Preparation of TiO2 Sol Using TiCl4 as a Precursor

A titanium dioxide sol with narrow particle size distribution was synthesized using TiCl₄ as the starting material. The sol was prepared by a process where HCl was added to a gel of hydrated titanium oxide to dissolve it. The resulting aqueous titanic acid solution was heated to form titanium dioxide sol. The effects of preparation parameters were investigated. TiCl₄ was slowly added to distilled water at 5°C. Aqueous solution of sodium hydroxide was added to adjust the pH of the system to 8–12. After aging for a period of time, the peptized sol was filtered and sufficiently washed. The filtered cake was repulped in water. Hydrochloric acid was slowly added to the solution with stirring. After condensation reaction and crystallization, a transparent sol with suspended TiO₂ was formed. XRD results show that the crystalline phase was anatase. The suspended TiO₂ particles were rhombus primary particles with the major axis ca. 20 nm and the minor axis ca. 5 nm. The TiO₂ particles prepared at pH 8 had the largest surface area of 141 cm³/g and it was microporous. The compositions of the solution which yielded the smallest suspended TiO₂ particles were TiO₂:HCl (35% HCl) = 1:1 (molar ratio), concentration of TiO₂ = 10%. Hydroxypropyl cellulose with viscosity of 150–400 cps was added as a dispersant. The sol was excellent in dispersibility and long-term stability. Transparent thin films could be obtained through dip-coating glass substrate in the sol. The dip-coating on glass can be less than three times to have one monolayer TiO₂. The transparent TiO₂ thin film had strong hydrophilicity after being illuminated by UV light.     

Li_3PO_4包覆LiMn_2O_4正极材料的结构表征和电化学性能

采用共沉淀法在尖晶石LiMn2O4颗粒表面包覆Li3PO4.XRD、SEM研究结果表明,包覆后的材料仍为尖晶石结构,粒径均匀.电化学性能测试表明,Li3PO4包覆层的存在,减少了正极材料与电解液的直接接触,抑制了高温下电解液对LiMn2O4材料的侵蚀,从而有效改善了高温下材料的循环性能.在40℃时,包覆样品的比容量衰减率都低于未包覆样品,其中包覆1%Li3PO4的样品的初始比容量为110.4mAh/g,50次循环后比容量为84.1mAh/g.     

Dynamically coating the capillary with 1-alkyl-3-methylimidazolium-based ionic liquids for separation of basic proteins by capillary electrophoresis

Ionic substances with melting points close to room temperature are referred to as ionic liquids. Because ionic liquids are environmentally benign and are good solvents for a wide range of both organic and inorganic materials, interest for their potential uses in different chemical processes is increasing. In this paper, a capillary electrophoretic method for the analysis of basic proteins including lysozyme, cytochrome c, trypsinoge, and α-chymotyypsinogen A is reported. The method, in which 1-alkyl-3-methylimidazolium-based ionic liquids are used as the running electrolytes, leads to a surface charge reversal on the capillary wall. The effects of the alkyl group, imidazolium counterion, and the concentration of the ionic liquids were discussed. The optimum buffer system was a 90 mM 1-ethyl-3-methylimidazolium tetrafluoroborate (1E-3MI-TFB) solution. The applied voltage was −15 kV and detection was performed by monitoring absorbance at 240 nm. Baseline separation, high efficiencies, and symmetrical peaks of four proteins were obtained. The R.S.D. values of migration times and peak areas were <0.68 and <3.0%, respectively. The separation mechanism seems to involve association between the imidazolium cations and the proteins.     

Protective Properties of Zinc-Rich Coatings: An Impedance Method Estimate

The impedance of zinc-rich polymer coatings on steel in a 3-% NaCl solution is studied. The electrochemical behavior of the electrode is satisfactorily described by an equivalent circuit that contains a constant-phase element, which reflects fractal properties of the zinc surface in the binder. From the results of calculations of the circuit elements for metal-rich electrodes with different zinc contents computed are fractions of the active area of the surface of the coating and its fractal dimensionality.     

