高质量AlPO4-5分子筛单晶的螯合剂法合成与表征

考察了几种螯合剂对AlPO4-5分子筛单晶合成的影响，结果表明，用邻苯二酚，乙酰丙酮，水杨醛为螯合剂可以得到高质量的，尺寸较大的分子筛单晶，其作用机理可能与它们加入到分子筛合成体系中，改变了溶胶中铝的配位数或产生了铝的螯合物有关。     

Surface film formation on a graphite electrode in Li‐ion batteries: AFM and XPS study

The formation of a passivation film (solid electrolyte interphase, SEI) at the surface of the negative electrode of full LiCoO₂/graphite lithium‐ion cells using LiPF₆ (1M ) in carbonate solvents as electrolyte was investigated by means of x‐ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM). The analyses were carried out at different potentials of the first and the fifth cycles, showing the potential‐dependent character of the surface‐film species formation. These species were mainly identified as Li₂CO₃ up to 3.8 V and LiF up to 4.2 V. This study shows the formation of the SEI during charging and its partial dissolution during discharge. Copyright © 2005 John Wiley & Sons, Ltd.     

改性聚苯乙烯微球的制备及其胶体晶体的组装

采用甲基丙烯酸改性的无皂乳液聚合方法制备了尺寸为210 nm、含羧基的聚苯乙烯(PS)微球，用红外光谱、透射电子显微镜和粒度分析仪对其形状和结构进行分析，结果表明，经甲基丙烯酸改性后得到了表面为高密度电荷的单分散性PS微球.用垂直沉积法快速制备出在较大范围(大于1 cm2)呈现很好有序性的密排结构聚苯乙烯胶体晶体薄膜，其在590 nm波长处存在光子带隙.在电子显微镜下，观察到这种胶体晶体是面心立方(fcc)密排结构.     

A new route for synthesizing cholesterol analogs with fluorocarbon side chains and their liquid-crystalline aliphatic esters

A new and efficient route has been developed to synthesize 17β-(1-methyl-3-perfluoroalkyl)propyl-3β-androsterol (1) in nine steps from hyodeoxycholic acid via selective addition of 1-perfluoroalkyl iodide to 24-norchola-5,22-dien-3β-ol. From (1), the first series of steroidal liquid crystalline aliphatic esters (smectic A) with fluorocarbon side chains has been prepared.     

Zur kenntnis ‚Kationen-reicher’︁ Tantalate und Niobate Über Na5TaO5 und Na5NbO5

On Tantalates and Niobates ‘rich in Cations’. On Na₅TaO₅ and Na₅NbO₅ Colourless, transparent single crystals of Na₅TaO₅ [annealed mixtures of Na₂O, Li₂O, and Ta₂O₅, Na : Li : Ta = 6.6 : 1.1 : 1, Ni-cylinder, 1000°C, 75 d] as well as Na₅NbO₅ [annealed mixtures of Na₂O, Li₂O, and Nb₂O₅, Na : Li : Nb = 6.6 : 1.1 : 1, Ni-cylinder, 1000°C, 75 d] have been prepared. Single crystal data show that both isotypic oxides represent a deformed variant of the NaCl-type of structure [Na₅TaO₅: 1154 from 1250 I₀ (hkl), four-cycle diffractometer Philips PW 1100, ω2-θ scan, Ag? Kα , R = 4.88%, space group c2/c with a = 629.3(1) pm, b = 1025.4(2) pm, c = 1004.6(2) pm, b? 106.80(2)°, z = 4 and Na₅NbO₅: 998 from 1247 I₀(hkl), four-cycle diffractometer Philips PW 1100, ω-2θ scan, Ag? Kα , R = 8.58% and R_w = 7.67%, space group C2/2 with a = 629.1(1) pm, b = 1024.4(2) pm, c = 1004.2(2) pm, b? = 106.80(2)°, Z = 4]. The Madelung Part of Lattice Energy, MAPLE, and Effective Coordination Numbers, ECoN, the latter derived from Mean Effective Fictive Ionic Radii, MEFIR, as well as Charge Distribution, CHARDI, are calculated.     

