纳米晶ZrO2:Er3+-Yb3+的制备及其室温上转换发射

用化学共沉淀法制备了ZrO₂:Er³⁺-Yb³⁺纳米晶粉体，所制备的纳米晶粉体具有较强的室温上转换发射和红外发射.研究了样品的晶体结构和上转换发光性质随着Yb³⁺掺杂浓度和煅烧温度的变化关系.通过X射线衍射谱分析发现，经800℃煅烧2h后得到的ZrO₂:Er³⁺-Yb³⁺纳米晶是四方相和单斜相的混合结构，经950℃煅烧2h后得到的样品以单斜相为主，随着Y     

Upconversion luminescence of Tm^3＋/Yb^3＋ codoped oxyfluoride glasses

Novel oxyfluoride glasses are developed with the composition of 30SiO2-15Al2O3-28PbF2-22CdF2-0.1TmF3 - xYbF3 - （4.9 - x） AlF3（x=0, 0.5, 1.0, 1.5, 2.0） in tool fraction, Furthermore, the upconversion luminescence characteristics under a 970nm excitation are investigated. Intense blue, red and near infrared luminescences peaked at 453nm, 476nm, 647nm and 789nm, which correspond to the transitions of Tm^3＋： ^1D2 →^3F4, ^1G4 →^3H6, ^1G4 →^3F4, and ^3H4 →^3H6, respectively, are observed. Due to the sensitization of Yb^3＋ ions, all the upconversion luminescence intensities are enhanced considerably with Yb^3＋ concentration increasing. The upconversion mechanisms are discussed based on the energy matching rule and quadratic dependence on excitation power. The results indicate that the dominant mechanism is the excited state absorption for those upconversion emissions.     

TiO2∶Mo体系的光子雪崩上转换

在 978nm激光二极管的激发下 ,Mo掺杂的TiO2 材料表现出很强的宽带上转换发光 ,该发光来源于 [MoO4]2 - 基团的激发态3T1 ,3T2 能级到基态1 A1 能级的电子跃迁 .通过研究发光强度与抽运功率的关系及上转换发光的上升时间曲线 ,发现TiO2 ∶Mo体系的上转换发光中存在着雪崩机制 ,应用转换函数理论分析了光子雪崩的产生条件和主要特征 ,理论结果和实验数据很好地符合     

e+e-实验中ψ(2S)能区连续态单光子湮没过程的贡献

研究了e+e-实验中ψ(2S)能区连续态单光子湮没过程的截面对观测总截面的贡献. 针对ψ(2S)质量处ωπ0和π+π-两个观测末态,利用唯象模型估计了单光子湮没过程贡献的大小. 分析表明,对于ψ(2S)→ωπ0和ψ(2S)→π+π-,以及其他电磁末态分支比的确定,单光子湮没过程的贡献必须认真考虑. 通过研究,我们认为对于BES实验来说,为了获得共振态电磁末态分支比的正确结果,至少需要在低于ψ(2S)共振峰的能量点采集10pb-1的数据.     

Er3+和Yb3+共掺氟氧化物微晶玻璃的研究

制备了Er3 、Yb3 共掺的SiO2-A12O3-PbF2-CdF2系统玻璃,并进行相应的微晶化热处理,研究了氟氧化物微晶玻璃中Er3 离子的上转换发光特性.研究结果表明:原始玻璃经热处理后得到的β-PbF2相氟氧化物微晶玻璃,Er3 和Yb3 所在局域基质声子能量的降低,使微晶玻璃中Er3 上转换发光强度显著提高,而微晶化后Er3 、Yb3 离子局域环境发生变化,导致微晶玻璃中Er3 离子的绿光上转换荧光强度较强,而红光上转换荧光强度相对较弱.     

Effects of oxygen in gamma irradiated aromatic polyesters in film

The effect of gamma irradiation in air is investigated on four thermoplastic polyesters (PET, PBT, PEN, PCT-co-ET) in films containing aromatic rings, in order to evaluate the influence of aromatic density and the role of oxygen on radiation resistance. Physical-chemical-nuclear analyses were used to this purpose. EPR measurements were carried out to detect radical stability against oxygen permeation. Viscometric investigations reported a very similar trend for all the investigated polyesters: a chain break effect that decreases at the highest doses. FT-IR analyses focused on the formation of oxidized species. Positron annihilation spectra pointed out a decrease of the intensity of ortho-positronium formation, while its lifetime remains unchanged with radiation dose.     

Symmetric form of the Hudson-Parthasarathy stochastic equation

We prove that the Hudson-Parthasarathy equation corresponds, up to unitary equivalence, to the strong resolvent limit of Schrödinger Hamiltonians in Fock space and that the symmetric form of this equation corresponds to the weak limit of the Schrödinger Hamiltonians.Translated fromMatematicheskie Zametki, Vol. 60, No. 5, pp. 726–750, November, 1996.     

双参数变形玻色湮没算符高次幂的本征态及其量子统计性质

本文构造了双参数变形玻色湮没算符高次幂a^'k(k≥3)的k个正交归一木征态的数学结构,发现它们能构成一个完备的Hilbert空间,并且讨论了它们的量子统计性质.     

冲击波处理的结晶MgO的化学分析正电子谱研究

冲击波处理的结晶ＭｇＯ的化学分析正电子谱研究＊张菊郑小明（杭州大学催化研究所，杭州３１００２８）常志向（抚顺石油化工研究院，抚顺１１３００１）关键词冲击波，化学分析正电子谱，结晶氧化镁，丁烯，脱氢冲击波是在介质中以超音速传播的压力脉冲．气体中的冲击波...     

一种新型铒镱共掺碲硅酸盐玻璃的光谱性质及荧光俘获效应研究

用高温熔制法制备了系列Er^3＋／Yb^3＋共掺碲硅酸盐玻璃样品，测试和分析了玻璃样品的吸收光谱、荧光光谱、上转换发光光谱及热稳定性。结果表明：这种玻璃具有较宽的荧光半高宽、较大的受激发射截面，较好的热稳定性。970nm泵浦下该系列玻璃在可见光525，546和658nm这3处存在明显的上转换现象，它们分别由Er^3＋离子^2H11/2→^4 I15/2，4S3/2→^4 I15/2和^4 F9/2→^4 I15/2辐射跃迁产生。另外，测试和讨论了在不同样品厚度下玻璃的光谱特性，如荧光光谱、荧光寿命和上转换发光光谱等。结果表明，荧光俘获效应对Er^3＋离子1．5μm波段荧光及上转换发光都有着较大的影响，并随着玻璃厚度的增加而增大，导致测量值与实际值产生较大的偏差。