Formation of the ferroelectric domains in epitaxial PbTiO3 thin films grown by metalorganic chemical vapor deposition

3 thin films have been prepared by metalorganic chemical vapor deposition under reduced pressure. The formation of ferroelectric domains in films grown on SrTiO₃ and LaAlO₃ substrates was investigated by synchrotron radiation and Rutherford backscattering spectroscopy. Single-domain (3000-Å thick) and multi-domain (4500-Å thick) PbTiO₃ films were produced on SrTiO₃. For multi-domain PbTiO₃ film, the c-domain presented epitaxial structure with its c-axis perpendicular to the substrate surface, while a-domains aligned four-fold symmetrically with c-domains by 2.79^° off the c-axis of c-domains. In the film, the measured lattice constants (a, b and c) of the a- and c-domains were different from each other, indicating that the films suffered a modulated strain during domain formation. In contrast, both the a and c domains of films on LaAlO₃ were alternatively aligned on substrate with the a-axis of the a-domain and the c-axis of c-domains perpendicular to the substrate surface. Two-dimensional distribution of these domains is proposed and the formation of these kinds of domains is discussed. The surface morphology and phase transition process of single and multi domain PbTiO₃ film on SrTiO₃ were studied by atomic force microscope (AFM) and high temperature X-ray diffraction, respectively. Received: 15 August 1996/Accepted: 21 January 1997