采及收光谱,用偏最小二乘法解析,同时测定了粮食中铜和锌。方法的线性范围锌为０．０５～０．４０μｇ．ｍｌ＾－１,铜为０．０２～０．６０μｇ．ｍｌ＾－１;检出限铜为０．０２μｇ．ｍｌ＾－１,平均加标回收率锌为９３．３％～９５．７     

Stretchable electromagnetic interference shielding and antenna for wireless strain sensing by anisotropic micron-steel-wire based conductive elastomers

We prepare stretchable elastic electromagnetic interference(EMI) shielding and stretchable antenna for wireless strain sensing using an elastic composite comprising commercial steel wool as a conducting element. The prepared elastic conductor shows anisotropic electrical properties in response to the external force. In the stretchable range, the electrical resistance abnormally decreases with the increase of tensile deformation. The EMI shielding effectiveness of the elastic conductor can reach above-30 d B under 80% tensile strain. The resonance frequency of the dipole antenna prepared by the elastic conductor is linearly correlated with the tensile strain, which can be used as a wireless strain sensor. The transmission efficiency is stable at about-15 d B when stretched to 50% strain, with attenuation less than 5%. The current research provides an effective solution for stretchable EMI shielding and wireless strain sensing integrated with signal transmission by an antenna.     

咪唑类离子液体辅助水热法合成棒状微/纳米ZnO晶体

以醋酸锌和氢氧化钠为原料,以水和含不同长度烷基链的咪唑类氯盐离子液体的混合物作为反应介质,采用水热法合成出不同形貌的微/纳米ZnO晶体,用扫描电子显微镜(SEM)和X射线衍射仪(XRD)对合成的ZnO晶体进行表征.研究了烷基链长度、离子液体用量、反应时间以及反应温度对形成棒状ZnO晶体形貌的影响.实验结果表明,所制备的棒状ZnO晶体样品均为六方晶系结构.在棒状ZnO晶体的制备过程中,控制反应温度,选择不同的离子液体及其用量十分重要.     

低共熔溶剂辅助水热法合成分层球状微/纳米ZnO晶体及其光催化性能

使用尿素-氯化胆碱低共熔溶剂(UCC-DES),采用水热合成和反溶剂(乙醇)法,以化工材质ZnO粉末为原料制备了分层的球状微/纳米ZnO晶体.分析了反应时间、反溶剂的种类和含量对ZnO晶体形貌的影响以及ZnO晶体析出的原因.并将制备的分层球状ZnO微/纳米晶体应用于光催化降解甲基橙.结果表明,制备的ZnO晶体对甲基橙有良好的光催化降解性能.     

熔纺聚氨酯系中空纤维膜的结构与性能

将聚氨酯/聚偏氟乙烯/聚乙二醇(PU/PVDF/PEG)熔融共混纺丝制得中空纤维膜,对纤维膜的微孔结构与性能进行研究,分析影响其水通量衰减的因素。结果表明:所得纤维膜具有界面及非界面微孔结构;随着水通量工作环境的变化,膜孔结构发生相应变化,表现出压力及温度响应性能;而经热处理后,所得膜部分微孔闭合,水通量下降;随测试时间延长,膜结构趋于致密化,水通量衰减。     

聚合物分离膜成形过程中相分离数值模拟研究进展

针对热力学、动力学、流体力学等多方面研究成果,分析多种先进的计算机模拟方法,对聚合物分离膜相分离过程的数值模拟进行介绍.从简单的二元体系到三元、四元体系,从等温传质到非等温传质,从自扩散系数到共扩散系数的应用,从一维扩散到多维扩散,对蒙特卡洛法、Lattice Boltzmann法、Cahn-Hilliard方程、物质...