聚合物共混物脆韧转变性能研究 Ⅲ.分散相形态参数之间的关系

为了研究形态（特别是分散状态）对聚合物共混物韧性的影响，建立了准网络形态模型，定义了分散相分布系数（ξ，０＜ξ１），并给出其物理意义，推导了基体层厚度的计算公式，研究了形态参数的变化对基体层厚度的影响．对于常见的无规形态，ξ≈１．对于准网络形态，ξ＜１，并且不是常数．计算结果表明，减小ξ和分散相粒径及其分布、增大其体积分数有利于减小基体层厚度．从理论上证明了准网络形态比无规形态更有利于减小基体层厚度．     

用TMS—2型热机分析仪测量热释蠕变

对已经商品化的Perkin-Elmer TMS-2型热机分析仪进行改进,用来测量聚合物材料的热释蠕变行为。按照7SCr分步加载的程序,用弯曲法测量了-83～300℃温度范围内低密度聚乙烯的玻璃化转变松弛过程,并从TSCr谱上计算其相应的分子参数,实验结果与用扭转的TSCr方法所得结果相等,因此这是一种研究聚合物材料松弛行为的方便可行的技术。     

ADSORPTION OF 4-METHYLANILINE IN AQUEOUS SOLUTION BY BENZOYL-CONTAINING POLYMERIC ADSORBENTS

New polymeric adsorbents (ZH-02, ZH-03) containing benzoyl group for adsorbing and removing 4-methylaniline from its aqueous solutions were prepared. Studies on the isotherms and the comparison of desorption conditions evidenced through the adsorption of 4-methylaniline in water onto ZH-02 and ZH-03, namely that there are chemisorption‘s transitions at a proper higher temperature. Mini-colunm adsorption studies of 4-methylaniline on XAD-4, ZH-02 and ZH-03 at 288 K show that the breakthrough capacities are 2.39, 2.99 and 3.19 mmol/g and the total capacities are 3.45, 3.92 and 4.35 mmol/g, respectively.     

WOBr_4催化聚苯乙炔的合成与表征

本文研究了苯乙炔在WOBr_4催化剂作用下的聚合行为,并对催化聚合机理进行了探讨。所得聚合物是可溶可熔的褐红色固体,其最高分子量为1830(M_n)。WOBr_4催化剂具有催化剂用量少(2/100),聚合反应时间短(10秒钟),产物收率高(80％以上)等特点。结构分析结果表明,WOBr_4催化聚苯乙炔具有顺-反式微观结构。     

一维〔M（tmp）〕_2ReO_4（M＝Ni、Cu、Pd）聚合物的能带结构

用紧束缚ＥＨＴ晶体轨道方法对一维〔Ｍ（ｔｍｐ）〕_２ＲｅＯ_４（Ｍ＝Ｎｉ、Ｃｕ、Ｐｄ）聚合物进行了能带计算，利用键向量近似方法对能带的结构及组成进行了讨论。结果表明，该类型聚合物具有不同的导电机理，并进一步研究了环平面间的成键性质及转角改变对聚合物导电性能的影响。     

乙烯-甲基丙烯酸共聚物离聚体在聚对苯二甲酸乙二酯中的相分离行为

聚对苯二甲酸乙二酯(PET)结晶速度很慢,通常加入成核剂来提高结晶速度。从专利文献来看,以离子聚合物为成核剂的例子也是很多的。离子聚合物与小分子成核剂的显著差别是:离子聚合物有一个很长的碳氢主链,其侧基为酸基,酸基被部分或全部地中和成盐。很明显,离子聚合物不象小分子成核剂那样能很好地分散在PET基体中,而是以独立的相存在。作为PET体系系列研究的继续,本文报道了离子聚合物Surlyn在PET中的相分离行为。     

Preparation of a Star Network PEG-based Gel Polymer Electrolyte and Its Application to Electrochromic Devices

A star network polymer with a pentaerythritol core linking four PEG-block polymeric arms was synthesized, and its corresponding gel polymer electrolyte based on lithium perchlorate and plasticizers EC/PC with the character being colorless and highly transparent has been also prepared. The polymer host was characterized and confirmed to be of a star network and an amorphous structure by FTIR, ^1H NMR and XRD studies. The polymer host hold good mechanical properties for pentaerythritol cross-linking. Maximum ionic conductivity of the prepared polymer electrolyte has reached 8.83 × 10 ^-4 S·cm^-1 at room temperature. Thermogravimetry （TG） of the polymer electrolyte showed that the thermal stability was up to at least 150 ℃. The gel polymer electrolyte was further evaluated in electrochromic devices fabricated by transparent PET-ITO and electrochromically active viologen derivative films, and its excellent performance promised the usage of the gel polymer electrolyte as ionic conductor material in electrochrornic devices.     

向日葵状葫芦脲的合成与超分子自组装

葫芦脲(CB[n],n为最小重复单元数)是一类由苷脲与甲醛经缩合环化而形成的大环分子,因具有良好的分子识别性能及配位性能,在分离、催化、医药、互锁分子及超分子体系构建等领域有着广泛的应用。本课题组在苷脲分子中间的桥上增加一个碳原子,得到苷脲类似物丙基二脲(TD),TD进一步与甲醛缩合环化得到一系列向日葵状葫芦脲类似物(TD[n])。与传统苷脲相比,TD容易在碳原子上衍生化,衍生物对成环反应的影响较小,容易获得TD[n]。相比CB[n]的n最小值为5,TD[n]的n最小值减小到4,TD[4]是目前为止文献报道的葫芦脲家族的最小成员。此外,这些TD[n]有的对金属离子具有很好的选择配位能力,有的对质子化有机胺具有强的外结合性能,它们分别构建了一系列一维、二维或刺激响应型超分子聚合物。研究结果为TD[n]在超分子化学等领域的进一步应用打下坚实的基础。     

缩聚反应合成侧链液晶聚合物

侧链液晶聚合物的合成方法,可归纳为3类:一是烯基的单体,如甲基丙烯酸酯,或丙烯酸酯,氯代丙烯酸酯等,经自由基聚合反应,阴离子聚合反应及甲基丙烯酸酯的基团转移聚合反应,得到侧链液晶聚合物;二是变性反应,如聚硅氧烷与丙烯酸酯介     

一维链状配位聚合物[M(H2bpb)(H2O)4](SO4)2·6H2O[M=Zn(Ⅱ)，Cu(Ⅱ)]的合成及晶体结构表征

设计并合成了一个含吡啶基团的柔性配体：N，N′-Bis(3-pyridylmethyl)-1，4-benzenedimethylamine(bpb)。通过bpb与硫酸锌及硫酸铜反应得到了两个新型具有一维链状结构的配位聚合物：[M(H₂bpb)(H₂O)₄](SO₄)₂·6H₂O[M=Zn(Ⅱ) 1，Cu(Ⅱ) 2]。X-射线晶体结构测定表明，这两个