Singlewall carbon nanotubes covered with polystyrene nanoparticles by in‐situ miniemulsion polymerization

This work is to make carbon nanotubes dispersible in both water and organic solvents without oxidation and cutting nanotube threads. Polystyrene‐singlewall carbon nanotube (PS‐SWNT) composites were prepared with three different methods: miniemulsion polymerization, conventional emulsion polymerization, and mixing SWNT with PS latex. The two factors, crosslinking and surface coverage of PS are important factors for the mechanical and electrical properties, including dispersion states of SWNT in various solvents. The PS‐SWNT composite prepared via a conventional emulsion polymerization showed SWNT bundles entirely covered with PS, whereas the PS‐SWNT composite prepared via a miniemulsion polymerization showed SWNT partially covered with crosslinked PS nanoparticles. The method of mixing SWNTs with PS latex did not show the well dispersed state of carbon nanotubes because PS was not crosslinked and was dissolved in a solvent, and nanotubes separated from PS precipitated. So the PS nanoparticle‐SWNT composite had lower electrical resistance, and higher mechanical strength than the other composites made by the latter two methods. As the amount of SWNT increases, the bare surface area of SWNT increases and the electrical conductivity increases in the composite made by the miniemulsion polymerization. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 573–584, 2006     

Synthesis,characterization, and electrical properties of polypyrrole/multiwalled carbon nanotube composites

Size‐controllable polypyrrole (PPy)/multiwalled carbon nanotube (MWCNT) composites have been synthesized by in situ chemical oxidation polymerization directed by various concentrations of cationic surfactant cetyltrimethylammonium bromide (CTAB). Raman spectra, FTIR, SEM, and TEM were used to characterize their structure and morphology. These results showed that the composites are core (MWCNT)–shell (PPy) tubular structures with the thickness of the PPy layer in the range of 20–40 nm, depending on the concentration of CTAB. Raman and FTIR spectra of the composites are almost identical to those of PPy alone. The electrical conductivities of these composites are 1–2 orders of magnitude higher than those of PPy without MWCNTs. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6449–6457, 2006     

Continuous reaction system to investigate the dispersion polymerization of vinyl monomers in supercritical carbon dioxide

A laboratory‐scale continuous reaction system using a stirred tank reactor was assembled in our laboratory to study the dispersion polymerization of vinyl monomers in supercritical carbon dioxide (scCO₂). The apparatus was equipped with a suitable downstream separation section to collect solid particles entrained in the effluent stream from the reactor, whose monomer concentration could be measured online with a gas chromatograph. The dispersion polymerization of methyl methacrylate in scCO₂ was selected as a model process to be investigated in the apparatus. The experiments were performed at 65 °C and 25 MPa with 2,2′‐azobisisobutyronitrile as the initiator and a reactive polysiloxane macromonomer as a surfactant to investigate the effect of the mean residence time of the reaction mixture on the monomer conversion, polymerization rate, polymer molecular weight, and particle size distribution. The results were compared with those obtained in batch polymerizations carried out under similar operative conditions. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 4122–4135, 2006     

Measurement and prediction of solubilities and diffusion coefficients of carbon dioxide in starch–water mixtures at elevated pressures

The solubility and diffusion coefficient of carbon dioxide in intermediate‐moisture starch–water mixtures were determined both experimentally and theoretically at elevated pressures up to 16 MPa at 50 °C. A high‐pressure decay sorption system was assembled to measure the equilibrium CO₂ mass uptake by the starch–water system. The experimentally measured solubilities accounted for the estimated swollen volume by Sanchez–Lacombe equation of state (S‐L EOS) were found to increase almost linearly with pressure, yielding 4.0 g CO₂/g starch–water system at 16 MPa. Moreover, CO₂ solubilities above 5 MPa displayed a solubility increase, which was not contributed by the water fraction in the starch–water mixture. The solubilities, however, showed no dependence on the degree of gelatinization (DG) of starch. The diffusion coefficient of CO₂ was found to increase with concentration of dissolved CO₂, which is pressure‐dependent, and decrease with increasing DG in the range of 50–100%. A free‐volume‐based diffusion model proposed by Areerat was employed to predict the CO₂ diffusivity in terms of pressure, temperature, and the concentration of dissolved CO₂. S‐L EOS was once more used to determine the specific free volume of the mixture system. The predicted diffusion coefficients showed to correlate well with the measured values for all starch–water mixtures. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 607–621, 2006     

