熔融浸渍法制备锂离子电池正极材料LiMn2O4的研究

采用LiNO3和MnO2为原料,在650℃下制备了尖晶石型的LiMn2O4.通过X射线衍射、扫描电子显微镜、热重分析和电化学性能测试,发现该化合物具有很高的放电比容量和较好的循环性能,首次放电比容量可达到122 mA·h/g.并对循环性能衰减的各种因素进行了讨论.     

Thermal and structure analysis of FeSO4·H2O-BaO2 mixtures

Investigations on the thermal decomposition of FeSO₄·H₂O-BaO₂ mixtures were carried out under isothermal conditions by using simultaneously solid electrolyte cell (EMF-method). Evoked interactions producing oxygen in the temperature range 553-673 K were established by means of a solid electrolyte oxygen analyzer. Based on Mössbauer spectroscopy data and X-ray analysis it was proved that these reactions were associated with the release of oxygen from barium peroxide, oxidation of ferrosulphate-monohydrate to FeOHSO₄, and formation of barium ferrites such as BaFe₂O₄ and BaFe₁₂O₁₉.     

Review of Directly Producing Light olefins via CO Hydrogenation

Directly making light olefins via CO hydrogenation is a promising process to obtain a nonpetroleum based supply of alkenes.Limited by the ASF distribution function of Fischer-Tropsch synthesis,the yield of light olefins (C2-C4) can not reach the desired levels,which is a great challenge to overcome.Beginning thermodynamic analysis,the ASF distribution function,the reaction performance of CO hydrogenation and slurry reactor studies.The problems currently faced by this research area are presented at the end of the article.     

尖晶石锂锰氧化物锂离子嵌脱过程的交流阻抗谱研究

用粉末微电极研究了尖晶石锂锰氧化物在不同嵌锂状态下嵌脱锂过程的交流阻 抗图谱，提出了新的等效电路模型。描述锂离子在固体中扩散的Warburg阻抗与累 积或消耗的嵌入电容在Lix MnO4中的x≤0．5时串联，0．5＜x≤1时并联。用提出 的等效电路模型分阶段拟合了实验所得的交流阻抗谱，拟合值与实验值相当吻合， 由拟合结果得到不同电位下锂离子在表面膜中的迁移电阻和电容，界面电荷传递电 阻，双层电容，锂离子在固体中扩散系数和累积或消耗的嵌入电容。     

四元交互体系Li~＋，Mg~（2＋）／Cl~－，SO_4~（2－）－H_2O

本文采用等温溶解平衡法研究了四元交互体系Ｌｉ＋，Ｍｇ２＋／ＣＩ－，ＳＯ－Ｈ２Ｏ２５℃的机关系和平衡液相的物化性质（密度、粘度、电导率、折光率和ｐＨ）．该体系２５℃有七个相区Ｌｉ２ＳＯ４·Ｈ２Ｏ，ＭｇＳＯ４·７Ｈ２Ｏ．ＭｇＳＯ４·６Ｈ２Ｏ．ＭｇＳＯ４·５Ｈ２Ｏ，ＭｇＣ１２，６Ｈ２Ｏ，ＬｉＣＩ．ＭｇＣｌ２．７Ｈ２Ｏ，ＬｉＣＩ·Ｈ２Ｏ，十一条单变量线，五个共饱点．其中ＬｉＣＩ·Ｈ２Ｏ＋ＬｉＣＩ·ＭｇＣｌ２·７Ｈ２Ｏ＋Ｌｉ２ＳＯ４·Ｈ２Ｏ为一致零变量点．与文献中的研究结果比较，我们得到两个新相区ＭｇＳＯ４·６Ｈ２Ｏ和ＭｇＳＯ４·５Ｈ２Ｏ．用经验和半经验公式计算了平衡液相的密度、折光率．由实验测定的溶解度数据求得了高锂浓度下的Ｐｉｔｚｅｒ参数．对该体系２５℃溶解度进行了理论计算复证．     

Thermal decomposition of struvite

Struvite (NH₄MgPO₄·6H₂O) is a mineral often found in urinary tracts and kidneys. Thermal decomposition using slow low heating shows that the 'kidney' stone can be decomposed at temperatures below 40°C. At this temperature both ammonia and water are evolved. If more rapid heating is employed the decomposition occurs at around 80°C. The implication of this work rests with the use of low slow heat for the decomposition of the kidney stones. This revised version was published online in July 2006 with corrections to the Cover Date.     

