纳米MgNb2O6微波介质陶瓷粉体制备及表征

Nano-crystalline MgNb₂O₆ was prepared using Mg(NO₃)₂·6H₂O, Nb₂O₅, HF and citric acid as raw materials by auto-ignition route. The process involves the formation of a viscous gel by thermal dehydration of the citrate-nitrate solution at about 80 ℃. The auto-ignition (at about 200 ℃) of the gel resulted in a high reactivity powder containing intimate blending of MgNbF₇ and NbF₃. The crystalline phase of MgNb₂O₆ could be formed easily at 700 ℃, which is 400 ℃ lower than that of common solid-state reaction process. The nano-crystalline MgNb₂O₆ (～30 nm) powder with good dispersity could be obtained at 850 ℃.     

溶胶-凝胶法制备(Ca1-xMgx)SiO3陶瓷及其微波介电性能

以硝酸钙、硝酸镁、正硅酸乙酯为先驱体, 利用溶胶-凝胶法合成(Ca1-xMgx)SiO3(x=0.1、0.2、0.3、0.4、0.5)陶瓷粉体, 研究了Mg2+取代Ca2+对陶瓷物相组成、烧结特性以及微波介电性能的影响规律. 结果表明, Mg2+在CaSiO3中的最大固溶度不超过0.2；随着Mg2+对Ca2+取代量的增加, 陶瓷在烧结后的主晶相出现从CaSiO3相向CaMgSi2O6相的转变,陶瓷的烧结特性及介电性能出现先增加后下降的趋势；当x=0.3 时, 陶瓷体中CaSiO3相与CaMgSi2O6相共存, 克服了单相CaSiO3或CaMgSi2O6易成片长大的缺点,有效减少了陶瓷中残留的气孔, 提高烧结体致密性. (Ca0.7Mg0.3)SiO3在1320 益烧结后介电常数为6.62, 品质因数为36962 GHz.     

CaTiO3纳米粉体溶胶-凝胶法合成、表征及介电特性

采用无机盐溶胶-凝胶法制备了CaTiO₃纳米粉体，采用TG-DTA、XRD、TEM等技术进行了表征，并探讨了CaTiO₃纳米粉体烧结特性及介电效应。结果表明，干凝胶800 ℃低温煅烧可获得粒径分布较窄、平均粒径为60～70 nm的单相CaTiO₃纳米粉。纳米CaTiO₃粉具有较大的比表面积，使作为粉体烧结驱动力的表面能剧增，促使CaTiO₃在1 200 ℃实现致密烧结，比固相法制备的微米粉烧结降低100～200 ℃，且具有较宽的烧结温区。与微米级粉体烧结体介电特性相比，纳米粉具有更高的Q_f值。纳米CaTiO₃粉制备的陶瓷在1 250 ℃烧结2 h，获得优良的介电性能：ε_r=172，Q_f=4 239 GHz，τ_f=+7.68 × 10^-4 ℃^-1。     

纳米CaMgSi2O6粉体的低温合成与微波介电性能

以硝酸锂、偏钒酸铵、硝酸钙、硝酸镁、正硅酸乙酯为原料，采用溶胶-凝胶法低温合成纳米CaMgSi₂O₆微波介质陶瓷粉体，研究了不同粒径粉体的烧结行为与微波介电性能。结果表明，通过在钙镁硅溶胶中引入锂钒烧结助剂可大大降低陶瓷粉体的晶相合成温度，干凝胶在750 ℃煅烧后可获得主晶相为CaMgSi₂O₆、分散性良好、粒径为78～98 nm的陶瓷粉体，可满足微型片式元器件用超薄陶瓷介质层的制备要求;该粉体在890 ℃烧结后获得致密结构的陶瓷，具有良好的微波介电性能:介电常数为7.68，品质因数为24 542 GHz，频率温度系数为-57.25×10^-6 ℃^-1。     

Eu2+/Dy3+共掺SrSiO3透明微晶玻璃的光学性质

在还原气氛中采用高温熔融法制备了Eu2+-Dy3+共掺硅酸盐玻璃,热处理后得到了Eu2+-Dy3+共掺透明SrSiO3微晶玻璃。测试了样品的激发光谱和发射光谱,研究了不同Eu2+-Dy3+物质的量比下微晶玻璃发光的变化并计算了对应的色坐标。研究发现,样品发射光谱范围在400～600nm,其中400～550nm(绿光)的宽发射谱带来自Eu2+的5d→4f跃迁,而位于483nm(蓝光)和575nm(黄光)的尖峰则来自Dy3+的4F9/2→6 H15/2和4F9/2→6 H13/2跃迁;在紫外(UV)光(365nm)激发下通过调控Eu2+-Dy3+物质的量比可得到发白光的微晶玻璃,当Eu2+-Dy3+物质的量比为1∶8时,Eu2+-Dy3+共掺SrSiO3透明微晶玻璃所发白光最佳,对应的色坐标(0.268,0.356)位于CIE标准色坐标图的白光区域且最接近理想白光。结果表明,Eu2+-Dy3+共掺SrSiO3透明微晶玻璃可作为一种潜在的白光发光二极管用基质材料。     

