PLA/EMAG共混物的制备与表征

通过熔融共混挤出法制备了不同乙烯-丙烯酸甲酯-甲基丙烯酸缩水甘油酯(EMAG)含量下的聚乳酸(PLA)/EMAG共混物,考察共混体系中EMAG与PLA基体之间的相互作用,研究了PLA/EMAG共混物的结晶性能、力学性能、熔体指数、加工性能以及热稳定性.表征结果显示:EMAG中的环氧基团与PLA的端羟基或端羧基发生化学反应,形成反应性共混体系,PLA/EMAG共混物的韧性较纯PLA有大幅提高,在EMAG含量为15;时达到最大.     

烧结温度对Cao.9(NaCe)0.05Bi2Nb2O9无铅压电陶瓷性能的影响

采用传统固相反应法制备了Ca0.9(NaCe)0.05Bi2 Nb2 O9铋层状无铅压电陶瓷.采用XRD、SEM、EDS及相关电学性能测试系统表征了样品的晶体结构、断面形貌、元素组成以及介电、压电、铁电等性能,探究不同烧结温度对于陶瓷性能的影响.结果表明:当烧结温度为1150℃时,样品的晶体结构单一均匀,呈现片层状结构,致密性较好,压电常数高达17 pC/N,介电损耗仅为0.42;,居里温度为908℃,并且具有很好的温度稳定性,说明固相反应法制备的Ca0.9(NaCe)0.05Bi2Nb2O9压电陶瓷最佳烧结温度为1150℃.     

烧结温度对煤系高岭土制备堇青石陶瓷的影响

我国的煤系高岭土具有明显的资源优势,应对其进行充分地研究和合理地应用,以缓和优质高岭土资源枯竭的燃眉之急.以鄂尔多斯煤系高岭土、鄂尔多斯滑石、工业氧化铝为原料,通过反应烧结一步合成堇青石,探讨了堇青石合成温度范围,以拓宽该煤系高岭土的应用范围.通过高温显微镜观察堇青石试样的合成温度范围为1400～1420℃.经1420℃合成的堇青石试样的吸水率为16.11;,显气孔率为28.44;,体积密度为1.77 g/cm3,径向烧成收缩为1.77;,厚度烧成收缩为4.80;,抗折强度为43.56 MPa.镁铝尖晶石是合成堇青石的重要中间产物,适当提高烧结温度可以促进镁铝尖晶石相向堇青石相转变,有利于堇青石晶粒的生长与发育.烧结温度的变化是堇青石晶粒发生变化的原因,同时导致液相量的变化,最终影响堇青石试样显微结构和烧结性能.     

Organocatalytic asymmetric chlorinative dearomatization of naphthols

An organocatalytic asymmetric chlorinative dearomatization of naphthols was realized for the first time, providing chiral naphthalenones with a Cl-containing all-substituted stereocenter in excellent yields and enantioselectivity (up to 97% yield and 96% ee). The reaction features mild reaction conditions, good tolerance of diverse functional groups and simple reaction operation.     

A post curing strategy toward the feasible covalent adaptable networks in polyacrylate latex films

The implementation of covalent adaptable networks (CANs) in general resin system is becoming attractive. In this work, we propose a simple post-curing strategy based on the core-shell structured acrylate latex for the achievement on both the improved general performance and the CANs characteristics in latex films. The building to the CANs was relied on the introduction of 4,4′-diaminophenyl disulfide as the curing agent, which cured the acetoacetoxy decorated shell polymer through the ketoamine reaction. The metathesis reaction of aromatic disulfides in the crosslinking segments enabled the thermally induced dynamic behavior of the network as revealed in the stress relaxation tests by comparison with other diamine crosslinking agents without the incorporation of disulfide. The synergism of the dynamic crosslinking of the shell polymer and static crosslinking in the core polymer contributed to the improved mechanical strength (15 MPa, strain% = 250%) and the suppressed water adsorption (~1% in 24 h of soaking) of the latex film, which exhibited above 90% of recovery in both strength and strain from a cut-off film damage within 1 h at 80°C. Moreover, the cured latex film could be recycled, and 75% of the mechanical performance was regained after three fragmentation-hot-pressing cycles. These, in addition with the feasible and environmental friendly characteristics, suggest a sustainable paradigm toward the smart thermosetting latex polymers.     

用标准件对梯度磁场定标

就标准厚度卡片在霍尔传感器的定标方面的应用作了有益的探讨。在纵向测量微小长度时,霍尔片处于磁场边缘位置,其对磁场的梯度更大,即灵敏度更高,且靠中心位置的线性更好。     

NO分子宏观气体热力学性质的理论研究

采用量子统计系综理论,研究了基态NO分子宏观气体摩尔熵、摩尔内能、摩尔热容等热力学性质.首先应用课题组前期建立的变分代数法(variational algebraic method, VAM)计算获得了基态NO分子的完全振动能级,得到的VAM振动能级作为振动部分,结合欧拉-麦克劳林渐进展开公式的转动贡献,应用于经典的热力学与统计物理公式中,从而计算得到了1000-5000 K温度范围内NO宏观气体的摩尔内能、摩尔熵和摩尔热容.将不同方法计算得到的摩尔热容结果分别与实验值进行比较,结果表明基于VAM完全振动能级获得的结果优于其他方法获得的理论结果.振动部分采用谐振子模型对无限能级求和计算热力学性质的方法有一定的局限性,应当使用有限的完全振动能级进行统计求和.     

松木-聚氯乙烯复合材料催化热解特性的研究

通过热重法研究了松木与聚氯乙烯复合材料的催化热解特性,结果表明聚氯乙烯脱氯阶段与松木的纤维素、半纤维素热分解阶段温度区间重合,二者共热解时存在协同效应,并且HCl的释放对纤维素的脱水反应能够产生催化作用,HCl释放也对木质素的热分解及碳化反应有着明显的催化作用,导致二者共热解制备的碳化物产率提高,约为29.61%。并且利用元素分析仪、扫描电镜和能谱仪对成碳材料进行表征分析,结果表明成碳材料表面粗糙呈现多孔结构,其碳元素含量较高达到74.67%。     

盐酸伊达比星杂质A的合成工艺优化及其高效液相分析

通过对盐酸伊达比星脱羟基杂质A的合成研究，为盐酸伊达比星的质控标准提供参考。以盐酸伊达比星为起始原料，经过4步反应得到脱羟基杂质A。本文提供了盐酸伊达比星杂质A的制备方法以及高效液相色谱分析方法，为杂质含量控制提供了依据。该工艺可以稳定、快速制备高纯度脱羟基杂质A，制备总收率为57.20%，纯度为57.20%，其结构经¹H NMR， ¹³C NMR和MS(ESI)表征。