Yb:Y2O3透明陶瓷的光学性能研究

介绍了一种基于纳米粉末真空烧结技术的新型固体激光材料--Yb:Y2O3多晶陶瓷的制备工艺、物理化学特性、能级结构和光谱特性,并与Yb:YAG单晶进行了对比.采用紧凑型有源镜激光器(CAMIL)的抽运方式,验证了Yb:Y2O3透明陶瓷的激光输出性能.在35W的最大抽运功率下,得到波长1078 nm,功率10.5 W的连续激光输出.斜率效率达到37.5%.实验中还观察到激光输出波长随抽运功率增加而红移以及随输出耦合镜变化而漂移的现象.Yb:Y2O3多晶陶瓷是一种理想的激光材料,不仅具有与Yb:YAG单晶同样优秀的物理化学性能和光谱特性,而且其热导率和发射带宽约为Yb:YAG单晶的两倍,非常适合于高亮度激光器和超短脉冲激光器领域的发展应用.     

Fabrication of Two-Dimensional Photonic Crystals with Controlled Defects by Combination of Holographic Lithography and Two-Photon Polymerization

A new ternary photopolymer system is used in fabricating photonic crystals （PhCs） with controlled defects by combination of single-photon and two-photon photopolymerization. The former process can produce PhCs in one-step recording with a low-power （tens mW） continuous-wave laser at 532nm, while the latter can create desired defects. The preparation of the material, the optical setup and the preliminary experimental results are given. Compared with other methods, this approach is much more accessible and convenient for use of visible light and has advantages of making PhCs in a large scale quickly and economicaJly and introducing any defects exactly, especially for three-dimensional structures.     

Mn掺杂ZnSe前驱体纳米带的制备及其磁光性质

采用了改进的水热途径制备稀磁半导体Mn掺杂ZnSe前驱体纳米带MnxZn1-xSe?en3 (en=ethylenediamine). 与先前方法相比， 具有省时高效的优势. 并通过电子能谱仪、热重分析仪、场发射扫描电子显微镜表征这种前聚体的形态与组成. 在有关电子顺磁共振波谱(ESR)和发光光谱(PL)的实验中，ESR和PL用来研究和表征Mn2+掺杂效率及ZnSe前驱体纳米带中Mn2+-Mn2+的相互作用.Mn掺杂ZnSe前驱体纳米带的ESR谱出现Mn2+特征超精细分裂六重峰，表明了Mn2+-Mn2+的     

光强检测型光纤光栅温变不敏感动态压力传感研究

报道了基于光纤光栅反射谱带宽调制和光强差分检测技术实现单一光纤光栅温变不敏感动态压力传感的新方法。设计了一种结构新颖的双孔梁压力传感装置,依据双孔梁有限元受力分析将光纤光栅准确定位于线性梯度应变区,压力作用下光纤光栅反射谱对称展宽,反射光强线性正比于压力变化。基于光波导理论和材料力学原理推导了线性梯度应变场作用下光栅反射谱带宽、反射光强与压力之间的响应关系。利用光强差分检测技术取代传统波长解调方法,简化解调过程的同时传感系统免受温变影响。实验表明,在-10~80℃的温度变化范围内,系统测量误差小于总量程(120kPa)的1.8%,动态响应速度约80Hz,重复测量系统输出稳定,具有较好的应用价值。     

稠密等离子体表面不稳定性的入射光偏振态效应

用二维粒子模拟程序研究了相对论强激光和稠密等离子体相互作用引起的表面不稳定。数值模拟表明,在s偏振光作用下,等离子体表面出现了类瑞利泰勒不稳定性。形成的不稳定结构随时间发展进一步深入到等离子体内部,最终使等离子体密度形成分层泡状结构,并向前传播。这种不稳定的产生与初始等离子体密度有密切关系,在高于20倍临界密度等离子体的表面没有明显观察到这种不稳定。在p偏振激光作用下,等离子体表面不能明显地形成这种结构。因此在三维几何结构下,这种等离子体表面不稳定性将呈现各向异性。这种表面不稳定将直接影响高次谐波产生和离子加速效率。     

