Electrocatalysis of Nitrate Reduction at Copper‐Nickel Alloy Electrodes in Acidic Media

The cathodic reduction of NO in 1.0 M HClO₄ is investigated by voltammetry at pure Ni and Cu electrodes, and three Cu‐Ni alloy electrodes of varying composition, all configured as rotated disks. Voltammetric data obtained using these hydrodynamic electrodes demonstrate significantly improved activity for NO reduction at Cu‐Ni alloy electrodes as compared to the pure Ni and Cu electrodes. This observation is explained on the basis of the synergistic benefit of different surface sites for adsorption of H‐atoms, generated by cathodic discharge of H⁺ at Ni‐sites, and adsorption of NO at Cu‐sites on these binary alloy electrodes. Koutecky‐Levich plots indicate that the cathodic response for NO at a Cu₇₅Ni₂₅ electrode corresponds to an 8‐electron reduction, which is consistent with production of NH₃. In comparison, the cathodic response at Cu₅₀Ni₅₀ and Cu₂₅Ni₇₅ electrodes corresponds to a 6‐electron reduction, which is consistent with production of NH₂OH. Flow injection data obtained using Cu₅₀Ni₅₀ and Cu₂₅Ni₇₅ electrodes with 100‐μL injections exhibit detection limits for NO of ca. 0.95 μM (ca. 95 pmol) and 0.60 μM (ca. 60 pmol), respectively.     

Anodic behavior of nickel-based alloys in the electrolytic production of NF3

The Ni-based alloys, such as Ni-Co, Ni-Mn, Ni-Ag, Ni-Cu, Ni-Al and Ni-Si, prepared by hot isostatic pressing (HIP) at 1000 °C under 2 × 10⁸ Pa for 2 h were employed as the anodes for electrolytic production of NF₃. The current efficiencies for NF₃ formation were 42-38, 52-40, 52-47, 63-62, 50 and 41% for Ni-Co, Ni-Mn, Ni-Ag, Ni-Cu, Ni-Al and Ni-Si alloys, respectively. The current efficiencies only on Ni-Cu alloys with Cu concentrations lower than 10 mol% were almost the same as those on Ni sheet and HIPed Ni anodes, whereas those on the other alloys used in this study were smaller compared with those on both Ni anodes. On the other hand, the current losses caused by anodic dissolution of Ni-Co, Ni-Mn, Ni-Ag, Ni-Cu, Ni-Al and Ni-Si alloy electrodes were 7.95-4.42, 6.40-7.02, 5.60-6.30, 3.34-6.33, 5.10 and 0.18%, respectively. The anode consumptions of Ni-5 mol% Cu and Ni-5 mol% Si alloys were almost the same or smaller compared with those of Ni sheet and HIPed Ni electrodes, though those of other alloys used were large compared with those of both Ni anodes. Consequently, addition of Cu to the nickel matrix is available for a cheaper cost of anode with keeping a same current efficiency as that on the Ni anode and addition of Si to the nickel matrix is effective for decreasing anode consumption largely. A Ni sheet electrode containing a trace of impurities, such as Co, Mn, Ag and Al, is also favorable as the anode for electrolytic production of NF₃.     

环氧化橡胶及其合金的研究与应用

综述了国内外环氧化橡胶及其合金的研究现状和应用趋势,重点介绍了环氧化天然橡胶、环氧化聚丁二烯、环氧化苯乙烯-丁二烯-苯乙烯三嵌段共聚物及其合金的优点,以及影响其物理机械性能的因素和环氧化橡胶的发展方向。     

Hydrogen-induced metal-oxide interaction studied on noble metal model catalysts

Summary The effect of hydrogen reduction on the structure and catalytic properties of “thin film”and “inverse”model systems for supported metal catalysts is discussed. Thin film model catalysts were obtained by epitaxial growth of Pt and Rh nanoparticles on NaCl(001), which were coated with amorphous or crystalline supports of alumina, silica, titania, ceria and vanadia. Structural and morphological changes upon hydrogen reduction between 473 and 973 K were examined by high resolution electron microscopy. Metal-oxide interaction sets in at a specific reduction temperature and is characterized by an initial “wetting”stage, followed by alloy formation at increasing temperature, in the order VO_x< TiO_x< SiO₂< CeO_x< Al₂O₃. “Inverse”model systems were prepared by deposition of oxides on a metal substrate, e.g. VO_x/Rh and VO_x/Pd. Reduction of inverse systems at elevated temperature induces subsurface alloy formation. In contrast to common bimetallic surfaces, the stable subsurface alloys of V/Rh and V/Pd have a purely noble metal-terminated surface, with V positioned in near-surface layers. The uniform composition of the metallic surface layer excludes catalytic ensemble effects in favor of ligand effects. Activity and selectivity, e.g. for CO and CO₂methanation and for partial oxidation of ethene, are mainly controlled by the temperature of annealing or reduction. Reduction above 573 K turned out to be beneficial for the catalytic activity of the subsurface alloys, but not for the corresponding thin film systems which tend to deactivate viaparticle encapsulation.</o:p>     

