Deposition of Layer－by－layer Inorganic－organic Nano－hybrid Ultrathin Films onto SBA－15

Deposition of inorganic-organic nano-hybrid ultrathin films onto mesoporous silicate materials has been proven possible by using layer-by-layer assembly method. In combination with sol-gel method, titania, subsequently dye molecules (or polymer) were successfully fabricated onto the inner wall of SBA-15. Their structures were preliminarily characterized by FTIR and solid-state UV-Vis spectroscopy, thermal analysis, and BET surface area measurements,respectively.     

PEG-PLA嵌段共聚物的合成及~(13)C NMR对平均链段长度的测定

本文报道聚乙二醇(PEG)在辛酸亚锡存在下与丙交酯(LA)反应合成PEG-PLA嵌段共聚物,用~(13)C NMR测定了共聚物的结构,估算了平均链段长度.实验结果表明,L_(PEG)在反应过程中保持不变,而L_(PLA)随反应时间和LA在原料配比中含量的增加而增加,呈逐步聚合反应特点.对聚合反应机理作了推测.     

Pd-Rh型国Ⅲ排放三效催化剂的研制

对满足欧Ⅲ排放限值的Pd-Rh型三效催化剂进行研究开发,测试了新鲜催化剂的空燃比特性和起燃温度特性,并与市场上的欧Ⅲ催化剂在同等条件下老化后的性能进行了比较.对研制的催化剂进行封装总成后,按照GB18352.3-2005标准进行了常温冷起动Ⅰ型和低温冷起动IV型试验,测试结果完全能满足该标准的限值要求.     

(TiNi)_x(x=2~4)团簇结构和电子结构

从团簇角度对TiNi形状记忆合金进行了量子化学从头算研究。设计并优化了等原子比(TiNi)x(x=2~4)簇的多种可能几何结构,并对较稳定构型进行电子结构的分析。结果表明,等原子比的(TiNi)n团簇以TiNi成键为主要分子骨架,小团簇有较多能量接近的异构体,TiTi成键对能量降低有较大贡献。     

PrCl3催化漆酚干燥成膜的研究

Pr原子特殊的电子层结构使其具有多方面的催化特性．实验发现质量分数为0．7％的PrCl3就可使漆酚(U)于110℃固化成膜的时间从5h降低到1h．用可见分光光度法、电子能谱、紫外和红外光谱等方法研究U在PrCl3作用下的固化成膜历程．结果表明，在Pr(Ⅲ)催化U聚合的过程中首先是U与PrCl3发生配位作用，生成U镨配合物(UPr)，然后该配合物分子中的Pr(Ⅲ)催化U聚合成体形结构的高分子化合物．     

沐浴海绵Spongia zimocca aubspecles irregularia(Lendenfeld)中的含氮化合物

从沐浴海绵Spongia zimocca aubspecles irregularia(Lendenfeld)分离和处理得到3种含氮化合物,通过波谱法鉴定化学结构,化合物1为新的神经酰胺N-2-(1,3-二羟基-十五烷基)-2′,20′-二十一酰胺,2为神经酰胺(E)-N-2-(1,3-二羟基-4-十八烯基)-十六酰胺,3为醋酸胍.     

Preparation of Ce-Zr-O solid solution

A single phase solid solution of Ce-Zr-O can be made by using NH₄HCO₃ solution as precipitating agent. The influence of preparation conditions, such as pH, Zr⁴⁺/(CO₃ ^2-+HCO₃ ^-) and Ce³⁺/Zr⁴⁺ ratio on the formation of the solid solution were investigated. The results show that a single phase Ce-Zr-O solid solution can be formed only under a narrow window of preparation conditions, indicating that some compounds are formed in the precipitating process. The compound may contain Ce³⁺, Zr⁴⁺, CO₃ ^2-, HCO^3-, and OH^-. The solid solution so prepared can be described as Ce_0.37Zr_0.63O₂. This revised version was published online in August 2006 with corrections to the Cover Date.