Preparation of phenyl‐modified natural rubber in latex stage

Phenyl‐modified natural rubber was prepared in latex stage by bromination of deproteinized natural rubber followed by Suzuki‐Miyaura cross‐coupling reaction. First, the bromination of natural rubber was carried out using N‐bromosuccinimide in latex stage. The bromine atom content increased as amount of N‐bromosuccinimide increased. Second, the allylic bromine atom was replaced with a phenyl group using phenyl boronic acid in the presence of a palladium catalyst, according to the Suzuki‐Miyaura cross‐coupling reaction in latex stage. The resulting products were characterized by nuclear magnetic resonance (NMR) spectroscopy. Signal at 7.13 ppm was assigned to the phenyl group of the product, while signals at 3.98, 4.14, and 4.44 ppm were assigned to the remaining allylic brominated cis‐1,4‐isoprene units. The estimated phenyl group content and the conversion of the Suzuki‐Miyaura cross‐coupling reaction were 1.32 and 23.7 mol%, respectively. Glass transition temperature (T_g) of deproteinized natural rubber increased from ?62°C to ?46.7°C, when the phenyl group was introduced into the rubber.     

Structural and magnetic ordering in the VxNb1+yS2 system

The influence of composition on the structural ordering and magnetism in the V_xNb_1+yS₂ system has been investigated by X-ray diffraction and magnetic measurements. Stoichiometric V_1/3NbS₂ did not exhibit the structural ordering of vanadium between the NbS₂ layers. In the ordered structure, the vanadium composition deviated from the ideal value of to both higher and lower values, while the niobium composition was in the range of 0.05?y?0.18. Excess niobium, y>0, is thought to play an essential role in the structural ordering in this system. For samples with excess niobium and ordered structures, a magnetic transition was observed at 20-50 K, depending on the composition. The spontaneous magnetization of 3-5×10⁻³ μ_B/V atom is thought to be intrinsic to this system. The magnetization curves consisted of a constant and a proportional parts of the magnetic field, which correspond to the spontaneous magnetization and high-field susceptibility, respectively. The magnetization curves and the temperature dependencies of the high-field susceptibility were quite similar to those of the canted antiferromagnetic NiS₂. A correlation between the structural and magnetic ordering is suggested.     

Fine-patterning on glass substrates by the sol-gel method

A novel process has been developed to form fine patterns on glass substrates. The process consists of the following steps: (1) coating of gel film on a substrate, (2) patterning on the gel film, and (3) heat-treatment. The key point in this process is the control of hardening of the gel films by the addition of organic polymers such as polyethylene glycol (PEG). The addition of PEG increased the viscosity of the coating solutions and delayed the gelation time, but had little effect on the optical properties of the resultant heat-treated glass films. The newly developed process is expected to be applicable to the formation of the optical devices such as diffraction gratings and pre-groovesof optical memory disks.     

Predictive activity profiling of drugs by topological-fragment-spectra-based support vector machines

Aiming at the prediction of pleiotropic effects of drugs, we have investigated the multilabel classification of drugs that have one or more of 100 different kinds of activity labels. Structural feature representation of each drug molecule was based on the topological fragment spectra method, which was proposed in our previous work. Support vector machine (SVM) was used for the classification and the prediction of their activity classes. Multilabel classification was carried out by a set of the SVM classifiers. The collective SVM classifiers were trained with a training set of 59,180 compounds and validated by another set (validation set) of 29,590 compounds. For a test set that consists of 9,864 compounds, the classifiers correctly classified 80.8% of the drugs into their own active classes. The SVM classifiers also successfully performed predictions of the activity spectra for multilabel compounds.     

Algorithm for in vitro Sun Protection Factor based on transmission spectrum measurement with concomitant evaluation of photostability

In the in vitro evaluation of Sun Protection Factor (SPF), the photostability of the ultraviolet (UV) filters can have a major impact, especially for high-SPF formulations, but is generally not taken into consideration. In this study, we present a UV transmission spectrum measurement system utilizing a high-sensitivity UV photomultiplier tube with concomitant evaluation of photostability. We have developed an algorithm to estimate SPF in vitro by converting the amount of UV light transmission through the sunscreen layer into cumulative relative erythema effectiveness to obtain one minimal erythema dose. Thus, the algorithm uses the same endpoint as in vivo SPF methods, but with a photomultiplier tube as the detector instead of skin. The values obtained showed an excellent correlation with in vivo SPF values, even for high-SPF sunscreens exceeding SPF 50. This method should be suitable as an in vitro SPF testing method for regulatory purposes.     

Rapid development of hydrophilicity and protein adsorption resistance by polymer surfaces bearing phosphorylcholine and naphthalene groups

In order to provide a protein adsorption resistant surface even when the surface was in contact with a protein solution under completely dry conditions, a new phospholipid copolymer, poly (2-methacryloyloxyethyl phosphorylcholine (MPC)- co-2-vinylnaphthalene (vN)) (PMvN), was synthesized. Poly(ethylene terephthalate) (PET) could be readily coated with PMvN by a solvent evaporation method. Dynamic contact angle measurements with water revealed that the surface was wetted very rapidly and had strong hydrophilic characteristics; moreover, molecular mobility at the surface was extremely low. When the surface came in contact with a plasma protein solution containing bovine serum albumin (BSA), the amounts of the plasma protein adsorbed on the dry surface coated with PMvN and that adsorbed on a dry surface coated with poly(MPC-co-n-butyl methacrylate) (PMB) were compared. Substantially lower protein adsorption was observed with PMvN coating. This is due to the rapid hydration behavior of PMvN. We concluded that PMvN can be used as a functional coating material for medical devices without any wetting pretreatment.     

Electroresponsive Structurally Colored Materials: A Combination of Structural and Electrochromic Effects

Electroresponsive structurally colored materials composed of ordered arrays of polyaniline@poly(methyl methacrylate) (PANI@PMMA) core–shell nanoparticles have been successfully prepared. The core–shell nanoparticles were synthesized by deposition of PANI shells on the surfaces of the PMMA cores by the oxidative polymerization of anilinium chloride. Ordered arrays were then fabricated by using the fluidic cell method. Because the ordered arrays and the PANI shells generate structural and electrochromic colors, respectively, these core–shell colloidal crystals exhibited colors resulting from the combined effects of these materials. The crystal colors depended greatly on the size of PANI@PMMA particles and could also be varied by the application of a voltage. The electrochromic colors of these arrays were found to be quite different from those exhibited by pure PANI films prepared by electrochemical oxidation.