Structural and electrical properties of crystalline (1−x)Ta2O5−xTiO2 thin films fabricated by metalorganic decomposition

Polycrystalline (1−x)Ta₂O₅−xTiO₂ thin films were formed on Si by metalorganic decomposition (MOD) and annealed at various temperatures. As-deposited films were in the amorphous state and were completely transformed to crystalline after annealing above 600 °C. During crystallization, a thin interfacial SiO₂ layer was formed at the (1−x)Ta₂O₅−xTiO₂/Si interface. Thin films with 0.92Ta₂O₅–0.08TiO₂ composition exhibited superior insulating properties. The measured dielectric constant and dissipation factor at 1 MHz were 9 and 0.015, respectively, for films annealed at 900 °C. The interface trap density was 2.5×10¹¹ cm⁻² eV⁻¹, and flatband voltage was −0.38 V. A charge storage density of 22.8 fC/μm² was obtained at an applied electric field of 3 MV/cm. The leakage current density was lower than 4×10⁻⁹ A/cm² up to an applied electric field of 6 MV/cm.     

Preparation and characterization of iron oxide thin films by spray pyrolysis using methanolic and ethanolic solutions

Iron oxide thin films have been obtained by spray pyrolysis using 100% methanolic and ethanolic solutions of iron tri-chloride. The films were deposited onto ITO-coated glass substrates. The preparative conditions have been optimized to obtain compact, pin-hole-free and smooth thin films which are adherent to the substrate. The structural, morphological and compositional characterizations have been carried out by X-ray diffraction, scanning electron microscopy and energy dispersive X-ray analysis. The films deposited using ethanolic solution results into pure hematite; α-Fe₂O₃ thin films, however, films deposited using methanolic solution consists of hematite and maghemite-c phases of iron oxide. The films are nanocrystalline with particle size of 30-40 nm. The optical absorbance of the film was of the order of 10⁵ cm⁻¹. The optical band gap of films was found to be 2.26 and 2.20 eV for the films deposited using methanolic and ethanolic solutions, respectively.     

Synthesis and properties of triethylammonium 2,2,5-triphenyl-1,3,2,5-dioxaborataphosphorinane

The reaction of bis(hydroxymethyl)phenylphosphine with isobutyl diphenylborate in the presence of triethylamine leads to the formation of triethylammonium 2,2,5-triphenyl-1,3,2,5-dioxaborataphosphorinane (1). The reaction of compound 1 with electrophilic reagents (O, S, Se, CH₂O, RHal) leads to quaternization of the phosphorus atom, giving the corresponding phosphine oxides, sulfides, and selenides and P,B-containing betaines. In the reactions of compound 1 with amines aminomethylphosphines of the diazaphosphorinane and diazadiphosphacyclooctane series are formed. Ammonium 1,3,2,5-dioxaborataphosphorinanes dissociate in solutions and enter into ion exchange with phosphonium iodides, leading to phosphonium 1,3,2,5-dioxaborataphosphorinanes. The latter, in the case of the aminomethylphosphonium cation, undergo intramolecular rearrangement with the formation of P,B-containing betaines and aminomethylphosphines.Deceased.A. E. Arbuzov Institute of Organic and Physical Chemistry, Kazan' Scientific Center, Russian Academy of Sciences, 420083 Kazan'. Translated fromIzvestiya Akademii Nauk, Seriya Khimicheskaya, No. 6, pp. 1398–1405, June, 1992.     

Tuning size and catalytic activity of nano-clusters of cobalt oxide

Cobalt oxides were prepared by three different methods: (1) by reacting cobalt nitrate with oxalic acid, (2) co-precipitating cobalt nitrate with sodium carbonate, and (3) using sodium dodecyl sulphate as organic surfactant. All three samples were characterized before and after calcination by solvent extraction and the resulting products examined by IR spectroscopy. In the case of method 3, the removal of surfactant was followed by TGA studies. Products from all three methods were identified by XRD. Peaks in low angle XRD indicate the porous nature of the oxides. The morphology of the pores was studied by transmission electron microscopy. Some irregular pore structures were obtained for samples from methods 1 and 2, with an average size of 4–6 nm. Only the product from method 3 using SDS as template showed ordered structure and optimum size, and Brunauer-Emmet-Teller surface areas of the as-prepared, as well as the treated samples, exhibited H3 type hysteresis. The samples from the three methods were used as catalysts in the oxidation reaction of cyclohexane under mild conditions and the catalytic efficiency of the cobalt oxide was comparable with mesoporous cobalt oxides.     

Orientation and relaxation of polymer–clay solutions studied by rheology and small-angle neutron scattering

The influence of shear on viscoelastic solutions of poly(ethylene oxide) (PEO) and clay [montmorillonite, i.e., Cloisite NA+ (CNA)] was investigated with rheology and small-angle neutron scattering (SANS). The steady-state viscosity and SANS were used to measure the shear-induced orientation and relaxation of the polymer and clay platelets. Anisotropic scattering patterns developed at much lower shear rates than in pure clay solutions. The scattering anisotropy saturated at low shear rates, and the CNA clay platelets aligned with the flow, with the surface normal parallel to the gradient direction. The cessation of shear led to partial and slow randomization of the CNA platelets, whereas extremely fast relaxation was observed for laponite (LRD) platelets. These PEO–CNA networklike solutions were compared with previously reported PEO–LRD networks, and the differences and similarities, with respect to the shear orientation, relaxation, and polymer–clay interactions, were examined. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3102–3112, 2004     

