Synthesis of submicron CaZrO<Subscript>3</Subscript> in combustion reactions

Submicron CaZrO₃ powder is obtained in combustion reactions (solution combustion synthesis—SCS) with glycine. It is found that SCS reduces the sintering temperature of CaZrO₃ powders. The dielectric properties of calcium zirconate ceramics are studied by the electrochemical impedance method. It is shown that a ceramics of powders obtained by the SCS method has high dielectric characteristics.     

Gas-phase 21Ne NMR studies and the nuclear magnetic dipole moment of neon-21

Gas-phase ²¹Ne nuclear magnetic resonance spectra were measured at the natural abundance of ²¹Ne isotope for samples consisting of pressurized neon up to 60 bar at room temperature and applying the magnetic field of the strength B₀ = 11.7574 T. It showed that the nuclear magnetic resonance frequency is linearly dependent on the density of gaseous neon. The resonance frequency was extrapolated to the zero-density point, and it permitted the determination of the ²¹Ne nuclear magnetic moment, μ(²¹Ne) = 0.6617774(10) μ_N. The present value of μ(²¹Ne) is not influenced by the bulk magnetic susceptibility of neon and interactions between neon atoms; therefore, it is more precise and reliable than the previous result obtained for μ(²¹Ne).     

Enhancing the Water Stability of Al‐MIL‐101‐NH2 via Postsynthetic Modification

The resistance of metal–organic frameworks towards water is a very critical issue concerning their practical use. Recently, it was shown for microporous MOFs that the water stability could be increased by introducing hydrophobic pendant groups. Here, we demonstrate a remarkable stabilisation of the mesoporous MOF Al‐MIL‐101‐NH₂ by postsynthetic modification with phenyl isocyanate. In this process 86 % of the amino groups were converted into phenylurea units. As a consequence, the long‐term stability of Al‐MIL‐101‐URPh in liquid water could be extended beyond a week. In water saturated atmospheres Al‐MIL‐101‐URPh decomposed at least 12‐times slower than the unfunctionalised analogue. To study the underlying processes both materials were characterised by Ar, N₂ and H₂O sorption measurements, powder X‐ray diffraction, thermogravimetric and chemical analysis as well as solid‐state NMR and IR spectroscopy. Postsynthetic modification decreased the BET equivalent surface area from 3363 to 1555 m² g^?1 for Al‐MIL‐101‐URPh and reduced the mean diameters of the mesopores by 0.6 nm without degrading the structure significantly and reducing thermal stability. In spite of similar water uptake capacities, the relative humidity‐dependent uptake of Al‐MIL‐101‐URPh is slowed and occurs at higher relative humidity values. In combination with ¹H‐²⁷Al D ‐HMQC NMR spectroscopy experiments this favours a shielding mechanism of the Al clusters by the pendant phenyl groups and rules out pore blocking.