高负载脉冲氙灯管壁特性实验

利用“神光”-Ⅲ原型装置所用氙灯（内径为Ф31mm，弧长为1430mm，壁厚为3．5mm，管材为掺铈石英玻璃）进行高负载（爆炸系数fx=0.6）实验。图1给出了氙灯放电时的电流电压波形。实验发现，氙灯运行不到10发时，氙灯灯管内壁出现白色花纹，而且白色花纹的出现是随机的，并且不是一直都会存在。随着运行发次的增加，氙灯内壁出现乳状积淀物，发白区域从两端向氙灯中间延伸，但并不是均匀分布，而是成块状遍及整支灯管。运行到约20发时，在灯管内壁会出现短的亮线（即极限负载条纹），随着运行发次的增加，亮线的长度会沿圆周发展成弧形或圆环形，亮线的数量也会由两端离电极30mm处向氙灯中间增加，呈一系列的圆环分布，但圆环的间距并不相同，而且当氙灯冷却到室温时，可以观察到灯管内壁和氙灯下端（竖直）附有白色颗粒物。     

140 keV质子辐照对石英玻璃光谱性能影响的研究

研究了JGS3 光学石英玻璃在真空、冷黑和能量为 14 0keV的质子辐照下光学透过率变化的基本规律。在辐照剂量大于 5× 10 14 proton/cm2 后 ,主要引起 2 30～ 2 5 0nm的吸收带 ,其吸收峰值随辐照剂量的增加而单调增加。在较大辐照剂量下 ,近紫外和可见区域也存在某些弱的吸收带。 2 30～ 2 5 0nm的吸收带由E′心引起。质子辐照下在JGS3 光学石英玻璃中形成的E′心是受氢扰动的 ,即辐照过程中不仅发生Si -O键的断裂 ,而且发生[≡Si- ]和 [≡Si-O]向 [≡Si-H]和 [≡Si-OH]的转变     

凝胶老化对镱铝共掺SiO_2粉晶化和光谱性能的影响EI北大核心CSCD

采用SiCl_4水解法制备了镱铝共掺石英光纤纤芯原料粉,在O_2氛围下1100℃烧结除羟基处理后,原料粉析出了α-石英相。对镱铝共掺硅酸凝胶进行了常温老化和高压釜高温高压老化处理。测试结果表明,老化处理有效地抑制了镱铝共掺石英玻璃原料粉的析晶行为,Yb^(3+)的荧光强度和荧光寿命得到提高,说明高压釜处理可缩短老化处理时间并提高荧光性能,是制备镱铝共掺石英玻璃原料粉的重要工艺。     

掺Yb3+石英玻璃中非桥氧空穴缺陷特性的研究

为了对存在于石英玻璃中的非桥氧空穴缺陷的特性进行研究,采用高频等离子体法对掺Yb³⁺石英玻璃进行了制备。首先介绍了玻璃样品的制备过程,然后对所制备的掺Yb³⁺石英玻璃样品的吸收特性、发射特性以及傅里叶变换红外吸收光谱进行了分析。结果表明,所制备的玻璃样品具有Yb³⁺离子典型的吸收特性。位于260 nm波长的吸收峰以及200 nm激发波长下产生的位于630 nm波长的发射峰都表明所制备的玻璃样品中存在非桥氧空穴缺陷。并且不同激发波长所产生的发射峰以及红外吸收光谱都说明玻璃样品中的非桥氧空穴缺陷是由≡Si－O↑和≡Si－O↑…H－O－Si≡两类空穴中心构成,Yb³⁺离子对合作发光与非桥氧空穴缺陷间存在能量转移过程。     

Pulsed Laser Deposition ZnS Buffer Layers for CIGS Solar Cells

Polycrystalline ZnS films were prepared by pulsed laser deposition （PLD） on quartz glass substrates under different growth conditions at different substrate temperatures of 20, 200, 400, and 600 ℃, which is a suitable alternative to chemical bath deposited （CBD） CdS as a buffer layer in Cu（In,Ga）Se2 （CIGS） solar cells. X-ray diffraction studies indicate the films are polycrystalline with zinc-blende structure and they exhibit preferential orientation along the cubic phase β-ZnS （111） direction, which conflicts with the conclusion of wurtzite structure by Murali that the ZnS films deposited by pulse plating technique was polycrystalline with wurtzite structure. The Raman spectra of grown films show Al mode at approximately 350 cm^-1, generally observed in the cubic phase β-ZnS compounds. The planar and the cross-sectional morphology were observed by scanning electron microscopic. The dense, smooth, uniform grains are formed on the quartz glass substrates through PLD technique. The grain size of ZnS deposited by PLD is much smaller than that of CdS by conventional CBD method, which is analyzed as the main reason of detrimental cell performance. The composition of the ZnS films was also measured by X-ray fluorescence. The typical ZnS films obtained in this work are near stoichiometric and only a small amount of S-rich. The energy band gaps at different temperatures were obtained by absorption spectroscopy measurement, which increases from 3.2 eV to 3.7 eV with the increasing of the deposition temperature. ZnS has a wider energy band gap than CdS （2.4 eV）, which can enhance the blue response of the photovoltaic cells. These results show the high-quality of these substitute buffer layer materials are prepared through an all-dry technology, which can be used in the manufacture of CIGS thin film solar cells.     

光纤传感器

光纤是用石英、玻璃、稀土石英玻璃等光透射率高的媒质制作的极细纤维．它具有许多特异性能，为本世纪后半叶的重要发明之一．光纤的研制，主要是为了用于通信，世界上第一条光纤通信实验光路于1977年建成．就在当年，光纤开始进入传感器领域．80年代以来，各种用途的光纤传感器相继出现．     

紧聚焦飞秒脉冲与石英玻璃相互作用过程中的电子动量弛豫时间研究

本文通过数值模拟(3+1)维扩展的广义非线性薛定谔方程,研究了紧聚焦飞秒激光脉冲在诱导石英玻璃的非线性电离过程中电子动量弛豫时间对于该电离过程的影响.计算结果证明电子动量弛豫时间会直接影响入射脉冲在焦点区域所形成的峰值场强、自由电子态密度和能流等参量的分布态势,因此在与实验结果相比较后发现适合于相互作用过程的电子动量弛豫时间的理论值约为1.27 fs.进一步的研究表明,电子动量弛豫时间与逆韧致吸收效应、雪崩电离的概率、等离子体密度、等离子体的自散焦效果以及间接引起的焦平面位置的移动都有着密切的联系.当前的研究结果表明电子动量弛豫时间在飞秒激光脉冲与物质相互作用的过程中发挥着重要作用.     

石英玻璃高温分子动力学模拟中的势函数

根据石英玻璃高温下的分子动力学研究, 分析了势函数中多体势在高温应用下的局限性, 认为离子型对势在模拟石英玻璃高温结构方面优于多体势. 在原子电荷转移方面, 计算并分析了Si和O原子电荷大小对计算原子自扩散系数的影响, 发现用原子电荷转移较少的Morse势函数计算的原子自扩散激活温度比BKS势函数计算的低, 而且在同一温度下, 自扩散系数的计算值也随着原子电荷的减小而增大, 因此, 较小的原子电荷转移应该有利于石英玻璃在高温下的动力学性能的研究.