二氧化碳转化已成为现今世界研究的热点. 本工作采用原位电化学转化的策略, 将简单溶剂热法合成的层状甲酸氧铋纳米花(BiOCOOH NFs)还原为带有大量晶格位错的多孔铋纳米花(p-Bi NFs). 研究结果表明, p-Bi NFs电催化二氧化碳转化为甲酸盐具有较小的过电位(436 mV). 在–1.8 V(相对饱和甘汞电极, vs. SCE)时, 甲酸盐的分电流密度(j_formate)高达24.4 mA•cm^-2, 法拉第效率(FE_formate)为96.7%, 且在超过500 mV的宽电位窗口内FE_formate超过90%, 并具有很好的稳定性. 该催化剂的高催化性能可归因于前驱体晶格坍塌和重构而形成特殊的多孔粗糙的微纳多级结构, 其表面富含晶格位错和缺陷等高本征活性位, 且具有较强的电子传递能力. 本研究为设计合成高性能的电催化二氧化碳还原产甲酸催化剂提供了新的思路.     

射频等离子制备石墨烯负载Co3O4催化剂及其析氧性能研究

氢能的引入能有效提升配电网的供电可靠性,而电解水制氢是实现低碳转型的关键技术,开发高效的电解水催化剂势在必行。过渡金属氧化物储量大、催化活性高,是具有广阔应用前景的析氧反应催化剂。本文通过射频等离子体处理制备石墨烯上负载Co₃O₄析氧催化剂,XRD、Raman和XPS测试结果显示,二维结构石墨烯的引入加速表面电子迁移,增大了反应面积。等离子体处理促进了纳米粒子在石墨烯上的负载,利用等离子体刻蚀作用在催化剂表面制造出大量碳结构缺陷和氧空位结构,改善了活性位点分布,有效调控Co₃O₄电子结构,提高析氧催化活性。电化学测试表明,本文中合成的Co₃O₄@rGO在电流密度为50 mA·cm^-2时的过电位为410 mV,动力学反应速率较快,表现出优于商业IrO₂的析氧催化活性。     

General π‐Electron‐Assisted Strategy for Ir,Pt, Ru,Pd, Fe,Ni Single‐Atom Electrocatalysts with Bifunctional Active Sites for Highly Efficient Water Splitting

Both the hydrogen evolution reaction (HER) and the oxygen evolution reaction (OER) are crucial to water splitting, but require alternative active sites. Now, a general π‐electron‐assisted strategy to anchor single‐atom sites (M=Ir, Pt, Ru, Pd, Fe, Ni) on a heterogeneous support is reported. The M atoms can simultaneously anchor on two distinct domains of the hybrid support, four‐fold N/C atoms (M@NC), and centers of Co octahedra (M@Co), which are expected to serve as bifunctional electrocatalysts towards the HER and the OER. The Ir catalyst exhibits the best water‐splitting performance, showing a low applied potential of 1.603 V to achieve 10 mA cm^?2 in 1.0 m KOH solution with cycling over 5 h. DFT calculations indicate that the Ir@Co (Ir) sites can accelerate the OER, while the Ir@NC₃ sites are responsible for the enhanced HER, clarifying the unprecedented performance of this bifunctional catalyst towards full water splitting.     

General Formation of Macro-/Mesoporous Nanoshells from Interfacial Assembly of Irregular Mesostructured Nanounits

Mesoporous core–shell nanostructures with controllable ultra-large open channels in their nanoshells are of great interest. However, soft template-directed cooperative assembly to mesoporous nanoshells with highly accessible pores larger than 30 nm, or even above 50 nm into macroporous range, remains a significant challenge. Herein we report a general approach for precisely tailored coating of hierarchically macro-/mesoporous polymer and carbon shells, possessing highly accessible radial channels with extremely wide pore size distribution from ca. 10 nm to ca. 200 nm, on diverse functional materials. This strategy creates opportunities to tailor the interfacial assembly of irregular mesostructured nanounits on core materials and generate various core–shell nanomaterials with controllable pore architectures. The obtained Fe,N-doped macro-/mesoporous carbon nanoshells show enhanced electrochemical performance for the oxygen reduction reaction in alkaline condition.     