CZE separations of basic proteins at low pH in fused silica capillaries with surfaces modified by silane derivatization and/or adsorption of polar polymers

Mixtures of several basic proteins have been used to test CZE capillaries with surfaces modified by new pretreatment procedures; the performance obtained has been compared with that achieved using capillaries treated by procedures described in the literature. It has been shown that addition of non-ionic polyvinylalcohols (PVA) to CZE buffer solutions deactivates even bare, i.e. untreated, fused silica surfaces and renders them suitable for separations of basic proteins. The performance obtained from such surfaces was comparable with that of capillaries modified by the more elaborate procedures of etching, silanol derivatization, and/or adsorptive coating (again with polymers). A home-made device is described which enables derivatization and coating reactions to be performed on fused silica capillaries under an inert atmosphere, i.e. one free from oxygen and water.     

环氧丙烯酸酯的紫外光固化

制备了适于配制紫外光固化涂料的环氧丙烯酸酯，研究了反应温度、阻聚剂、催化剂等因素对环氧树脂与丙烯酸反应的影响；讨论了反应机理和动力学；并利用红外光谱观察了产物的紫外光固化行为。季铵盐能有效地催化环氧树脂和丙烯酸的反应，当其用量为０．６％～１．２％时，在９０～１１０℃反应４．５～８小时后，环氧基转化率大于９７％。由此配制的光固化涂料经紫外光辐照能快速固化。     

Carbon film growth on iron substrates by a CVD method

Carbon film coatings have been produced by a hot‐wall chemical vapor deposition (CVD) method under moderate conditions from pyrolysis of a mixture of propane and argon on an Fe(110) substrate at temperatures of 800–900 °C for different deposition times. The effects of temperature and reaction time on the growth of the carbon films were studied. Field‐emission scanning electron microscopy (FESEM), Raman microscopy, Auger electron spectroscopy (AES) and x‐ray diffraction methods have been performed to study the surface morphologies, growth features and microstructures of the carbon film coatings. The FESEM analyses indicated that carbon films on an Fe substrate consisted of flat‐layer and filamentous morphologies. Raman and AES analyses showed that the carbon initially was crystalline but the degree of disorder in the top layer of the carbon film increased with increasing deposition temperature. High‐resolution transmission electron microscopy studies are also in agreement with Raman results. The same trend was observed when the deposition time was increased from 5 to 30 min. Copyright © 2005 John Wiley & Sons, Ltd.     

Coaxial electrospinning core-shell fibers for self-healing scratch on coatings

Polystyrene (PS) fibers with core-shell structure were prepared by coaxial electrostatic spinning using liquid epoxy or curing agent as the core and PS solution as the shell. Scratch self-healing coatings were realized by using the healant-loaded core-shell fibers in the matrix.     

Preparation and properties of sol-gel coating films

The present state of our knowledge on sol-gel coating films has been reviewed. A qualitative discussion is made on the limit of the film thickness which can be achieved in the sol-gel method and the factors affecting the film thickness. Considering that properties of the film are intimately related to the microstructure, types of microstructures accomplished by the sol-gel coating are introduced with examples.     

Surface and interface characterization of polyester‐based polyurethane/nano‐silica composites

Polyester‐based polyurethane/nanosilica composites were prepared via in situ polymerization and investigated by contact angle measurement, transmission electron microscopy (TEM), atomic force microscopy (AFM) and peel testing in an Instron testing machine. The contact angle and surface free energy results show that nanosilica tended to enrich at the interface between nanocomposite polymers and the substrates, TEM indicated that nanosilica particles were evenly dispersed in the bulk and AFM demonstrated that nanoparticles were located at both the surfaces and interfaces of nanocomposite polymers and that the roughness of both the surfaces and interfaces had a decreasing tendency as the nanosilica content increased, as did the adhesion strength between the nanocomposite polymers and substrates. Copyright © 2003 John Wiley & Sons, Ltd.