Structural and magnetic investigations of the mixed-valence Fe(II,III) two-dimensional layer complex, [Fe2(II) Fe2(III)(HCOO)10(C6H7N)6]n.

The structure of the complex, [Fe2(II)Fe2(III)(HCOO)10(C6H7N6)n, (1) exhibits a neutral two-dimensional layer network of alternating iron(II) and iron(III) ions, bridged equatorially by formate groups. All iron atoms are octahedrally coordinated, with iron(III) coordinating axially to one gamma-picoline and one formate group, while the iron(II) centers interact axially with two gamma-picoline groups, above and below the layer plane. The complex crystallizes in the triclinic space group P1 at all studied temperatures [at 120 K, the cell dimensions are: a = 10.228(1), b = 12.071(1), c = 12.072(1) A, alpha = 89.801(2), beta = 71.149(2), gamma = 73.371(2) degrees]. An intralayer antiferromagnetic exchange interaction of J = -2.8 cm(-1) between iron(II) and iron(III) was observed in the magnetic studies. Decreasing the temperature to close to 20 K causes a magnetic-ordering phenomenon to occur and a low-temperature phase with a long-range antiferromagnetic spin orientation appears. The magnetic phase transition was confirmed by M?ssbauer spectroscopic studies at temperatures above and below the critical temperature. Structural information of 1 from synchrotron X-ray diffraction data collected at room temperature and 16 K suggests that the antiferromagnetic ordering is caused by an enhanced pi-pi interaction between chi-picoline groups from adjacent layers.     

Nontrivial structural organization of pivalate complexes with the fragment {Fe2Li(μ3-O)}

1. Download : Download high-res image (228KB)
2. Download : Download full-size image

     

Structural and electrochemical studies of annealed LiNiVO4 thin films

We prepared stoichiometric lithium nickel vanadate amorphous thin films by using r.f. magnetron sputtering under controlled oxygen partial pressure. The amorphous films were heated at various temperatures, 300–600 °C, for 8 h. The as‐deposited and annealed thin films were characterized by Rutherford backscattering spectroscopy, nuclear reaction analysis, Auger electron spectroscopy, X‐ray diffraction, scanning electron microscopy and atomic force microscopy. The electrochemical behavior of the various films was studied by the galvanostatic method. The cells were tested in a liquid electrolyte at room temperature, with lithium metal used as the counter and reference electrode. The best electrochemical storage value was obtained with the thin film annealed at 300 °C, which showed superior capacity and small capacity loss during cycling. Copyright © 2007 John Wiley & Sons, Ltd.     

Cleavage of the Fe-Fe Bond of(Me_2SiSiMe_2)[η~5-C_5H_4Fe(CO)_2]_2 with Na/Hg and Molecular Structure of the Ring-Opened Complex

The reaction of the title cyclic complex(1) with sodium amal-gam in THF resulted in the expected cleavage of the Fe--Febond to afford bis-sodium salt (Me_2SiSiMe_2) [η~5-C_5H_4Fe(CO)_2Na]_2 (4). The latter was not isolated and was used di-rectly to react with MeI, PhCH_2Cl, CH_3C(O)Cl, PhC(O)Cl,Cy_3SnCl (Cy=cyclohexyl) or Ph_3SnCl to afford correspondingring-opened derivatives (Me_2SiSiMe_2) [η~5-C_5H_4Fe(CO)_2R]_2[5, R=Me; 6, R=PhCH_2; 7, R=CH_3C(O); 8, R=PhC