Er^3＋-doped phosphor-tellurite glass for broadband short-length Er^3＋-doped fiber amplifier

Er^3＋-doped phosphor-tellurite glass for broadband short-length Er^3＋-doped fiber amplifier （EDFA） is fabricated and characterized. The differential value （AT） of onset crystalline temperature （Tx） and glass transition temperature （Tg） is 206 ℃. The stimulated emission cross section of Er^3＋ is calculated from absorption spectrum by McCumber theory and is 0.87 × 10 ^-20 cm^2 at 1532 nm. A broad 1.5-μm fluorescence spectrum with 54-nm full-width at half maximum （FWHM） is demonstrated. Especially, the maximum phonon energy of undoped phosphor-tellurite glass is 1100 cm^- 1, which restricts the upconversion luminescence. It is possible to pump efficiently at 980 nm. These results indicate Er^3＋-doped phosphor-tellurite glass is suitable for fabricating broadband short-length EDFA.     

Enhancement of the upconversion luminescence in Y2O3:Er3+ powders by codoping with La3+ ions

Infrared-to-visible upconverted luminescent spectra of Er3 t and La3 t codoped Y2O3 powders are investigated.By introducing La3 t ions, the upconversion green radiation is found to be greatly enhanced when compared with the powders with La3 t absent. Such enhancement can be attributed to the modification of the local symmetry surrounding the Er3 t ion, which benefits the intra-4f transitions of Er3 t ion, and the decreasing interaction between Er3 t ions, which suppresses the energy transfer process4F7∕2t 4I11∕2→ 4F9∕2t 4F9∕2.     

溶胶-凝胶法制备Nd_(1.85)Ce_(0.15)CuO_(4-δ)先驱体及粉体（英文）

以柠檬酸为螯合剂,采用一种简单的溶胶-凝胶法,成功的合成了蓝色透明的Nd-Ce-Cu-O体系的凝胶,保证了各元素在分子级别的均匀混合。采用红外光谱仪、热分析和XRD对实验过程和产物进行了分析。结果表明,对干凝胶及粉体的分析结果显示金属离子与柠檬酸螯合形成金属-柠檬酸螯合物,这些螯合物又通过酯化反应相互聚合成胶体粒子。干凝胶在30～600℃的温度区间内有五个失重过程。在600℃下已经合成了Nd1.85Ce0.15CuO4-δ粉体,该合成温度远低于固相法,此外通过谢勒公式计算得在600℃、700℃和1000℃下煅烧获得的粉体的平均粒径分别是18.2nm,31.1 nm和60.5 nm。     

用于白光LED的规则球形YAG:Ce3+荧光粉制备及封装性能研究（英文）

采用高温固相法和筛分法合成了YAG:Ce3+系列黄色荧光粉。采用X射线衍射仪(XRD)、电子扫描显微镜(SEM)、激光粒度分布仪及荧光分光光度计对所制备样品进行了表征。结果表明:所得3种样品形貌规则成球形,粒度分布集中,其中心粒径(D50)分别为29.59,17.40,9.56μm,粒径分布离散度分别为0.85,0.80和0.87。通过Reitveld精修拟合发现,随着荧光粉粒径大小的变化,基质的晶格常数并未发生明显变化。随着中心粒径(D50)逐渐变小,其荧光发射强度逐渐降低,且发生明显的蓝移,同时对蓝光的吸收逐渐减弱。通过对荧光粉与蓝光芯片配合所得白光LED的发光效率、显色指数及色温进行测试发现,当使用相同粉胶比浓度、相同点胶量时,随着荧光粉粒径的减小,所得白光LED的流明效率从109.95 lm/W降低到了99.85 lm/W,而显色指数和色温同时升高。     

Research on upconversion codoped oxyfluoride luminescence in new Er^3＋/Yb^3＋ borosilicate glass ceramics

The upconversion luminescence of Er^3＋/Yb^3＋ ions is researched in a novel transparent oxyfluoride borosil- icate glass and glass ceramics under 980-nm excitation. Fluoride nanocrystals Ba2YF7 are successfully precipitated in glass matrix, which is affirmed by the X-ray diffraction results. Compared with the parent glasses, significant enhancement of upconversion luminescence is observed in the Er^3＋/Yb^3＋ codoped transparent glass-ceramics, which may be due to the variation of coordination environment around Er^3＋ and Yb^3＋ ions after crystallization. The possible upconversion mechanism is also discussed.