超拉伸聚乙烯的弹性模量和导热性能

为了揭示聚合物分子链伸展、取向的本征特性，发展了两个新的测量方法和实验装置，用于研究拉伸比高达２００的超拉伸聚乙烯凝胶的弹性性能、传热性能和聚合物结构的关系．应用激光脉冲热致超声法给出材料拉伸方向和横向杨氏模量，应用激光脉冲光热辐射法给出拉伸方向，横向和厚度方向的导热系数．随拉伸比λ的增加，轴向杨氏模量急剧的增加，而横向的仅有少许减小．导热系数具有相似的特性．本文发现当λ＝２００时，这种拉伸取向聚乙烯的轴向模量可达钢的８０％，而导热系数甚至可达２倍，直至成为热的良导体，这是由于在高拉伸比时形成了相当数量的伸展分子链构成的针状晶体———晶桥．本文提出晶桥作为短纤维分散相的取向聚合物的结构模型，对于超拉伸聚乙烯的上述特性可以进行统一描述和定量化分析，和实验结果很好符合．     

Cyclic Voltammograms of Ferrocene on Multi‐Walled Carbon Nanotubes (MWCNTs)‐Modified Edge Plane Pyrolytic Graphite (EPPG) Electrode in Room Temperature Ionic Liquids (RTILs) of 1‐Ethyl‐3‐Methylimidazolium Tetrafluoroborate (EMIBF4)

In this work, the electrochemical behavior of ferrocene (Fc) was investigated by cyclic voltammetry (CV) in room temperature ionic liquids (RTILs) of 1‐ethyl‐3‐methylimidazolium tetrafluoroborate (EMIBF₄) on glass carbon (GC), edge plane pyrolytic graphite (EPPG) and multi‐walled carbon nanotube (MWCNTs)‐modified EPPG electrodes, respectively. The results demonstrated that on GC electrode, pairs of well‐defined reversible peaks were observed, while for the electrode of EPPG, the peak potential separation (ΔE_p) is obviously larger than the theoretical value of 59 mV, hinting that the electrode of EPPG is distinguished from the commonly used electrode, consistent with the previous proposition that EPPG has many “defects”. To obtain an improved electrochemical response, multi‐walled carbon nanotubes (MWCNTs) were modified on the electrode of EPPG; the increased peak current and promoted peak potential separation not only proved the existence of “defects” in MWCNTs, but also supported that “creating active points” on an electrode is the main contribution of MWCNTs. Initiating the electrochemical research of Fc on the MWCNTs‐modified EPPG electrode in RTILs and verifying the presence of “defects” on both EPPG and MWCNTs using cyclic voltammograms (CVs) of Fc obtained in RTILs of EMIBF₄, is the main contribution of this preliminary work.     

Preparation of Silicalite-1 Within Macroporous Silica Glass

Microcrystalline silicalite-1 was formed on the inner surface of macroporus silica glasses prepared by the sol-gel process. By heating a homogeneous precursor solution at 100°C under a hydrothermal condition, 2–5 m of plate-like particles of silicalite-1 were deposited. With an increase of mixing time of the precursor solution, the number of silicalite-1 particles increased, accompanied by the relative decrease of the particle size. Depending on the temperature and the duration of the heat-treatment of the macroporous silica, the amount of deposited silicalite-1 varied. Below 1000°C, the amount increased with the heat-treatment temperature, as a result of the competition between the precipitation of silicalite-1 and the dissolution of silica from the macroporous silica glass under a strongly basic condition. On the other hand, above 1000°C the amount of deposited silicalite-1 decreased in accordance with the decrease of the macropore diameter by the heat-treatment, because of the limited transport of the dissolved silicate species through the smaller macropores.     

The effects of substituent size and molecular weight on the liquid crystalline properties of poly(2-alkyl-1,4-phenylene terephthalate)s

A series of low molecular weight, thermotropic poly(2-alkyl-1,4-phenylene terephthalate)s was prepared by the solution polycondensation reaction of terephthaloyl chloride and alkylhydroquinones containing n-alkyl substituents of increasing size from methyl to dodecyl. Samples of the low molecular weight polymers so obtained were also further polycondensed in the solid state to obtain high molecular weight polymers. The liquid crystalline phase behaviors and textures were determined, and the effects of polymer structure and molecular weight on these properties are discussed. All of the polymers obtained formed thermotropic, nematic mesophases, which were less stable for the lower molecular weight polymers, as expected, than were the mesophases formed by the higher molecular weight polymers. © 1994 John Wiley & Sons, Inc.     

Characterization of structural transitions in the SLS/decanol/water system

The ternary system sodium-dodecylsulphate (SLS)/decanol/water has been investigated at three different water contents and varying ratios of cosurfactant to surfactant by means of polarized optical microscopy,²H-NMR quadrupole splittings and small angle x-ray scattering. Upon addition of decanol a hexagonal phase transforms into a lamellar phase. For the highest water content of 0.65 no intermediate two-phase regions are detected but nematic phases are formed between. The lamellar phase at low cosurfactant content is very sensitive to changes of temperature and seems to be a so-called defective one with curved interfaces. From the scaling behavior it is concluded that the building units seem to be ribbons of increasing width on addition of cosurfactant or amphiphilic substance. By reaching a decanol mole fraction of 0.4 a classical lamellar phase with well-known behavior is formed. During these transformations the position of the first diffraction maximum changes gradually irrespective of phase transitions. The maximum mole fraction of cosurfactant the lamellar phase of our system can incorporate is 0.77.