1,8-亚乙基萘在三氟化硼乙醚-聚乙二醇中的电化学聚合

在三氟化硼乙醚(BFEE)-聚乙二醇(分子量400,PEG400)混合电解质溶液中,1,8-亚乙基萘直接阳极氧化聚合可以获得自支撑聚(1,8-亚乙基萘)膜.单体在三氟化硼乙醚+10%PEG400中的起始氧化电位为0.95 Vversus SCE,远低于单体在0.1 mol.L-1四氟化硼四丁基胺-乙腈溶液中的起始氧化电位(1.38 VversusSCE).同时PEG400的加入可以有效改善单体在三氟化硼乙醚中的溶解性.UV-Vis,FTIR和1H-NMR确定了1,8-亚乙基萘在4,5位聚合,荧光光谱表明固态及可溶聚(1,8-亚乙基萘)膜是蓝色发光材料.     

可控降解超支化聚碳硅氮烷的合成与表征

通过锂化四甲基二乙烯基二硅氮烷分别与甲基氢二氯硅烷和二甲基氢氯硅烷的亲核取代反应合成了AB4和AB2型单体AB4M和AB2M,两种单体通过Karstedt催化剂催化的硅氢加成反应分别生成聚碳硅氮烷PAB4M和PAB2M.单体和聚合物的结构通过FT-IR、1H-NMR、13C-NMR、29Si-NMR和体积排除色谱-多角度激光光散射联用(SEC-MALLS)技术进行了表征,结果表明,单体的结构与设计结构相符合;单体聚合时主要以α-硅氢加成方式为主;聚合物具有超支化结构并由N(Si—C)3链节和大量端基双键组成.PAB4M和PAB2M的重均分子量分别为7800和5860g/mol,分子量分布系数分别为2·54和2·31·对PAB4M稳定性的初步研究表明,该聚合物对氯硅烷和在中性条件下对水稳定,但在HCl水溶液中可以降解,且通过控制HCl浓度可以调节其降解速度,从而实现对其控制降解.     

Synthesis and Crystal Structure of 3,3,6,6-Tetramethyl-N-hydroxy-9-ethyl-1,8-dioxo-1,2,3,4,5,6,7,8,9,10-decahydroacridine

1 INTRODUCTION 1,4-Dihydropyridines (1,4-DHPs) are well-knowncompounds because of their pharmacological pro-perty as calcium channel modulators[1, . The che- 2]mical modifications, such as the introduction of dif-ferent substituents[3, or heteroatoms[5], of the DHP 4]ring have allowed the expansion of researches onthe structure-activity relationship to gain new in-sights into the molecular interactions at the receptorlevel. In fact, it is well established th…     

聚偏氟乙烯取向薄膜的结晶形态

本文用小角激光散射法研究了聚偏氟乙烯薄膜在拉伸取向过程中晶体形态及结构的变化。拉伸使球晶形变为椭球,同时伴随着局部熔融与重结晶过程,散射图案由原来的四叶瓣发展为八叶瓣。红外测量及X-射线衍射分析表明,拉伸引起分子链构象改变,使晶型发生了转变。     

过氧化苯甲酰的光敏电荷转移分解反应及引发甲基丙烯酸甲酯的聚合

过氧化苯甲酰(BPO)的光诱导分解曾为许多工作者所注意。Walling和Gibian认为:以二苯酮为敏化剂时,BPO的敏化光解是通过三重态的能量转移过程。Encinas和Lissi则认为敏化是通过单重激发态使激发能转移至过氧化物基态的热振动态,从而导致过氧化物的分解。Tokumarur是最早提出过氧化苯甲酰光敏化诱导分解过程中存在着激基复合物(Exciplex)的可能性。最近他们又进一步研究以BPO为猝灭剂去猝     

微波辐照下无皂阳离子聚(St-MMA)高分子纳米粒子的制备和表征

讨论了微波辐照下 ,以丙酮 水为分散介质 ,利用阳离子型自由基引发剂偶氮二异丁基脒盐酸盐(AIBA)引发苯乙烯 (St)和甲基丙烯酸甲酯 (MMA)共聚 ,合成出表面带正电荷的P(St MMA)共聚物纳米粒子 ,考察了丙酮用量、单体和引发剂浓度对纳米粒子粒径、粒径分布和乳液稳定性的影响 .结果表明 ,丙酮 水的体积比由 0增加到 1 2 6∶1时 ,粒子的平均水化半径从 12 2 2 1nm降低到 2 4 6 8nm ,粒径分布变宽 ,乳液抗电解质稳定性逐渐增强 ;增加引发剂和共聚单体MMA的浓度 ,粒子的水化半径逐渐减小 ,粒径分散系数增大 .     

FTIR-ATR技术研究聚氨酯类文物保护材料的光降解

Polyurethanes are one kind of relic protection materials commonly used. During artificial photo-ageing, three polyurethanes, HDI-based polyurethane, MDI-based polyurethane and TDI-based polyurethane, have been considered to undergo UV radiation. Photochemical degradation of the polyurethanes has been monitored by means of Fourier transform infrared spectroscopy with attenuated total reflection accessory （FTIR-ATR）. It was proved that the mechanism of the photochemical degradation of polyurethanes might be the scissions of carbamate （urethane） groups and the re-reactions of radical groups formed in the scission reactions. From the experiment results HDI-based polyurethane, an aliphatic diisocyanate, could be considered to be more suitably used as relic protection materials among these three polyurethanes for its ageing products with less color.     

Synthesis and Crystal Structures of Novel Keggin and Dawson Polyoxometalates Containing Amantadine

Heteropolyoxometalates are a large family of potent medicines due to their excellent antiviral and antitumor activity 1-4, while their application in clinic meets great difficulties for their toxicity 5. How to synthesize heteropolyoxometalate medicines possessing high activity and low toxicity has become the focus in heteropolyoxometalate medicine research. Previously reported polyoxometalates showing medical activities are all salts simple Na+, K+ or NH4+ etc. inorganic cations, in which o…     

微米级PSt,P(St/MAA)磁性高分子微球的合成Ⅰ. 温度、引发剂、介质极性、稳定剂量的影响

以Fe3O4为核，采用分散聚合法，合成了粒径为0．5－2．0μm、单分散性好、磁含量可达10％的PSt、P（St/MAA)磁性高分子微球。讨论了温度、引发剂、分散介质、稳定剂等因素对反应结果的影响。对所得磁性微球的外观形态、磁响应性进行了表征。     

有机硅弹性体表面生物相容性的研究进展

生物材料表面的生物相容性一直是生物材料研究领域倍受关注的问题.本文综述了对有机硅弹性体进行改性以提高其表面生物相容性的研究进展,介绍了各种常用的化学改性方法如本体接枝、等离子体处理、光化学诱导接枝、臭氧活化接枝以及硅氢加成反应、原子转移自由基聚合反应在有机硅弹性体表面改性中的应用.对改性后的有机硅弹性体表面抗非特异性蛋白质和血小板的能力等方面进行了评述,并进一步分析了有机硅弹性体表面化学改性的发展趋势和研究重点.