Effect of engineered PLGA‐gelatin‐chitosan/PLGA‐gelatin/PLGA‐gelatin‐graphene three‐layer scaffold on adhesion/proliferation of HUVECs

A three‐layered fibrous scaffold composed of fibers of different diameters in each layer was fabricated in correspondence with the structure of the blood vessels. Effect of solution and electrospinning parameters on morphology and diameters of the fibers were investigated by scanning electron microscopy (SEM), for each layer. The SEM images showed that 18% poly (lactic‐co‐glycolic acid) (PLGA)‐gelatin‐chitosan in 1,1,1,3,3,3‐hexafluoro‐2‐propanol (HFIP)/acid acetic solution resulted in bead‐free fibers for the outer layer. For the middle layer, 18% PLGA‐gelatin in HFIP at 13 kV with 13 cm needle to collector distance was chosen as the optimum condition. SEM imaging demonstrated that by increasing graphene content from 0.5 to 2 wt% in the inner layer (as an electrically conductive/platelet anti‐adhesion material), the fiber diameter decreased from 324.01 ± 58.90 to 288.59 ± 70.77 nm. The effect of gelatin crosslinking on the microstructure of the fibers was also examined. Shrinkage ratio decreased from 57 to below 21% upon crosslinking of the three‐layered scaffold in exposure to vapor of 50% glutaraldehyde solution for 2 hours. Mechanical test showed that tensile strength of the crosslinked three‐layer scaffold in the longitudinal direction was 2.90 MPa which is comparable to that of the vein and artery. The MTT [3‐(4,5‐Dimethylthiazol‐2‐yl)‐2,5‐diphenyltetrazolium bromide] assay displayed cell viability of above 96% for the PLGA‐gelatin containing 2 wt% graphene. SEM analysis revealed that the addition of graphene to PLGA‐gelatin (up to 2%) causes a remarkable improvement in cell adhesion.     

pH‐Triggered Self‐Assembly of Cellulose Oligomers with Gelatin into a Double‐Network Hydrogel

Multicomponent systems for self‐assembled molecular gels provide huge opportunities to generate collective or new functions that are not inherent in individual single‐component gels. However, gelation tends to require careful and complicated procedures, because, among a myriad of kinetically trapped structures related to the degree of mixing of multiple components over a wide range of scales, from molecular level to macroscopic scale, a limited number of structures that exhibit the desired function need to be constructed. This study presents a simple method for the construction of double‐network (DN) hydrogels with improved stiffness composed of crystalline cellulose oligomers and gelatin. The pH‐triggered self‐assembly of cellulose oligomers leads to the formation of robust networks composed of crystalline nanofibers in the presence of dissolved gelatin, followed by cooling to allow for the formation of soft gelatin networks. The resultant DN hydrogels exhibit improved stiffness; the improvement in gel stiffness with double networking is comparable to that of previously reported DN hydrogels produced via a time‐consuming enzymatic reaction.     

纳米CdS与明胶蛋白质的相互作用

利用荧光光谱和紫外-可见吸收光谱研究了pH＝12.0及不同温度下, CdS纳米晶与明胶结合反应的光谱行为, 实验发现在明胶溶液中CdS的生成对明胶的内源荧光有较强的猝灭作用. 用Lineweave-Burk方程处理实验数据, 发现CdS与明胶发生反应生成了配合物, 结合红外和紫外-可见吸收光谱结果, 属于静态荧光猝灭; 计算了不同温度下反应的结合常数K (285 K: 1.07×104 L•mol－1; 292 K: 9.69×103 L•mol－1; 299 K: 8.06×103 L•mol－1)及对应温度下结合反应的热力学参数(ΔrHm＝－14.18 kJ•mol－1; ΔrGm＝－21.98/－22.28/－22.36 kJ•mol－1; ΔrSm＝27.36/27.74/27.36 J•K－1•mol－1), 证明二者主要靠静电作用力结合. 根据Förster的偶极-偶极非辐射能量转移原理计算出结合位置距离色氨酸残基4.09 nm, 发生分子内的非辐射能量转移. 为探讨纳米颗粒与此类生物大分子之间相互作用的化学机制提供了重要的信息.     

Gelatin/PLLA sponge-like scaffolds allow proliferation and osteogenic differentiation of human mesenchymal stromal cells

Tissue engineering has the potential to supply constructs capable of restoring the normal function of native tissue following injury. Poly(L-lactic acid) (PLLA) scaffolds are amongst the most commonly used biodegradable polymers in tissue engineering and previous studies performed on ovine fibroblasts have showed that addition of gelatin creates a favorable hydrophilic microenvironment for the growth of these cells. The attractiveness of using mesenchymal stromal cells (MSCs) in tissue regeneration is that they are able to differentiate into several lines including osteoblasts. In this study, we investigated the ability of gelatin/PLLA sponges to support the adhesion, proliferation, and osteogenic differentiation of human MSCs isolated from the bone marrow of four donors. [Figure: see text].     

