Hydroxyapatite coating on porous silicon substrate obtained by precipitation process

Hydroxyapatite Ca₁₀(PO₄)₆(OH)₂ (HAP) is known as a bioactive and biocompatible material, HAP coatings were used to improve the biocompatible of substrate by many researcher, In this work, HAP thin films on porous silicon (PS) substrates have been prepared by aqueous precipitation method with rapid thermal annealing (RTA) processes. The HAP films had been prepared under the annealing temperature ranging from 300 to 1000 °C. By the measurement of X-ray diffraction (XRD), it was found that for the crystallinity optimization, the heat-treatment at 850–950 °C for 1 h would be favorable. Atomic force microscopy (AFM) and scanning electron microscope (SEM) measurements reveal a dense and smooth surface of the HAP film, and tightly adherence of the coating on porous silicon substrate after sintered. Thus, by this method, porous silicon could be increased its bioactivity and so that could be used in the biomedical area.     

On the origin of 1.5 μm luminescence in porous silicon coated with sol–gel derived erbium-doped Fe2O3 films

Sol–gel derived Fe₂O₃ films containing about 10 wt% of Er₂O₃ were deposited on porous silicon by dipping or by a spin-on technique followed by thermal processing at 1073 K for 15 min. The samples were characterized by means of PL, SEM and X-ray diffraction analyses. They exhibit strong room-temperature luminescence at 1.5 μm related to erbium in the sol–gel derived host. The luminescence intensity increases by a factor of 1000 when the samples are cooled from 300 to 4.2 K. After complete removal of the erbium-doped film by etching and partial etching the porous silicon, the erbium-related luminescence disappears. Following this, luminescence at 1.5 μm originating from optically active dislocations (“D-lines”) in porous silicon was detected. The influence of the conditions of synthesis on luminescence at 1.5 μm is discussed.     

Fractal porous media III: Transversal Stokes flow through random and Sierpinski carpets

The transversal Stokes flow of a Newtonian fluid through random and Sierpinski carpets is numerically calculated and the transversal permeability derived. In random carpets derived from site percolation, the average macroscopic permeability varies as (- _c)^3/2, close to the critical porosity _c. This exponent is found to be slightly different from the conductivity exponent. Results for Sierpinski carpets are presented up to the fourth generation. The Carman equation is not verified in these two model porous media.     

超临界co2中模板法制备氧化铝多孔材料

超临界co2;活性炭;模板;氧化铝;多孔     

氧化铝/碳纳米管复合材料的制备及表征

采用聚乙烯醇对碳纳米管表面进行改性，通过化学沉淀法将Al(OH)₃均匀沉积在碳纳米管表面，然后在氮气气氛下于500 ℃煅烧2 h，制备出氧化铝/碳纳米管复合材料。采用TEM、TG、DTA、XRD、IR、氮吸附脱附(比表面积及孔结构分析)等对氧化铝/碳纳米管复合材料进行表征，结果表明:未经聚乙烯醇改性的碳纳米管，氧化铝与碳纳米管相互分离;经聚乙烯醇改性的碳纳米管，氧化铝与碳纳米管结合良好。经聚乙烯醇改性的碳纳米管表面均匀覆盖一层聚乙烯醇膜，通过聚乙烯醇的吸附作用， Al(OH)₃沉积在碳纳米管表面形成一层连续的覆盖层。     

铕离子探针研究Al2O3的相变过程

氧化铝具有许多重要的工业用途，而制备高热稳定活性氧化铝的技术也在不断地发展[1，2]，因此，研究其高温烧结下的相变过程很有意义．离子深法作为新型测试手段，已成功地用于生物大分子结构与功能研究方面［‘］，而在固体材料测试中的应用尚未见报道．我们以EU’“作为荧光探针，并结合＊＊D和＊nR研究了川对。在不同烧结温度下的相变过程．1实验部分样品的制备采用复盐分解法．先将Elf刀s用高纯硝酸溶解定容．以占AlzO。重量1％的量加入到硫酸铝锭溶液中，进行超声处理，冷冻干燥．再依次登于900”C、1000C、1100C、1200C的高温炉…     

多孔硅的电化学制备

单晶硅在氢氟酸溶液中阳极氧化可制得多孔硅, 多孔硅是一种以新形态存在的硅, 与单晶硅相比, 它表现出独特的物理性质和化学活性。荧光光谱峰的蓝移表明, 在p-型低掺杂衬底硅上形成的多孔硅中存在量子尺寸效应, 新近获得的Raman光谱也证实了这一点。     

La2O3对氧化铝透明陶瓷显微结构和透光性能的影响

采用传统无压烧结工艺在氢气氛下制备Al2O3透明陶瓷。实验结果表明：MgO和La2O3复合添加时，随着La2O3掺杂量的增加体积密度总体上保持上升的趋势。随着保温时间的延长，陶瓷的致密化程度增大，残余气孔逐步排出，晶粒进一步长大。采用La2O3和MgO复合添加比单独掺入MgO陶瓷样品透过率更高，掺杂效果更好。在烧结温度为1750℃，保温时问为1h条件下，在波艮为300～800nm测试范围内，陶瓷样品的全透过率大于82％，最大值为86％。     

Donor-acceptor properties, catalytic activity, and negative charge exoemission from the alumina surface modified with lithium cations

Donor-acceptor properties of alumina modified with lithium cations were studied by ESR of paramagnetic complexes of adsorbed anthraquinone. The results were compared with the data on negative ion emission (exoemission) accompanying the decomposition of isopropyl alcohol in the adsorption layer. The data on the activity measured by the pulse microcatalytic technique in isopropyl alcohol decomposition are discussed. Small additives of lithium were found to promote catalytic activity of the samples. The role of acid and basic sites in isopropyl alcohol decomposition was discussed. Published in Russian in Izvestiya Akademii Nauk. Seriya Khimicheskaya, No. 4, pp. 616–621, April, 2006.     

ESR study of products of transformation of 3,6-tert-butylpyrocatechol on alumina, zinca, silica, and titania

The formation of semiquinone and phenoxazyl radicals and metallocomplexes with semiquinone ligands was observed by ESR during the interaction of di-tert-butylpyrocatechol with Al₂O₃, ZnO, SiO₂, and TiO₂. In the case of different modifications of SiO₂, admixtures of TiO₂ exhibit a higher reactivity in complex formation with the organic substrate. Translated fromIzvestiya Akademii Nauk. Seriya Khimicheskaya, No. 10, pp. 1975–1978, October, 1998.