电子关联对类铍离子1s~22s2p~3P_(0,1)能级的超精细结构常数的影响

基于MCDF方法系统地计算了Z=20~83范围内24个类铍离子的1s22s2p3P0,1态的精细结构,得到了与其它理论和实验符合很好的结果.在此基础上,进一步计算了超精细结构对角及非对角常数,并分析了不同电子关联效应和Breit相互作用对它们的影响.     

Q-Switched Large-Mode-Area Yb-Doped Fibre Laser Using GaAs as Saturable Absorber

A passive Q-switched large-mode-area Yb-doped fibre laser is demonstrated using a GaAs wafer as the saturable absorber. A high Yb doping concentration double-clad fibre with a core diameter of 30μm and a numerical aperture of 0.07 is used to increase the laser gain volume, permitting greater energy storage and higher output power than conventional fibres. The maximum average output power is 7.2W at 1080nm wavelength, with the shortest pulse duration of 580ns and the highest peak power of 161W when the laser is pumped with a 25W diode laser operating at 976nm. The repetition rate increases with the pump power linearly and the highest repetition rate of 77kHz is obtained in the experiment.     

Effect of Precursor Molar Ratio of [S^2-]/[Zn^2＋] on Particle Size and Photoluminescence of ZnS：Mn^2＋ Nanocrystals

We investigate the influence of precursor molar ratio of [S^2-]/[Zn^2＋] on particle size and photoluminescence （PL） of ZnS：Mn^2＋ nanocrystMs. By changing the [S^2-]/[Zn^2＋] ratio from 0.6 （Zn-rich） to 2.0 （S-rich）, the particle size increases from nearly 2. 7nm to about 4.Ohm. The increase in the ratio of [S^2-]/[Zn^2＋] cadses a decrease of PL emission intensity of ZnS host while a distinct increase of Mn^2＋ emission. The maximum intensity for the luminescence of Mn^2＋ emission is observed at the ratio of [S^2-]/[Zn^2＋] ≈ 1.5. The possible mechanism for the results is discussed by filling of S^2- vacancies and the increase of Mn^2＋ ions incorporated into ZnS lattices.     

催化裂化碳四馏份在φ1米流化床中氧化制顺酐

本文叙述流化床内催化裂化碳四馏份氧化制取顺酐所用V-P-K-Fe/硅胶催化剂的制备方法及其性能。在φ1m 流化床中,以从分布板上下同时进料的方式,考察了温度、原料浓度对反应结果的影响,认为最佳温度为410℃,原料浓度为2.2—2.5%。该催化剂在上述条件下经2000小时运转,活性稳定,顺酐重量收率约在75%左右。采用从分布板上下同时进料的方法,能将碳四馏份以高浓度在爆炸极限内操作,从而可大大强化设备生产能力。     

纳米SiO2颗粒增强镍基复合镀层的组织与微动磨损性能研究

采用电刷镀技术在45#钢表面制备了纳米SiO2颗粒增强镍基复合镀层,用扫描电子显微镜和透射电子显微镜观察分析了复合镀层的表面形貌和微观组织形貌,用纳米压痕仪测试了复合镀层的微观力学性能,并采用PLINT型高温微动疲劳试验机考察了复合镀层在室温至500 ℃下的微动磨损行为.结果表明:纳米SiO2颗粒促进了镀层的晶粒细化,提高了镀层的力学性能,复合镀层的硬度和弹性模量分别比镍镀层提高了2.01GPa和5 GPa,从而改善了镀层的微动磨损性能;复合镀层的耐磨性能约为镍镀层的2倍,这是由于纳米SiO2颗粒对复合镀层具有超细晶强化、硬质点弥散强化以及高密度位错强化机制所致.