Titanium carbonitride films on cemented carbide cutting tool prepared by pulsed high energy density plasma

Hard films prepared by pulsed high energy density plasma (PHEDP) are characterized by high film/substrate adhesive strength, and high wear resistance. Titanium carbonitride (TiCN) films were deposited onto YG11C (ISO G20) cemented carbide cutting tool substrates by PHEDP at room temperature. XRD, XPS, SEM, AES, etc. were adopted to analyze the phases (elements) composition, microstructure and the interface of the films, respectively. The results show that, the uniform dense films are composed of grains ranging from 70 to 90 nm. According to the AES result, there is a broad transition layer between the film and the substrate, due to the ion implantation effect of the PHEDP. The transition layer is favorable for the film/substrate adhesion.     

Dialdehyde starch‐crosslinked chitosan films and their antimicrobial effects

For improved mechanical and water‐swelling properties of chitosan films, a series of transparent films were prepared with dialdehyde starch as a crosslinking agent. Fourier transform infrared and X‐ray analysis results demonstrated that the formation of Schiff's base disturbed the crystallization of chitosan. The mechanical properties and water‐swelling properties of the films were significantly improved. The best values of the tensile strength and breaking elongation were 113.1 MPa and 27.0%, respectively, when the dialdehyde starch content was 5%. All the crosslinked films still retained obvious antimicrobial effects toward S. aureus and E. coli, and they showed potential for biomedical applications. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 993–997, 2003     

Coupled lubrication and Stokes flow finite elements

A method is developed for performing a local reduction of the governing physics for fluid problems with domains that contain a combination of narrow and non‐narrow regions, and the computational accuracy and performance of the method are measured. In the narrow regions of the domain, where the fluid is assumed to have no inertia and the domain height and curvature are assumed small, lubrication, or Reynolds, theory is used locally to reduce the two‐dimensional Navier–Stokes equations to the one‐dimensional Reynolds equation while retaining a high degree of accuracy in the overall solution. The Reynolds equation is coupled to the governing momentum and mass equations of the non‐narrow region with boundary conditions on the mass and momentum flux. The localized reduction technique, termed ‘stitching,’ is demonstrated on Stokes flow for various geometries of the hydrodynamic journal bearing—a non‐trivial test problem for which a known analytical solution is available. The computational advantage of the coupled Stokes–Reynolds method is illustrated on an industrially applicable fully‐flooded deformable‐roll coating example. The examples in this paper are limited to two‐dimensional Stokes flow, but extension to three‐dimensional and Navier–Stokes flow is possible. Copyright © 2003 John Wiley & Sons, Ltd.     

Properties of sol-gel dip-coated zinc oxide thin films

Zinc oxide (ZnO) films were deposited on glass substrates by the sol-gel dip coating method using acrylamide route. The films were characterized by X-ray diffraction studies which indicated wurtzite structure. Optical absorption measurements indicated band gap in the range 3.17-3.32 eV. XPS studies indicated the formation of ZnO. The resistivity of the films were in the range 1000-10,000 ohm cm.     

Thickness dependence of free‐standing thin films

Below a critical thickness, of about 60 nm, the glass transition temperature of polystyrene (PS) films decreases with film thickness, as demonstrated using free‐standing films. A geometrical model is developed here describing this phenomenon in the case of ideal (Gaussian) chains. This model, which can be considered as an application of the free volume model, assumes that the decrease of the glass transition temperature from thick to ultrathin films is due to the modification of the interpenetration between neighboring chains. The theoretical curve deduced from the model is in excellent agreement with the PS experimental results, without using any adjustable parameters. From these results, it can be concluded that new chain motions, usually buried in bulk samples, are expressed by the presence of the surface. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 10–17, 2007     

用电泳技术制备YBCO高温超导厚膜

介绍了电泳技术制备YBCO高温超导厚膜的实验方法和YBCO高温超导厚膜的电学性质测量 ,讨论了在学生小型科研实验或设计实验中开展此实验的学时安排、注意事项和实验内容的扩展 .     

Effect of nonstoichiometry on Raman scattering of VO2 films

We report on Raman scattering of VO2 films prepared by radio frequency magnetron sputtering under different conditions. Our investigations revealed that the dominated Raman peaks shift towards high frequency for both V-rich and O-rich VO2 films, compared with the stoichiometry VO2 films. The experimental evidence is presented and the cause for nonstoichiometry dependence of Raman spectra of VO2 films is discussed.     

Structure and optical properties of lead iodide based two-dimensional perovskite compounds containing fluorophenethylamines

Phenethylammonium-based perovskites, which can be regarded as a semiconductor/insulator multiple quantum well consisting of lead halide semiconductor layers sandwiched between phenethylammonium insulator layers were prepared. To investigate the effects of the electronic state and the orientation of organic insulator layers on the optical properties of layered perovskites, fluorine substituted analogues were also prepared. The structure and optical properties were investigated by the XRD, UV–Vis absorption, and fluorescence measurements. The exciton absorption peak was shifted by the substitution of fluorine atoms in organic ammonium compounds. It became clear that the optical properties of two-dimensional perovskite compounds were controlled by the substitution of fluorine atoms.     

Electrical characterization of low temperature deposited TiO2 films on strained-SiGe layers

Thin films of titanium dioxide have been deposited on strained Si_0.82Ge_0.18 epitaxial layers using titanium tetrakis-isopropoxide [TTIP, Ti(O-i-C₃H₇)₄] and oxygen by microwave plasma enhanced chemical vapor deposition (PECVD). The films have been characterized by X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR). Dielectric constant, equivalent oxide thickness (EOT), interface state density (D_it), fixed oxide charge density (Q_f/q) and flat-band voltage (V_FB) of as-deposited films were found to be 13.2, 40.6 Å, 6×10¹¹ eV⁻¹ cm⁻², 3.1×10¹¹ cm⁻² and −1.4 V, respectively. The capacitance–voltage (C–V), current–voltage (I–V) characteristics and charge trapping behavior of the films under constant current stressing exhibit an excellent interface quality and high dielectric reliability making the films suitable for microelectronic applications.     

后退火温度对溅射沉积Pb(Zr0.52Ti0.48)O3铁电薄膜结构和性能的影响

在具有Ti缓冲层的Pt(111)底电极上,用射频溅射工艺在较低的衬底温度(370℃)和纯Ar气氛中沉积Pb(Zr0.52Ti0.48)O3(PZT)薄膜,沉积过程中基片架作15°摇摆以提高膜厚的均匀性。然后将样品在大气中进行5min快速热退火处理,退火温度550-680℃。用XRD、SEM分析薄膜的微结构,RT66A标准铁电测试系统测量样品的铁电和介电性能。结果表明,所沉积的Pt为(111)取向,仅当后退火温度高于580℃,沉积在Pt(111)上的PZT薄膜才能形成钙钛矿结构的铁电相,退火温度在580-600℃时结晶为(110)择优取向,退火温度高于600℃时结晶为(111)择优取向。PZT薄膜的极化强度随退火温度的升高而增加,但退火温度超过650℃时漏电流急剧上升,因此退火处理的温度对PZT薄膜的结构和性能有决定性的影响。