A Shear-Thinning,Self-Healing,Dual-Cross Linked Hydrogel Based on Gelatin/Vanillin/Fe3+/AGP-AgNPs: Synthesis,Antibacterial, and Wound-Healing Assessment

A shear-thinning and self-healing hydrogel based on a gelatin biopolymer is synthesized using vanillin and Fe³⁺ as dual crosslinking agents. Rheological studies indicate the formation of a strong gel found to be injectable and exhibit rapid self-healing (within 10 min). The hydrogels also exhibited a high degree of swelling, suggesting potential as wound dressings since the absorption of large amounts of wound exudate, and optimum moisture levels, lead to accelerated wound healing. Andrographolide, an anti-inflammatory natural product is used to fabricate silver nanoparticles, which are characterized and composited with the fabricated hydrogels to imbue them with anti-microbial activity. The nanoparticle/hydrogel composites exhibit activity against Escherichia coli, Staphylococcus aureus, and Burkholderia pseudomallei, the pathogen that causes melioidosis, a serious but neglected disease affecting southeast Asia and northern Australia. Finally, the nanoparticle/hydrogel composites are shown to enhance wound closure in animal models compared to the hydrogel alone, confirming that these hydrogel composites hold great potential in the biomedical field.     

Role of Zinc-Doped Bioactive Glass Encapsulated with Microspherical Gelatin in Localized Supplementation for Tissue Regeneration: A Contemporary Review

Gelatin, a natural polymer, provides excellent tissue compatibility for use in tissue rehabilitation. Bioactive glasses (BAG) offer superior capacity in stimulating a bioactive response but show high variability in uptake and solubility. To tackle these drawbacks, a combination of gelatin with BAG is proposed to form composites, which then offer a synergistic response. The cross-linked gelatin structure’s mechanical properties are enhanced by the incorporation of the inorganic BAG, and the rate of BAG ionic supplementation responsible for bioactivity and regenerative potential is better controlled by a protective gelatin layer. Several studies have demonstrated the cellular benefits of these composites in different forms of functional modification such as doping with zinc or incorporation of zinc such as ions directly into the BAG matrix. This review presents a comprehensive perspective on the individual characteristics of BAG and gelatin, including the synthesis and mechanism of action. Further, adaptation of the composite into various applications for bone tissue engineering is discussed and future challenges are highlighted.     

Crosslinked Silk Fibroin/Gelatin/Hyaluronan Blends as Scaffolds for Cell-Based Tissue Engineering

3D porous scaffolds fabricated from binary and ternary blends of silk fibroin (SF), gelatin (G), and hyaluronan (HA) and crosslinked by the carbodiimide coupling reaction were developed. Water-stable scaffolds can be obtained after crosslinking, and the SFG and SFGHA samples were stable in cell culture medium up to 10 days. The presence of HA in the scaffolds with appropriate crosslinking conditions greatly enhanced the swellability. The microarchitecture of the freeze-dried scaffolds showed high porosity and interconnectivity. In particular, the pore size was significantly larger with an addition of HA. Biological activities of NIH/3T3 fibroblasts seeded on SFG and SFGHA scaffolds revealed that both scaffolds were able to support cell adhesion and proliferation of a 7-day culture. Furthermore, cell penetration into the scaffolds can be observed due to the interconnected porous structure of the scaffolds and the presence of bioactive materials which could attract the cells and support cell functions. The higher cell number was noticed in the SFGHA samples, possibly due to the HA component and the larger pore size which could improve the microenvironment for fibroblast adhesion, proliferation, and motility. The developed scaffolds from ternary blends showed potential in their application as 3D cell culture substrates in fibroblast-based tissue engineering.     

Preparation of microparticles composed of cinnamoyl gelatin and cinnamoyl alginate by spray-drying method and effect of UV irradiation and pH value on their release property

Microparticles composed of cinnamoyl gelatin (CinGel) and cinnamoyl alginate (CinAlg) were prepared as a UV irradiation- and pH-responsive carrier by a spray-drying method. CinGel and CinAlg were prepared by a condensation reaction. Using a colorimetric method, the gelatin to CA mass ratio and the alginate to CA mass ratio were calculated to be 1:0.04 and 1:0.02, respectively. The complexation of CinGel and CinAlg in aqueous solution took place when the medium was acidic (e.g., pH 4.0) and the maximum complexation was obtained when the CinGel/CinAlg mass ratio was 7:3. On SEM photographs, some spray-dried CinGel/CinAlg particles were spherical and others were irregularly shaped, and the diameter was a few to tens of micrometers. The release degrees of amaranth loaded in UV-treated microparticles were lower than those of the dye loaded in UV-untreated ones, possibly because of the photo cross-linkage of CinGel and CinAlg. Regardless of whether the microparticles were UV-treated, the release degree at pH 4.0 was significantly lower than the release degree at pH 6.0 and pH 8.0, possibly because of complexation of CinGel and CinAlg under the acidic condition.