Shape-controlled synthesis of nanocrystalline titania at low temperature

The interesting shape (shuttle-like, sphere with needles, uniform particles) rutile titania were prepared by the hydrolysis of TiCl₄ in high acidic aqueous solution in the absence or presence of PEG-1000. PEG-1000 acted as dispersant, which could control the shape and size of the precipitate of titania. As a result, shuttle-like nanocrystalline appeared and the aggregation was improved with the increase of the amount of acid and the decrease of the concentration of TiCl₄ in the absence of PEG-1000. Uniform nanoparticles were obtained in the presence of PEG-1000 and the diameter of the particles decreased with increasing the amount of PEG-1000. This process simplification will lower production cost and make continuous process possible. The products were analyzed using X-ray diffractometer, transmission electron microscopy.     

Thickness of a silica-tethered poly(ethylene oxide) layer measured by spin labeling

EPR spectroscopy of labeled poly(ethylene oxide) (PEO) grafted on silica has been used to characterize the conformation and local dynamics of the chains. Grafted molecules of MW 2000 with grafting ratios of 0.045, 0.057, 0.126, and 0.42 molecules/nm² were in contact with benzene. The mobility of the label was compared with that observed for solution of PEO from very diluted to highly concentrated and even bulk PEO. Thus, the concentration inside the grafted layer could be evaluated and also the thickness, which evolves rather linearly with the grafting ratio. © 1995 John Wiley & Sons, Inc.     

A comparative XPS and UPS study of VOx layers on mineral TiO2(001)‐anatase supports

Four vanadium oxide layers on mineral TiO₂(001)‐anatase supports with different thickness (3–33 Å) were prepared with reactive d.c. magnetron sputtering and were extensively studied with photoelectron spectroscopy. Al Kα radiation and 150 eV synchrotron radiation were used as excitation sources. The evolution of the 2p, 3s and 3p core level line shapes of V and Ti as a function of the vanadium oxide thickness was studied, as well as the O1s and O2s core lines and the valence band. All the V2p spectra of the deposited vanadium oxide layers consist of at least 60% V⁵⁺, the rest being V⁴⁺. The V3p region is complicated by multiplet splitting, which prevents the determination of the vanadium oxidation state. The V3p multiplet splitting is different for the two excitation energies. No reduction of the titania support surface due to the vanadium oxide deposition was observed. Copyright © 2006 John Wiley & Sons, Ltd.     

Heterograft copolymers of poly(ε‐caprolactone) prepared by combination of ATRA “grafting onto” and ATRP “grafting from” processes

This paper aims at reporting on the synthesis of a heterograft copolymer by combining the “grafting onto” process based on atom transfer radical addition (ATRA) and the “grafting from” process by atom transfer radical polymerization (ATRP). The statistical copolymerization of ε‐caprolactone (εCL) and α‐chloro‐ε‐caprolactone (αClεCL) was initiated by 2,2‐dibutyl‐2‐stanna‐1,3‐dioxepane (DSDOP), followed by ATRA of parts of the chlorinated units of poly(αClεCL‐co‐εCL) on the terminal double bond of α‐MeO,ω‐CH₂?CH? CH₂? CO₂‐poly(ethylene oxide) (PEO). The amphiphilic poly(εCL‐g‐EO) graft copolymer collected at this stage forms micelles as supported by dynamic light scattering (DLS) and transmission electron microscopy (TEM). The unreacted pendant chloro groups of poly(εCL‐g‐EO) were used to initiate the ATRP of styrene with formation of copolymer with two populations of randomly distributed grafts, that is PEO and polystyrene. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6015–6024, 2006     

Synthesis of new thermosetting poly(2,6‐dimethyl‐1,4‐phenylene oxide)s containing epoxide pendant groups

A new class of thermosetting poly(2,6‐dimethyl‐1,4‐phenylene oxide)s containing pendant epoxide groups were synthesized and characterized. These new epoxy polymers were prepared through the bromination of poly(2,6‐dimethyl‐1,4‐phenylene oxide) in halogenated aromatic hydrocarbons followed by a Wittig reaction to yield vinyl‐substituted polymer derivatives. The treatment of the vinyl‐substituted polymers with m‐chloroperbenzoic acid led to the formation of epoxidized poly(2,6‐dimethyl‐1,4‐phenylene oxide) with variable pendant ratios, and the structures and properties were studied with nuclear magnetic resonance spectroscopy, Fourier transform infrared spectroscopy, differential scanning calorimetry, thermogravimetric analysis, and gel permeation chromatography. The ratios of pendant functional groups were tailored for the polymer properties, and the results showed that the glass‐transition temperatures increased as the benzylic protons were replaced by bromo‐, vinyl‐, or epoxide‐functional groups, whereas the thermal stability decreased in comparison with the original polymer. Within a molar fraction of 20–50%, the degree of functionalization had little effect on the glass‐transition temperature; however, it correlated inversely with the thermal stability of each functionalized polymer. The thermal curing behavior of the epoxide‐functionalized polymer was enhanced by the increment of the pendant functionality, which resulted in a significant increase in the glass‐transition temperature as well as the thermal stability after the curing reaction. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5875–5886, 2006