Synthesis and characterization of nanostructure hydrous iron–titanium binary mixed oxide for arsenic sorption

Synthesis of nanostructure hydrous iron–titanium binary mixed oxide (NHITBMO) had been reported by a simple method, and characterized by the X-ray diffraction (XRD), thermal analysis, transmission electron microscope (TEM), Föurier Transform Infrared (FTIR), surface area, and zero surface charge pH (pHzpc). The synthetic oxide was hydrated and microcrystalline with 77.8 m² g^?1 BET surface area. The particle size (nm) calculated using XRD peak table and TEM image was ~10–13 and 6–8, respectively. The pH_zpc value was 6.0 (±0.05) for the oxide. The NHITBMO showed pH dependent good sorption affinity for arsenic from the aqueous solution and, the Langmuir monolayer capacity (mg g^?1) was 80.0 and 14.6, respectively, for the As(III) and As(V). The pseudo-second order equation described the room temperature arsenic sorption kinetic data well. The minimum dose required was 1.6 g NHITBMO per L of water (As_total = 0.24 mg L^?1) to reduce the arsenic level below 0.01 mg L^?1 in batch treatment process.     

Correlation of photoluminescence of (La,Ln) PO<Subscript>4</Subscript>:Eu<Superscript>3+</Superscript> (Ln = Gd and Y) phosphors with their crystal structures

Eu³⁺-doped (La, Ln) PO₄ (Ln = Gd and Y) phosphors were prepared by a facile co-precipitation method. Their structures and luminescent properties under UV excitation were investigated. Structural characterization of the nanostructured luminescence material was carried out with X-ray powder diffraction analysis. Scanning electron microscopy was carried out to understand the surface morphological features and grain sizes with 50–100 nm. It is found that (La, Gd) PO₄:Eu³⁺ phosphors have the same crystal structure as LaPO₄:Eu³⁺, which is monoclinic with a little different lattice parameters. In the case of (La, Y) PO₄:Eu³⁺ phosphors, however, the gradual change from monoclinic to tetragonal structure of host lattice was observed, as the amount of Y ion increased. From the photoluminescence spectra for (La, Ln) PO₄:Eu³⁺ (Ln = Gd and Y), the emission transition ⁵D₀ → ⁷F₁ has been found to be more prominent over the normal red emission transition ⁵D₀ → ⁷F₂. Furthermore, the size influence on the products was discussed. It was observed that the spectral features possess sharp and bright emission for potential applications on the monitors of the television and some other related electronic systems, in observing the images in orange–red color.     

A “ladder” Morphology in an ABC Triblock Copolymer

ABC triblock copolymers are known to exhibit a wide variety of unique types of morphologies compared to AB diblock copolymers. In the present study, poly(styrene-block-(ethylene-alt-propylene)-block-(methyl methacrylate)) (SEPM) triblock copolymers were synthesized and their morphologies were extensively studied by transmission electron microtomography (TEMT). In the SEPM triblock copolymer, two kinds of morphologies coexist: One was the well-known knitting morphology, and the other was a novel morphology called the “ladder morphology”. The ladder morphology was a major morphology in the SEPM copolymer, the stability of which was discussed in terms of the interfacial area and the solubility parameters between the three components.     

Fabrication and surface-enhanced Raman scattering (SERS) of Ag/Au bimetallic films on Si substrates

Ag films on Si substrates were fabricated by immersion plating and served as sacrificial materials for preparation of Ag/Au bimetallic films by galvanic replacement reaction. The formation procedure of films on the surface of Si was studied by scanning electron microscopy (SEM), which revealed Ag films with island and dendritic morphologies experienced novel structural evolution process during galvanic replacement reaction, and nanostructures with holes were produced within the resultant Ag/Au bimetallic films. SERS activity both of sacrificial Ag films and resultant Ag/Au bimetallic films was investigated by using crystal violet as an analyte. It has been shown that SERS signals increased with the process of galvanic substitution and reached intensity significantly stronger than that obtained from pure Ag films.     

The orientation of the self-assembled monolayer stripes on a crystalline substrate

Two-phase monolayers adsorbed on crystalline substrates can form many patterns. After reviewing the experimentally observed patterns on various substrates, we extend a thermodynamic theory to account for the anisotropy in surface stress, substrate stiffness, and phase boundary energy. We solve the elastic field in the anisotropic substrate by using the Stroh formalism. We then focus on the pattern of periodic stripes, and determine the orientation of the stripes that minimizes the free energy. As an example, we examine in detail the (110) surface of a cubic crystal. Depending on the parameters that characterize anisotropy, the stripes can orient along either , or [001], or certain directions off the two crystalline axes. The transition between these orientations can be of either first or second order. The predications point to additional experiments that are needed to further the understanding.     

Grafting of Vinyudene Chloride. Model Studies with Poly(Vinyl Alcohol) as Substrate

The modification of coatings resins by graft polymerization of vinylidene chloride should produce a coatings binder with improved barrier properties. For superior color stability, vinylidene chloride must be copolymer-ized with other monomers such as alkyl acrylates and methacrylates. Ceric ion initiation was used to graft vinylidene chloride free-radically onto a model alcohol-containing polymer, polyvinyl alcohol. The effects of various reaction parameters on vinylidene chloride grafting were studied. Graft copolymers were characterized using selective solvent extraction, FTIR, SEM, XES, DSC, and x-ray diffraction.     