Characterization and electrical properties of polypyrrole/multiwalled carbon nanotube composites synthesized by in situ chemical oxidative polymerization

This study describes the preparation of polypyrrole (PPy)/multiwalled carbon nanotube (MWNT) composites by in situ chemical oxidative polymerization. Various ratios of MWNTs, which served as hard templates, were first dispersed in aqueous solutions with the surfactant cetyltrimethylammonium bromide to form micelle/MWNT templates and overcome the difficulty of MWNTs dispersing into insoluble solutions of pyrrole monomer, and PPy was then synthesized via in situ chemical oxidative polymerization on the surface of the templates. Raman spectroscopy, Fourier transform infrared (FTIR), field‐emission scanning electron microscopy (FESEM), and high‐resolution transmission electron microscopy (HRTEM) were used to characterize the structure and morphology of the fabricated composites. Structural analysis using FESEM and HRTEM showed that the PPy/MWNT composites were core (MWNT)–shell (PPy) tubular structures. Raman and FTIR spectra of the composites were almost identical to those of PPy, supporting the idea that MWNTs served as the core in the formation of a coaxial nanostructure for the composites. The conductivities of these PPy/MWNT composites were about 150% higher than those of PPy without MWNTs. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1413–1418, 2006     

Activity evaluation of carbon paste electrodes loaded with pt nanoparticles prepared in different radiolytic conditions

Three Pt-based catalysts prepared in different radiolytic conditions and supported on graphite powder were packed into a carbon paste electrode configuration. They were compared to each other, to the commercial (Pt) deposited on activated carbon powder (Johnson Matthey) and to pure Vulcan XC-72 for their respective abilities toward the hydrogen evolution reaction (HER). The Tafel parameters were determined for all these electrodes. From the I–V curves and their quantitative treatment, the following order of activity emerged unambiguously and reads: (PtCO)₂ (fcc structure) > (PtCO)₁ (Chini cluster) > (Pt)_neat > (Pt)_JM (Johnson Matthey) ≫ (Vulcan XC-72). As expected, all the Pt-loaded electrodes were more efficient than Vulcan XC-72. The classification appears to be linked with the mean nanoparticle size, and for comparable sizes, with the surface morphology of the materials. The results and the stability of the electrodes suggest that the small particle sizes and the good dispersity on the carbon support were maintained during the HER.     

Preparation and characterization of activated carbons from impregnation pitch by ZnCl2

Using an impregnation pitch from bituminous coal tar (OP) supplied by Industrias Químicas del Nalon Company as raw material, two phases (isotropic and anisotropic) have been obtained. The latter was used as precursor for the preparation of activated carbons. First, a chemical activation process was carried out with ZnCl₂ as activating agent. The process was conducted at different concentrations and temperatures and by means of impregnation with solid zinc chloride. Optimal values were obtained for samples prepared by using a ZnCl₂:pitch ratio equal to 3:1 (sample AZn3). Next, this sample was thermally treated at two different temperatures, i.e., 700 and 800 °C. A lose of specific surface area, microporosity and mesoporosity was observed with respect to sample AZn3, such a lose being more remarkable as temperature increased. Moreover, impregnation of the anisotropic phase of the original pitch with an aqueous solution of ZnCl₂ followed by thermal treatment resulted in a poorly developed surface area and porous texture, probably due to the presence of Zn complexes, which interfere with the activation process.     

An amperometric detector with a tubular electrode deposited on the capillary for capillary liquid chromatography

A procedure is described for the preparation of a tubular electrode by chemical deposition of platinum at the end of a fused-silica capillary. The properties of the electrode were tested under liquid chromatographic conditions, demonstrating that both the static and the dynamic behaviour of the detection system satisfy the requirements of capillary chromatographic separations and compare well with a wall-jet amperometric system and with UV photometric detection. The detection system described is easy to prepare and does not require any time-consuming positioning of the electrode system as it is integrated into the separation part of the apparatus.     

气密性碳涂覆光纤筛选强度与电阻关系研究

通过实验分析确立了把光纤电阻作为衡量气密性碳涂覆光纤通过２％应变筛选的过渡标准。要拉制２％应变筛选的碳涂覆光纤，其电阻值应小于３０ｋΩ／ｃｍ。