Efficient Fe‐Co‐N‐C Electrocatalyst Towards Oxygen Reduction Derived from a Cationic CoII‐based Metal–Organic Framework Modified by Anion‐Exchange with Potassium Ferricyanide

Fe‐Co‐N‐C electrocatalysts have proven superior to their counterparts (e.g. Fe‐N‐C or Co‐N‐C) for the oxygen reduction reaction (ORR). Herein, we report on a unique strategy to prepare Fe‐Co‐N‐C?x (x refers to the pyrolysis temperature) electrocatalysts which involves anion‐exchange of [Fe(CN)₆]^3? into a cationic Co^II‐based metal‐organic framework precursor prior to heat treatment. Fe‐Co‐N‐C‐900 exhibits an optimal ORR catalytic performance in an alkaline electrolyte with an onset potential (E_onset: 0.97 V) and half‐wave potential (E_1/2: 0.86 V) comparable to that of commercial Pt/C (E_onset=1.02 V; E_1/2=0.88 V), which outperforms the corresponding Co‐N‐C‐900 sample (E_onset=0.92 V; E_1/2=0.84 V) derived from the same MOF precursor without anion‐exchange modification. This is the first example of Fe‐Co‐N‐C electrocatalysts fabricated from a cationic Co^II‐based MOF precursor that dopes the Fe element via anion‐exchange, and our current work provides a new entrance towards MOF‐derived transition‐metal (e.g. Fe or Co) and nitrogen‐codoped carbon electrocatalysts with excellent ORR activity.     

泡沫镍上电沉积花瓣状NiFeOxHy/rGO用于析氧反应

开发碱性体系的高效低成本析氧电催化剂是由可再生能源转化制氢的关键。本研究通过在泡沫Ni基底上原位电化学沉积的方法制备了花瓣状NiFeO_xH_y和NiFeO_xH_y/rGO复合催化剂用于析氧反应。花瓣状的结构不仅明显提高了催化剂的比表面积，而且暴露了更多的层状边缘和缺陷，进而增加了催化剂的活性中心。还原氧化石墨烯的加入进一步提升了催化剂的电导和析氧电催化性能，通过优化NiFeO_xH_y/rGO在1 mol/L KOH溶液中的析氧性能为：过电位200 mV（10 mA/cm²）、Tafel斜率29.11 mV/decade，并且保持了较好的稳定性。     

Devisable POM/Ni Foam Composite: Precisely Control Synthesis toward Enhanced Hydrogen Evolution Reaction at High pH

Polyoxometalates (POMs) are promising catalysts for the electrochemical hydrogen production from water owing to their high intrinsic catalytic activity and chemical tunability. However, poor electrical conductivity and easy detachment of the POMs from the electrode cause significant challenges under operating condition. Herein, a simple one-step hydrothermal method is reported to synthesize a series of Dexter–Silverton POM/Ni foam composites (denoted as Ni M -POM/Ni; M =Co, Zn, Mn), in which the stable linkage between the POM catalysts and the Ni foam electrodes lead to high activity for the hydrogen evolution reaction (HER). Among them, the highest HER performance can be observed in the NiCo-POM/Ni, featuring an overpotential of 64 mV (at 10 mA cm⁻², vs. reversible hydrogen electrode), and a Tafel slope of 75 mV dec⁻¹ in 1.0 m aqueous KOH. Moreover, the NiCo-POM/Ni catalyst showed a high faradaic efficiency ≈97 % for HER. Post-catalytic of NiCo-POM/Ni analyses showed virtually no mechanical or chemical degradation. The findings propose a facile and inexpensive method to design stable and effective POM-based catalysts for HER in alkaline water electrolysis.