Silica-supported PtSn alloy doped with Ga, In or, Tl: Characterization and catalytic behaviour in n-hexane dehydrogenation

Silica-supported trimetallic catalysts containing Pt, Sn and a group 13 metal (PtSnM, M=Ga, In, Tl) were prepared by consecutive impregnation steps from cis-[PtCl₂(PPh₃)₂] and chloride precursors. X-ray diffraction (XRD), transmission electron microscopy (TEM), selected-area electron diffraction (ED) and energy dispersive X-ray analysis (EDX) showed large platelet-like particles of PtSn_1−xM_x phases. PtSnGa catalyst with a Pt/(Sn+Ga) molar ratio of 1.72 showed a bimodal particle distribution and a Pt phase was identified. Differences in surface structures were also revealed by the performance of catalysts in the dehydrogenation of n-hexane. For PtSnIn and PtSnTl (Pt/(Sn+M) molar ratio of about 1) the dehydrogenation was favoured. In contrast, PtSnGa catalyst yielded hydrogenolysis products. Photoelectron spectra showed the Pt 4f_7/2 level at a binding energy of 70.0–71.8 eV in all cases. Moreover, the FT-IR spectra of chemisorbed CO on the PtSnGa showed a slight shift in the ν(CO) toward higher values with respect to the monometallic catalyst, pointing to an electronic effect in accordance with photoelectron spectroscopy.     

Electrochemical characterization of Ni–Fe alloy codeposition under MHD control

The nickel–iron alloy electrodeposition is affected by a superimposed magnetic field. Some previous papers [Msellak et al., Magnetohydrodynamics, 39:487–493, 2003 and Msellak et al., J Magn Magn Mat, 281:295–304, 2004] have exhibited some dramatic changes in iron amount and morphology of these deposits. As it is usual for a magnetic field up to 1 T, no charge transfer effect can be expected, and the observed modifications can be explained by the magnetohydrodynamic convection that controls the iron species flux during the electrochemical reaction. By electrochemical impedance spectroscopy and physical investigations (scanning electron microscopy, X-ray diffraction, and inductively coupled plasma), the reduction process is analyzed, the characteristic parameters of the mechanism are determined, and the magnetic field effects can be quantified. Contribution to special issue on “Magnetic field effects in Electrochemistry”.     

Formation of PdNiZn thin film at oil‐water interface: XPS study and application as Suzuki‐Miyaura catalyst

Nanosheet of PdNiZn and nanosphere of PdNiZn/reduced‐graphene oxide (RGO) with sub‐3 nm spheres have been successfully synthesized through a facile oil‐water interfacial strategy. The morphology and composition of the films were determined by X‐ray diffraction (XRD), X‐ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), scanning electron microscopy (SEM), energy dispersive analysis of X‐ray (EDAX) and elemental mapping. In the present study, we have developed a method to minimize the usage of precious Pd element. Due to the special structure and intermetallic synergies, the PdNiZn and PdNiZn/RGO nanoalloys exhibited enhanced catalytic activity and durability relative to Pd nanoparticles in Suzuki‐Miyaura C‐C cross‐coupling reaction. Compared to classical cross‐coupling reactions, this method has the advantages of a green solvent, short reaction times, low catalyst loading, high yields and reusability of the catalysts.     

Influence of aspect ratio and anisotropy distribution in ordered CoNi nanowire arrays

The size effects on magnetic properties of nanowires arrays were studied varying the nanowires diameter and maintaining the same periodicity among them, for two different nominal compositions of Co and Ni in the alloy form. The competition among magnetocrystalline and shape anisotropies changes drastically from smallest to biggest diameters altering the easy axis direction. In the case of 75% of Co in alloy, experimental values of the effective anisotropy constant (K_eff) vary from positive to negative depending on the diameter, which means a reversal of the easy axis direction. For 50% of Co the shape anisotropy dominates over the magnetocrystalline for all studied diameters.     

Dislocation driven chromium precipitation in Fe-9Cr binary alloy: a positron lifetime study

The influence of initial heat treatment on anomalous Cr precipitation within high temperature solubility region of the Fe–9Cr alloy has been investigated using positron lifetime studies. Air-quenched samples with pre-existing dislocations exhibited a distinct annealing stage in positron lifetime between 800 and 1100?K corresponding to Cr-precipitation. During this stage, Transmission Electron Microscopy showed fine precipitates of average size 4 nm, dispersed throughout the sample and from Energy-dispersive X-ray spectroscopy (EDS) analysis they are found to be Cr-enriched. The presence of dislocations is found to be responsible for Cr precipitation.