Spectroscopic Characterizations of Metal-Complexes of 4-Hydroxybenzoic Acid With the Ni(Ⅱ), Mn(Ⅱ), and Cu(Ⅱ) Ions

One of the phenolic acids is 4-hydroxybenzoic acid (HBA) which takes the form of a white crystalline solid with a molecular formula of C₇H₆O₃, a melting point of 214.5 ℃ and a molecular weight of 138.12 g·mol-1. It soluble in polar organic solvents like acetone and alcohols, and slightly soluble in chloroform and water. The reactions between the metal ions and the HBA were carried out under specific conditions like (molar reaction was 2∶2 (ligand to metal), reaction temperature was 60 ℃, media was neutral (pH 7), and solvent was H₂O ∶MeOH (1∶1). Under these conditions, the HBA was deprotonated to form (HOC₆H₄CO-₂; L-). The ligand L- was coordinated to the metal ions forming the metal complexation. The reaction of 4-hydroxybenzoic acid (HOC₆H₄CO₂H; HL) with the Ni(Ⅱ), Mn(Ⅱ) and Cu(Ⅱ) ions afford metal-complexes with gross formula of [Ni₂L₂(NO₃)₂(H₂O)₄], [Mn₂L₂(NO₃)₂(H₂O)₄] and [Cu₂L₂(NO₃)₂(H₂O)₄], respectively. These complexes were characterized by elemental analysis (CHN), magnetic susceptibility, UV-Vis spectra, infrared (IR), and X-ray powder diffraction (XRD) techniques. The complexes of HBA are insoluble in common solvents and hence molar conductance could not be measured, but this very insolubility indicates that the complexes are neutral. Data has demonstrated that the ligand (L-) was coordinated to the metal ion by bidentate bridging carboxylate group (COO-), with an octahedral geometry. Thus, HBA is expected to act as bidentate uninegative ions and the coordination number of the metal ions is six. XRD results showed that the complexes possess uniform and organized microstructures in the nanometer range with a main diameter in the range of 11～28 nm.     

Enhanced photoluminescence of conjugated polymer thin films on nanostructured silver

Photoluminescence of a conjugated polymer in the presence of surface plasmons on metallic nanoparticles is studied. A layered device structure was constructed that enabled control over nanoparticle diameter and separation between the polymer and nanoparticles layers. The dependence of the surface plasmon evanescent field and energy transfer has been investigated with the largest enhancement in photoluminescence observed at a 40 nm distance separation between the fluorophore and the surface plasmon. A spectrum of surface plasmon resonances ranging from the emission to the absorption energies of the conjugated polymer revealed largest enhancements when the resonance was tuned to the conjugated polymer emission energy. At peak photoluminescence the maximum photoluminescent enhancement was found to be 5.6 times of the photoluminescence of the control structure and the total integrated enhancement was 5.9 times.     

Preparation of nanowall Bi2S3 films by chemical bath deposition

Nanowall shaped Bi₂S₃ films were prepared by chemical bath deposition in which ammonium citrate and thioacetamide were used as chelating reagent and sulfur source, respectively. The nanowall Bi₂S₃ films show large-surface-area nanowall shaped morphology. It is found that the pH value (pH = 6 or pH = 6.5) of the solution is a crucial parameter to obtain the nanowall shaped Bi₂S₃ films. The composition of the nanowall Bi₂S₃ films is close to the stoichiometric ratio of Bi₂S₃. The absorption edge of the nanowall shaped Bi₂S₃ films is located at around 900 nm, indicating that the optical bandgap of the Bi₂S₃ films is around 1.4 eV. The nanowall Bi₂S₃ films show obvious photo-sensitivity. The photo-to-dark conductivity ratios of the nanowall Bi₂S₃ films prepared at pH = 6 and pH = 6.5 are all around 50. This value is around five times than that of the non-nanowall shaped Bi₂S₃ films which is prepared at pH = 7.     

Synthesis of Mn-doped ZnS architectures in ternary solution and their optical properties

Mn-doped ZnS sea urchin-like architectures were fabricated by a one-pot solvothermal route in a ternary solution made of ethylenediamine, ethanolamine and distilled water. The as-prepared products were characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM) and photoluminescence spectra (PL). It was demonstrated that the as-prepared sea urchin-like architectures with diameter of 0.5-1.5 μm were composed of nanorods, possessing a wurtzite structures. The preferred growth orientation of nanorods was found to be the [0 0 2] direction. The PL spectra of the Mn-doped ZnS sea urchin-like architectures show a strong orange emission at 587 nm, indicating the successful doping of Mn²⁺ ions into ZnS host. Ethanolamine played the role of oriented-assembly agent in the formation of sea urchin-like architectures. A possible growth mechanism was proposed to explain the formation of sea urchin-like architectures.