Mössbauer study of new vanadate glass with large charge-discharge capacity

Charge-discharge capacity and cyclicity of lithium ion battery (LIB) was evaluated in which 15Li₂O·10Fe₂O₃·xSnO₂·5P₂O₅·(70–x)V₂O₅ glass (x?=?0 and 20 in mol%, abbreviated as xLFSPV) was used as a cathode. A local structure of xLFSPV glass before and after charging was investigated by ⁵⁷Fe- and ¹¹⁹Sn-Mössbauer spectroscopies. ⁵⁷Fe-Mössbauer spectrum of xLFSPV glass with ‘x’ of 20 was composed of a doublet with isomer shift (δ) of 0.35_±0.02 mm s^???1 and quadrupole splitting (Δ) of 0.88_±0.03 mm s^???1 due to distorted Fe^IIIO₄ tetrahedra. ¹¹⁹Sn-Mössbauer spectrum of this glass consisted of a doublet with δ of 0.08_±0.01 and Δ of 0.52_±0.01 mms^???1 due to distorted Sn^VIO₆ octahedra. After discharging the battery from 4.5 to 1.0 V, larger δ of 0.40_±0.03 mm s^???1 and Δ of 0.94_±0.04 mm s^???1 were obtained, indicating that both iconicity of Fe-O bonds and local distortion of Fe^IIIO₄ tetrahedra were increased. On the contrary, identical δ of 0.09_±0.01 mm s^???1 and Δ of 0.50_±0.01 mm s^???1 were observed in the ¹¹⁹Sn-Mössbauer spectrum of 20LFSPV glass after the discharge, indicating that chemical environment of Sn^IVO₆ octahedra was not affected after the discharge. Charge-discharge curve of LIB containing 20LFSPV glass as a cathode active material recorded under the current density of 8.3 mA g^???1 (0.011 mA cm^???2) between 1.0 and 4.5 V showed a large initial charge capacity of 431.1 mAh g^???1 and discharge capacity of 382.3 mAh g^???1, respectively. These results indicate that 20LFSPV glass could be a new cathode active material for LIB.     

Numerical simulation of 2D granular particles and its analyses by means of the micropolar fluid model

Numerical simulations of two-dimensional granular flows under uniform mean shear and external body torque were performed following the setting of the authors’ previous study [10]. Convergence of the stresses with the increase of coarse-graining length is investigated. Difference R between vorticity field and spin field is controlled by the external torque and the stresses for the region R > 0 is obtained as well as those for R < 0. The symmetry of the stresses under the change of the sign of R is discussed.     

Mechanically strengthened new Hagi porcelain developed by controlling the chemical environment of iron

In order to enhance the mechanical strength of Hagi Porcelain (Hagiyaki), one of the oldest and famous potteries in Japan, new preparation condition was examined. Tempered Hagi porcelain, denominated as ‘Hagi Porcelain B’, was prepared with the Porcelain clay originating from Daido district, Yamaguchi Prefecture, Japan. Structural change of ‘Hagi Porcelain B’ was investigated by means of ⁵⁷Fe-Mössbauer spectroscopy, X-ray diffractometry (XRD) and three-point bending test. Mechanical strength of the ‘original Hagi Porcelain B’ was estimated to be 43.1 MPa by means of the three-point bending test, while much larger value of 104.5 MPa could be achieved when tempered by a chemical modification. Mössbauer spectrum of the ‘original Hagi porcelain B’ was composed of a paramagnetic doublet and a magnetic sextet due to Fe(III) of γ-Fe₂O₃(maghemite), while only one paramagnetic doublet due to to octahedral Fe(II)O₆ was observed for the ‘tempered Hagi Porcelain B’ with isomer shift and quadrupole splitting values of 1.13 and 2.15 mm s^?1, respectively. It is considered that the absence of magnetic phase causes an increase of the mechanical strength because the maghemite phase has a defect spinel structure. These results indicate that mechanical strength of the ‘Hagi porcelain B’ could be enhanced by controlling the sintering condition.     

Total Synthesis of Lajollamycin B

The first total synthesis of lajollamycin B, a structurally novel nitro-tetraene spiro-β-lactone/γ-lactone antibiotic, is described. The convergent synthesis involves the construction of the C8′–C11′ nitrodienylstannane and its coupling with the segment prepared from the C1′–C7′ ω-iodoheptadienoic acid and the right-hand heterocyclic fragment, which has been utilized for our previous syntheses of oxazolomycin A. The revision of the geometry of the terminal Δ^{10′, 11′}-double bond from E to Z is also described for the structure of natural lajollamycin B.     

1,2-Dihydro-1-hydroxy-2,3,1-benzodiazaborine Bearing an Acridine Moiety as a Circular Dichroism Probe for Determination of Absolute Configuration of Mono-Alcohols

A new chiral probe molecule for mono-alcohols is developed by using 1,2-dihydro-1-hydroxy-2,3,1-benzodiazaborine (DAB) bearing an acridine moiety 1 . In the presence of mono-alcohols, DAB 1 forms borate 2 by boronic ester formation, followed by coordination of the acridine moiety to the boron atom. Borate 2 has a chiral center on the boron atom and works as a stereodynamic circular dichroism (CD) probe molecule for chiral mono-alcohols based on the π–π interaction between the acridine moiety and the carbon–carbon unsaturated moiety on mono-alcohols.