TiO2修饰La0.6Sr0.4Co0.2Fe0.8O3-δ用于中温固体氧化物燃料电池的阴极

纳米TiO2修饰的La0.6Sr0.4Co0.2Fe0.8O3-δ(LSCF)阴极被直接应用于YSZ电解质电池上. TiO2可阻止LSCF和YSZ间的化学反应,抑制SrZrO3的形成. LSCF-0.25 wt% TiO2阴极电池在0.7 V和600°C下的电流密度是LSCF阴极电池的1.6倍.电化学阻抗谱结果表明, TiO2修饰显著加快了氧离子注入电解质的过程,这可能与TiO2抑制了阴极/电解质界面处高电阻SrZrO3层的形成有关.本文为在ZrO2基电解质上使用高性能的(La,Sr)(Co,Fe)O3阴极材料提供了一种简单有效的方法.     

Multiple Scattering Effects of Ag Particles in Random Ag-SiN Film

A layer of 40nm-thick Ag-SiN film with Ag nano-particles embedded and distributed randomly in the SiN thin film were deposited by the method of radiant-frequency magnetron sputtering. Specimens orderly comprising a random Ag-SiN film and an optical phase change recording layer were exposed to a focused laser beam with wavelength of 69Ohm. It is shown that, with a random Ag-SiN layer deposited above the recording layer. Calculation by the finite difference time domain method of a 4Ohm-thick SiN film under a Gaussian beam irradiation has been carried out to simulate the near-field distribution in the film, which showed a huge local near-field intensity enhancement of about 200 times if small Ag particles with diameter of 6 nm were modelled inthe SiN film in the central region of the in cident laser spot.     

TiO2修饰La0.6Sr0.4Co0.2Fe0.8O3-δ用于中温固体氧化物燃料电池的阴极

纳米TiO2修饰的La0.6Sr0.4Co0.2Fe0.8O3-δ(LSCF)阴极被直接应用于YSZ电解质电池上. TiO2可阻止LSCF和YSZ间的化学反应,抑制SrZrO3的形成. LSCF-0.25 wt% TiO2阴极电池在0.7 V和600°C下的电流密度是LSCF阴极电池的1.6倍.电化学阻抗谱结果表明, TiO2修饰显著加快了氧离子注入电解质的过程,这可能与TiO2抑制了阴极/电解质界面处高电阻SrZrO3层的形成有关.本文为在ZrO2基电解质上使用高性能的(La,Sr)(Co,Fe)O3阴极材料提供了一种简单有效的方法.     

通过溅射与退火制备的用于固体氧化物燃料电池的氧化钆掺杂氧化铈电解质隔层

采用溅射或溅射与退火相结合的方法制备了一系列氧化钆掺杂的氧化铈（GDC）隔层,并考察了其对固体氧化燃料电池性能的影响. 结果表明,200 ℃下溅射获得了立方结构氧化钆掺杂的氧化铈均匀薄膜,在900-1100 ℃范围内的退火处理使得GDC薄膜致密,从而有效阻止了氧化钇掺杂的氧化锆电解质与阴极材料之间的反应,大幅度提高了电池的电化学性能.